Ultrafine MnFe2O4 powder preparation by combusting the coprecipitate with and without Mg2+ or Zn2+ additives

Published online by Cambridge University Press:  31 January 2011

Hsuan-Fu Yu  and
Wen-Bing Zhong
Hsuan-Fu Yu
Affiliation:
Department of Chemical Engineering, Tamkang University, Taipei Hsien, Taiwan 25137, Republic of China
Wen-Bing Zhong
Affiliation:
Department of Chemical Engineering, Tamkang University, Taipei Hsien, Taiwan 25137, Republic of China
Get access

Extract

Ultrafine MnFe2O4 powder with its crystallites less than 100 nm was prepared using a combustion process. The coprecipitates containing the stoichiometric amount of Mn2+ and Fe3+ to form MnFe2O4 were prepared by dissolving the required metallic nitrates in de-ionized water and adding NH4OH to adjust the pH of the solutions to 9. The collected dried precipitates were then heated up to predetermined temperatures and then quickly contacted with the acetone spray. Upon contacting with the heated precipitates, the acetone spray was ignited. The combustion of acetone caused the precipitates to form crystalline MnFe2O4 without chemical segregation. The crystallinity of MnFe2O4 powder so obtained depended on the ignition temperature of acetone spray. MnFe2O4 powder obtained at acetone ignition temperature of 773 K had higher crystallinity than that obtained at acetone ignition temperature of 523 K. The presence of a small amount of Mg2+ or Zn2+ in the composition of the coprecipitates promoted the mobility of constituent ions of the combusted powder and resulted in bigger MnFe2O4 crystallites at a lower acetone ignition temperature.

Type
Articles
Information
Journal of Materials Research , Volume 15 , Issue 1 , January 2000 , pp. 170 - 175
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Mendelovici, E., Villalba, R., and Sagarzazu, A., J. Mater. Sci. Lett. 9, 28 (1990).CrossRefGoogle Scholar
2.Komarneni, S., Fregeau, E., Breval, E., and Roy, R., J. Am. Ceram. Soc. 7, C–26 (1988).Google Scholar
3.Sproson, D.W., Messing, G.L., and Gardner, T.J., Ceram. Int. 12, 3 (1986).CrossRefGoogle Scholar
4.Gadalla, A.M. and Yu, H., J. Mater. Res. 5, 2923 (1990).CrossRefGoogle Scholar
5.Yu, H. and Gadalla, A.M., J. Mater. Res. 11, 663 (1996).CrossRefGoogle Scholar
6.Gallagher, P.K., O'Bryan, H.M. Jr., Schrey, F., and Monforte, F.R., Ceram. Bull. 48, 1053 (1969).Google Scholar
7.Tesung, A.C.C and Goldstein, J.R., J. Mater. Sci. 7, 1383 (1972).Google Scholar
8.Johnson, D.W. Jr., Ceram. Bull. 60, 221 (1981).Google Scholar
9.Rigby, E.B., Kehr, W.D., and Meldrum, C.B., IEEE Trans. Magn. 20, 1506 (1984).CrossRefGoogle Scholar
10.Sato, T., Haneda, K., Seki, M., and Iijima, T., Appl. Phys. A. 50, 13 (1990).CrossRefGoogle Scholar
11.Torii, Y., Tsuzuki, A., Kato, K., Uwamino, Y., Choi, B.H., and Lee, M.J., J. Mater. Sci. 31, 2603 (1996).CrossRefGoogle Scholar
12.Chaudhuri, S.P. and Roy, I., Br. Ceram. Trans. 94, 250 (1995).Google Scholar
13.Bakare, P.P., Deshpande, C.E., Shrotri, J.J., Gupta, M.P., and Date, S.K., Ceram. Int. 13, 247 (1987).CrossRefGoogle Scholar
14.Sankarshana Murthy, M.N., Deshpande, C.E., Bakare, P.P., and Shrotri, J.J., Bull. Chem. Soc. Jpn. 52, 571 (1979).CrossRefGoogle Scholar
15.Tang, Z.X., Sorensen, C.M., Kilabunde, K.J., and Hadjipanayis, G.C., J. Colloid Interface Sci. 146, 38 (1991).CrossRefGoogle Scholar