Toughness determination of zirconia toughened alumina ceramics from growth of indentation-induced cracks

Published online by Cambridge University Press:  31 January 2011

D. Basu  and
B. K. Sarkar
D. Basu
Affiliation:
Central Glass and Ceramic Research Institute, Jadavpur University, Calcutta 700032, India
B. K. Sarkar
Affiliation:
Central Glass and Ceramic Research Institute, Jadavpur University, Calcutta 700032, India
Get access

Abstract

Short surface cracks were generated by Vickers indentation on the polished surface of alumina and different zirconia toughened alumina (ZTA) specimens, and their morphology was studied by serial sectioning. These cracks were grown in three-point bend tests under stepwise loading, and variation of toughness with crack extension was plotted to graphically separate the contributions from residual stress intensity and applied stress intensity factors. The plateau toughness determined from the intercept height of the crack extension plots exhibited an upward trend with zirconia content up to 15 vol % ZrO2 addition in the composition, which was proportional to the fraction of transformable tetragonal grains contributing to transformation toughening.

Type
Articles
Information
Journal of Materials Research , Volume 11 , Issue 12 , December 1996 , pp. 3057 - 3063
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Claussen, N., J. Am. Ceram. Soc. 59 (1–2), 49 (1976).CrossRefGoogle Scholar
2.Claussen, N., J. Am. Ceram. Soc. 61 (1–2), 85 (1978).CrossRefGoogle Scholar
3.Becher, P. F., J. Am. Ceram. Soc. 64 (1), 37 (1981).CrossRefGoogle Scholar
4.Lange, F. F., J. Mater. Sci. 17 (1), 247 (1982).Google Scholar
5.Steinbrech, R. W. and Schmenkel, O., J. Am. Ceram. Soc. 71 (5), C–27 (1988).Google Scholar
6.Marshall, D. B. and Swain, M. V., J. Am. Ceram. Soc. 71 (6), 399 (1988).CrossRefGoogle Scholar
7.Steinbrech, R. W., Fracture Mechanics of Ceramics, Vol. 9, Composites, R-Curve Behavior and Fatigue, edited by Bradt, R. C., Hasselman, D.P.H., Munz, D., Sakai, M., and Shevehenko, V. Y. (Plenum Press, New York).Google Scholar
8.Nihara, K., Morena, R., and Hasselman, D. P. H., J. Mater. Sci. Lett. 6, 355 (1987).Google Scholar
9.Shetty, D. K., Wright, I.G., Mincer, P. N., and Clauer, A. H., J. Mater. Sci. 20, 1873 (1985).CrossRefGoogle Scholar
10.Langier, M. T., J. Mater. Sci. Lett. 6, 355 (1987).Google Scholar
11.Tanaka, K., J. Mater. Sci. 22, 1501 (1987).Google Scholar
12.Evans, A. G. and Charles, E. A., J. Am. Ceram. Soc. 59 (7–8), 371 (1976).Google Scholar
13.Anstis, G. R., Chantikul, P., Lawn, B. R., and Marshall, D. B., J. Am. Ceram. Soc. 64 (9), 533 (1981).CrossRefGoogle Scholar
14.Cook, R. F. and Pharr, G. M., J. Am. Ceram. Soc. 73 (3), 787 (1990).Google Scholar
15.El Aslabi, A. M., Kleist, G., Steinbrech, R. W., and Nickel, H., Fortschrittsberichte der Deutschen KeramischenGesellschaft 6 (1) (1991).Google Scholar
16.Krause, R. F., J. Am. Ceram. Soc. 69 (9), 533 (1981).Google Scholar
17.Cook, R. F., Fairbanks, C. J., Lawn, B. R., and Mai, Y. W., J. Mater. Res. 2, 345 (1987).Google Scholar
18.Steinbrech, R. W., Krehans, R., and Schaarwachter, , J. Mater. Sci. (18), 265 (1983).Google Scholar
19.Kaliszewski, M. S., Behress, G., Heuer, A. H., Shaw, M. C., Marshall, D. B., Dransmann, G. W., and Steinbrech, R. W., J. Am. Ceram. Soc. 77 (5), 1185 (1994).CrossRefGoogle Scholar
20.Dransmann, G. W., Steinbrech, R. W., Pajares, A., Guiberteau, F., Rodriguez, A. D., and Heuer, A. H., J. Am. Ceram. Soc. 77 (5), 1194 (1994).Google Scholar
21.Fullman, R. L., J. Metall. Trans. AIME 197 (3), 447 (1953).Google Scholar
22.Lawn, B. R., Evans, A. G., and Marshall, D. B., J. Am. Ceram. Soc. 63 (9–10), 574 (1980).Google Scholar
23.Arora, A., Marshall, D. B., and Lawn, B. R., J. Non-Cryst. Solids 31, 415 (1979).Google Scholar
24.Cook, R. P. and Lawn, B. R., J. Am. Ceram. Soc. 66 (11), C–200 (1981).Google Scholar
25.Marshall, D. B. and Lawn, B. R., J. Mater. Sci. 14, 2001 (1979).Google Scholar
26.Marshall, D. B. and Swain, M. V., J. Am. Ceram. Soc. 71 (6), 399 (1988).Google Scholar
27.Lange, F. F., J. Mater. Sci. 17, 247 (1982).Google Scholar