The regeneration of human tissues with complex anatomy such as gastrointestinal (GI) tract remains greatly challenging since it requires appropriate cell microenvironments with well-defined structural and biochemical cues. In this investigation, bilayer scaffolds consisting of different polymer nanofibers with orthogonal fiber orientations were prepared, in which vascular endothelial growth factor (VEGF) and platelet-derived growth factor (PDGF) were encapsulated separately. The bilayer scaffolds have similar architecture to the anatomy of the GI tract and can achieve dual releases of VEGF and PDGF in sequential and sustained manners, which hold promise as appropriate cell microenvironments for promoting the regeneration of the GI tract.

Aluminum-doped zinc oxide films were prepared by atomic layer deposition using diethylzinc, trimethylaluminum, and water. High-purity water was used with low vacuum. The effect of growth temperature on characteristics of the films was investigated. The crystallinity was improved as growth temperature was increased from 180 to 235 °C, with the grain sizes increasing from 32.830 to 47.020 nm. The films possessed high transparency with a 95% transmission window blue shifted with growth temperature. This shift was seen in the energy-band gaps which changed from 3.46 to 3.68 eV, leading to a decreased resistivity from 1.52 × 10−5 to 1.28 × 10−5 Ω cm.

Composition-dependent microstructure and mechanical properties of ultrafine-grained Al and Al–Mg films fabricated by DC magnetron sputtering with the novel micro-combinatorial technique were studied by transmission electron microscopy, atomic force microscopy, and nanoindentation. It was revealed that these films have extremely high strength, enabling their potential application as protecting layers. Besides the possible practical applications, the results of the present work also confirm the validity of the modified Hall–Petch relationship for the uniform description of the strength of face-centered cubic metals and solid solution having ultrafine-grain size.

A simple and facile stereolithography 3D printing technique was utilized to fabricate piezoelectric photopolymer-based polyvinylidene fluoride (PVDF) blends. Different process variables, such as solvent (N,N-dimethylformamide, DMF) to PVDF ratio and PVDF solution to photopolymer resin (PR) ratio, were engineered to enhance the dispersion of the PVDF into the PR so as to achieve the maximum piezoelectric coupling coefficient. Our results demonstrate that a ratio of 1:10 (PVDF:DMF) and 2 wt%-PVDF/PR was optimal for the best dissolution of the PVDF, 3D printability, and piezoelectric properties. Under these conditions, the blend generated ±0.121 nA under 80 N dynamic loading excitation. We believe that the findings of this work would promote many further studies on the mass production of flexible piezoelectric polymer blends with higher quality finished surface and design flexibility.