Synthesis and characterization of Cr–B–N coatings deposited by reactive arc evaporation

Published online by Cambridge University Press:  31 January 2011

K. Polychronopoulou*
Affiliation:
Christian Doppler Laboratory for Advanced Hard Coatings, Department of Physical Metallurgy and Materials Testing, University of Leoben, A-8700 Leoben, Austria; and Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678 Nicosia, Cyprus
J. Neidhardt
Affiliation:
Christian Doppler Laboratory for Advanced Hard Coatings, Department of Physical Metallurgy and Materials Testing, University of Leoben, A-8700 Leoben, Austria
C. Rebholz
Affiliation:
Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678 Nicosia, Cyprus
M.A. Baker
Affiliation:
The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guilford GU2 4DL, United Kingdom
M. O’Sullivan
Affiliation:
PLANSEE Composite Materials GmbH, D-86983 Lechbruck, Germany
A.E. Reiter
Affiliation:
Oerlikon Balzers AG, FL-9496 Balzers, Liechtenstein
A.E. Gunnaes
Affiliation:
University of Oslo, Department of Physics, Blindern, NO-0316 Oslo, Norway
K. Giannakopoulos
Affiliation:
Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678 Nicosia, Cyprus; and IMS/NCSR Demokritos, Terma Patriarchou Grigoriou, Aghia Paraskevi, 15310 Athens, Greece
C. Mitterer
Affiliation:
Christian Doppler Laboratory for Advanced Hard Coatings, Department of Physical Metallurgy and Materials Testing, University of Leoben, A-8700 Leoben, Austria
*
a)Address all correspondence to this author. e-mail: kyriakip@ucy.ac.cy
Get access

Abstract

Nanocomposite Cr–B–N coatings were deposited from CrB0.2 compound targets by reactive arc evaporation using an Ar/N2 discharge at 500 °C and −20 V substrate bias. Elastic recoil detection (ERDA), x-ray photoelectron spectroscopy (XPS), x-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), and selected-area electron diffraction (SAED) were used to study the effect of the N2 partial pressure on composition and microstructure of the coatings. Cross-sectional scanning electron microscopy (SEM) showed that the coating morphology changes from a glassy to a columnar structure with increasing N2 partial pressure, which coincides with the transition from an amorphous to a crystalline growth mode. The saturation of N content in the coating confirms the formation of a thermodynamically stable CrN–BN dual-phase structure at higher N2 fractions, exhibiting a maximum in hardness of approximately 29 GPa.

Type
Articles
Copyright
Copyright © Materials Research Society 2008

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Su, Y.L., Yao, S.H.: On the performance and application of CrN coating. Wear 205, 112 1997CrossRefGoogle Scholar
2Polcar, T., Kubart, T., Novak, R., Kopecky, L., Siroky, P.: Comparison of tribological behaviour of TiN, TiCN and CrN at elevated temperatures. Surf. Coat. Technol. 193, 192 2005CrossRefGoogle Scholar
3Pradhan, S.K., Nouveau, C., Vasin, T.A., Djouadi, M-A.: Deposition of CrN coatings by PVD methods for mechanical application. Surf. Coat. Technol. 200, 141 2005CrossRefGoogle Scholar
4Gorishnyy, T.Z., Minut, D., Rohde, S.L., Aouadi, S.M.: Physical and mechanical properties of reactively sputtered chromium boron nitride thin films. Thin Solid Films 445, 96 2003CrossRefGoogle Scholar
5Rother, B., Kappl, H.: Results on the thermal stability of cathodic arc-deposited (Cr,B)N coatings. Surf. Coat. Technol. 73, 14 1995CrossRefGoogle Scholar
6Zhou, M., Nose, M., Nogi, K.: Influence of nitrogen on the structure and mechanical properties of r.f.-sputtered Cr–B–N thin films. Surf. Coat. Technol. 183, 45 2004CrossRefGoogle Scholar
7Budna, K.P., Mayrhofer, P.H., Neidhardt, J., Hegedũs, É., Kovács, I., Tóth, L., Pécz, B., Mitterer, C.: Effect of nitrogen-incorporation on structure, properties and performance of magnetron sputtered CrB2. Surf. Coat. Technol. 202, 3088 2008CrossRefGoogle Scholar
8Budna, K.P., Neidhardt, J., Mayrhofer, P.H., Mitterer, C.: Synthesis-structure-property relations for Cr–B–N coatings sputtered reactively from a Cr/B target with 20 at.% B. Vacuum 82, 771 2008CrossRefGoogle Scholar
9Mayrhofer, P., Mitterer, C., Clemens, H.: Self-organized nanostructures in hard ceramic coatings. Adv. Eng. Mater. 7, 1071 2005CrossRefGoogle Scholar
10Eberhart, M.E., Vvedensky, D.D.: Localized grain-boundary electronic states and intergranular fracture. Phys. Rev. Lett. 85, 61 1987CrossRefGoogle Scholar
11George, E.P., White, C.L., Horton, J.A.: Grain boundary cohesion and fracture in ordered intermetallics. Scr. Metall. Mater. 25, 1259 1991CrossRefGoogle Scholar
12Rogl, P., Schuster, J.C.: Phase Diagrams of Ternary Boron Nitride and Silicon Nitride Systems ASM Materials Park, OH 1992Google Scholar
13Brotherton, R.J., Steinberg, H.: Progress in Boron Chemistry 2, Pergamon Press NewYork 1970Google Scholar
14Neidhardt, J., Czigány, Z., Sartory, B., Tessadri, R., O’Sullivan, M., Mitterer, C.: Nanocomposite Ti–B–N coatings synthesized by reactive arc evaporation. Acta Mater. 54, 4193 2006CrossRefGoogle Scholar
15Rebholz, C., Monclus, M.A., Baker, M.A., Mayrhofer, P.H., Gibson, P.N., Leyland, A., Matthews, A.: Hard and superhard TiAlBN coatings deposited by twin electron-beam evaporation. Surf. Coat. Technol. 201, 6078 2007CrossRefGoogle Scholar
16Baker, M.A.: Advanced characterisation of nanocomposite coatings. Surf. Coat. Technol. 201, 6105 2007CrossRefGoogle Scholar
17Mitterer, C., Übleis, A., Ebner, R.: Sputter deposition of wear-resistant coatings within the system Zr–B–N. Mater. Sci. Eng., A 140, 670 1991CrossRefGoogle Scholar
18Brandstetter, E., Mitterer, C., Ebner, R.: A transmission-electron-microscopy study on sputtered Zr–B and Zr–B–N films. Thin Solid Films 201, 123 1991CrossRefGoogle Scholar
19Mayrhofer, P.H., Mitterer, C., Clemens, H.: Self-organized nanostructures in hard ceramic coatings. Z. Metallkd. 96, 5 2005Google Scholar
20Mitterer, C., Mayrhofer, P.H., Beschliesser, M., Losbichler, P., Warbichler, P., Hofer, F.: Microstructure and properties of nanocomposite Ti–B–N and Ti–B–C coatings. Surf. Coat. Technol. 120, 405 1999CrossRefGoogle Scholar
21Barbour, J.C., Doyle, B.L.: Handbook of Modern Ion Beam Materials Analysis: Materials Research Society Handbook, edited by J.R. Tesmer and M.A. Nastasi (Mater. Res. Soc. Pittsburgh, PA, 1995), p. 83Google Scholar
22Bohne, W., Röhrich, J., Röschert, G.: The Berlin time-of-flight ERDA setup. Nucl. Instrum. Methods 136, 633 1998CrossRefGoogle Scholar
23Barna, A.: Topographic kinetics and practice of low angle ion beam thinning in Specimen Preparation for Transmission Electron Microscopy of Materials—III, edited by R. Anderson, B. Tracy, and J. Bravman (Mater. Res. Symp. Proc. 254, Pittsburgh, PA, 1992), 3CrossRefGoogle Scholar
24Oliver, W.C., Pharr, G.M.: Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J. Mater. Res. 19, 3 2004CrossRefGoogle Scholar
25ISO 14577-4:2002Metallic Materials—Instrumented Indentation Test for Hardness and Materials Parameters, Part 1: Test Method (International Organization for Standardization, Geneva, Switzerland, 2002)Google Scholar
26Wilcock, J.D., Campbell, D.S.: A sensitive bending-beam apparatus for measuring the stress in evaporated thin films. Thin Solid Films 3, 3 1969CrossRefGoogle Scholar
27Rebholz, C., Ziegele, H., Leyland, A., Matthews, A.: Structure, mechanical and tribological properties of nitrogen-containing chromium coatings prepared by reactive magnetron sputtering. Surf. Coat. Technol. 115, 222 1999CrossRefGoogle Scholar
28Cheetham, A.K., Day, P.: Solid State Chemistry Clarendon Press Oxford 1987Google Scholar
29Ecker, G.: The vacuum arc cathode—A phenomenon of many aspects. IEEE Trans. Plasma Sci. PS-4, 218 1976CrossRefGoogle Scholar
30Neidhardt, J., O’Sullivan, M., Reiter, A.E., Rechberger, W., Grogger, W., Mitterer, C.: Structure–property–performance relations of high-rate reactive arc-evaporated Ti–B–N nanocomposite coatings. Surf. Coat. Technol. 201, 2553 2006CrossRefGoogle Scholar
31Onyiriuka, E.C.: Aluminum, titanium boride, and nitride films sputter-deposited from multicomponent alloy targets studied by XPS. Appl. Spectrosc. 47, 35 1993CrossRefGoogle Scholar
32Sakamoto, Y., Nose, M., Mae, T., Honbo, E., Zhou, M., Nogi, K.: Structure and properties of Cr–B, Cr–B–N and multilayer Cr–B/Cr–B–N thin films prepared by r.f.-sputtering. Surf. Coat. Technol. 174, 444 2003CrossRefGoogle Scholar
33Baker, M.A., Kench, P.J., Joseph, M.C., Leyland, A., Matthews, A.: The nanostructure and mechanical properties of PVD CrCu(N) coatings. Surf. Coat. Technol. 162, 222 2003CrossRefGoogle Scholar
34Monclus, M.A., Baker, M.A., Tsotsos, C., Davison, A., Leyland, A., Matthews, A.: Investigation of the nanostructure and post-coat thermal treatment of wear-resistant PVD CrTiCuBN coatings. Surf. Coat. Technol. 200, 310 2005CrossRefGoogle Scholar
35Aouadi, S.M., Namavar, F., Haasch, R.T., Nilchiani, R., Turner, J.A., Rohde, S.L.: Characterization of CrBN films deposited by ion-beam-assisted deposition. J. Appl. Phys. 91, 1040 2002CrossRefGoogle Scholar
36Leyland, A., Matthews, A.: On the significance of H/E ratio in wear control: A nanocomposite approach to optimized tribological behavior. Wear 246, 1 2000CrossRefGoogle Scholar
37Ichimura, H., Ando, I.: Mechanical properties of arc-evaporated CrN coatings: Part I—Nanoindentation hardness and elastic modulus. Surf. Coat. Technol. 145, 88 2001CrossRefGoogle Scholar