X-ray investigation of bredigite

Published online by Cambridge University Press:  14 March 2018

Audrey M. B. Douglas
Audrey M. B. Douglas*
Affiliation:
Department of Mineralogy and Petrology, University of Cambridge
Get access Rights & Permissions [Opens in a new window]

Extract

The X-ray work described below has been done on crystals of bredigite obtained from two different sources, the natural mineral from Scawt Hill, County Antrim, and the synthetic mineral from spiegeleisen slags. Both types of material have been fully deseribed by Tilley and Vincent (1948). Their analysis shows that the slag mineral is a calcium orthosilicate in which Ca is partly replaced by Mg, Mn, and Ba, the extent of the replacement being represented by the formula (Cal.59Ba0.08Mg0.31Mn0.09)SiO4. Tilley and Vincent conclude that this orthorhombic (pseudo-hexagonal) phase is identical with the high-temperature form α' of pure Ca2SiO4, the existence of which was suggested by Bredig (1943a), and confirmed by TrSmel (1949) using a high-temperature powder camera. Bredig (1943a) also suggests, on the basis of a comparison of X-ray powder patterns, that the crystal structure of α'-Ca2SiO4 is similar to that of β-K2SO4. The present single-crystal work was originally undertaken in order to investigate the structure of α'-Ca2SiO4 more fully.

Type
Research Article
Information
Mineralogical magazine and journal of the Mineralogical Society , Volume 29 , Issue 217 , June 1952 , pp. 875 - 884
Copyright
Copyright © The Mineralogical Society of Great Britain and Ireland 1952

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Beliankin, (D.S.) and Lapin, (V.V.), 1946. Compt. Rend. (Doklady) Acad. Sci. URSS, vol. 51, p. 705. [M.A. 10–106.[Google Scholar
Bredig, (M.A.), 1941. Journ. Amer. Chem. Soc., vol. 63, p. 2533.Google Scholar
Bredig, (M.A.), 1942. Journ. Phys. Chem., vol. 46, p. 747.Google Scholar
Bredig, (M.A.), 1943a. Amer. Min., vol. 28, p. 594. [M.A. 9–92.]Google Scholar
Bredig, (M.A.), 1943b. Journ. Phys. Chem., vol. 47, p. 587.Google Scholar
Bredig, (M.A.), 1950. Journ. Amer. Ceram. Soc., vol. 33, p. 188.Google Scholar
Greene, (K.T.), 1944. Journ. Research Nat. Bur. Standards, U.S.A., vol. 32, p. 1.Google Scholar
Howells, (E.R.), Phillips, (D.C.), and Rogers, (D.), 1950. Acta Cryst., vol. 3, p. 210.Google Scholar
Midgley, (C. M.), 1952. Acta Cryst. (in press). 1Google Scholar
O'Daniel, (H.) and Tscheischwili, (L.), 1942. Zeits. Krist., vol. 104, p. 124. [M.A. 8–290.[Google Scholar
Rait, (J.R.) and Goldschmidt, (H.J.), 1945. Journ. Iron & Steel Inst., vol. 151, p. 391.Google Scholar
Tilley, (C.E.), 1929. Min. Mag., vol. 22, p. 77.Google Scholar
Tilley, (C.E.), and Vincent, (H. C. G.), 1948. Min. Mag., vol. 28, p. 255.Google Scholar
Trömel, (G.), 1949. Naturwiss., vol. 36, p. 88.Google Scholar
Trömel, (G.), and Möller, (H.), 1950. Forts. Min., vol. 28 (for 1949), p. 80. [M.A. 11–470.[Google Scholar
Van Valkenburg, (A. Jr.) and McMurdie, (H.F.), 1947. Journ. Research Nat. Bur. Standards U.S.A., vol. 38, p. 415.Google Scholar