Aluminum-Induced Crystallization of PECVD Amorphous Silicon

Published online by Cambridge University Press:  21 March 2011

Kenneth Jenq ,
Shawn S. Chang ,
Yaguang Lian ,
Grant Z. Pan  and
Yahya Rahmat-Samii
Kenneth Jenq
Affiliation:
Microfabrication Laboratory
Shawn S. Chang
Affiliation:
Microfabrication Laboratory
Yaguang Lian
Affiliation:
Microfabrication Laboratory
Grant Z. Pan
Affiliation:
Microfabrication Laboratory
Yahya Rahmat-Samii
Affiliation:
Antenna Research, Analysis and Measurement Laboratory, Department of Electrical Engineering, University of California at Los Angeles, Los Angeles, CA 90095-1594.
Get access

Abstract

Aluminum-induced crystallization (AIC) of amorphous silicon (a-Si) in a conventional furnace with N2 protection has been studied at reaction temperatures ranging from 200 to 500°C by using optical microscopy, and transmission and scanning electron microscopy. The a-Si and Al layers were deposited with plasma-enhanced chemical vapor deposition (PECVD) and electron beam evaporation, respectively. The structures in the study are Al/a-Si and a-Si/Al on Si or glass wafers coated with 3000 Å PECVD SiO2. It was found that Al induces crystallization of a-Si for both Al/a-Si and a-Si/Al structures by exchanging positions of Al and Si layer through diffusion of Si into Al and the grain size of crystallized Si (c-Si) increases with the decrease of AIC temperature. AIC for Al/a-Si structures starts at a temperature as low as 200°C, which is 100°C lower than that for a-Si/Al structures. Kinetics analysis found that the activation energies are 1.76 eV and 1.65 eV for both Al/a-Si and a-Si/Al structures, respectively. The quality of AIC c-Si depends on the order, thickness and thickness ratio of a-Si to Al. Microstructural observations indicated that the c-Si for Al/a-Si structures is better and more suitable for use in fabrication of thin film transistors (TFTs) than that for a-Si/Al structures.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 808: Symposium A – Amorphous and Nanocrystaline Silicon Science and Technology-2004 , 2004 , A4.20
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Nast, Oliver, Brehme, S.et al., Solar Energy Materials & Solar Cells 65, 385(2001).Google Scholar
2. Fujikawa, S. I., Hirano, K. I. and Fukushima, Y., Metallurgical Transaction A 9, 1811(1978).Google Scholar