Silicon oxycarbide glasses: Part I. Preparation and chemistry

Published online by Cambridge University Press:  31 January 2011

Gary M. Renlund
Affiliation:
General Electric Corporate Research, Schenectady, New York 12301
Svante Prochazka
Affiliation:
General Electric Corporate Research, Schenectady, New York 12301
Robert H. Doremus
Affiliation:
Materials Engineering Department, Rensselaer Polytechnic Institute, Troy, New York 12180–3590
Get access

Abstract

Silicone polymers were pyrolyzed to form silicon oxycarbides that contained only silicon, oxygen, and carbon. The starting polymers were mainly methyl trichlorosilane with a small amount of dimethyl dichlorosilane. NMR showed that the polymers had a silicon-oxygen backbone with branching and ring units. When the polymer was heated in hydrogen, toluene and isopropyl alcohol, used in production of the polymer, were given off in the temperature range 150 °C to 500 °C. Substantial decomposition of the polymer itself began only above about 700°by evolution of methane. The network of silicon-oxygen bonds and silicon-carbon bonds did not react and was preserved; the silicon-carbon bonds were linked into the silicon-oxygen network. The silicon oxycarbide was stable above 1000 °C, showing no dimensional changes above this temperature. The interior of the silicon oxycarbide was at very low effective oxygen pressure because oxygen diffused slowly in it. There was also a protective layer of silicon dioxide on the surface of the silicon oxycarbide.

Type
Articles
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Sakka, S., in Treatise on Mater. Sci. and Technol, edited by Tomozawa, M. and Doremus, R. H. (Academic Press, San Diego, CA, 1982), Vol. 22, pp. 129167.Google Scholar
2.Wynne, K. J. and Rice, R. W., Ann. Rev. Mater. Sci. 14, 297334 (1984).CrossRefGoogle Scholar
3.Brinker, C. J. and Scherer, G. W., Sol-Gel Science (Academic Press, San Diego, CA, 1990).Google Scholar
4.Ellis, R. B., “Method of Making Electrically Conductive Glass and Articles Made Therefrom”, U.S. Patent No. 2556616 (1951).Google Scholar
5.Smith, C. F., “The Vibrational Spectra of High Purity and Chemically Substituted Vitreous Silicas”, Ph.D. Thesis, Alfred Univ., Alfred, NY, 1973.Google Scholar
6.Elmer, T. H. and Meissner, H. E., J. Am. Ceram. Soc. 59, 206209 (1976).CrossRefGoogle Scholar
7.Yajima, S., Hayashi, J., and Omori, M., Chem. Lett. 9, 931 (1975).CrossRefGoogle Scholar
8.Cooper, R. F. and Chyung, K., J. Mater. Sci. 22, 31483160 (1987).CrossRefGoogle Scholar
9.Mah, T., Hecht, N. L., McCullum, D. E., Hoenigman, J. R., Kim, H. M., Katz, A. P., and Lipsitt, H. A., J. Mater. Sci. 19, 11911201 (1984).CrossRefGoogle Scholar
10.Babonneau, F., Thorne, K., and Mackenzie, J. D., Chem. of Mater. 1, 554558 (1989).CrossRefGoogle Scholar
11.Renlund, G. M., “Silicon Oxycarbide Glasses”, Ph.D. Thesis, Rensselaer Polytechnic Institute, Troy, NY, 1989.Google Scholar
12.Saunders, K. A., Organic Polymer Chemistry (Chapman and Hall, New York, 1973), pp. 347369.CrossRefGoogle Scholar
13.NMR Basic Principles and Progress, edited by Diel, P., Fluck, E., and Kosfeld, R. (Springer-Verlag, Frankfurt, Germany, 1981), p. 184ff.Google Scholar
14.Schick, H. L., Chem. Rev. 60, 331362 (1960).CrossRefGoogle Scholar
15.Doremus, R. H., in The Physics and Chemistry of SiO2 Interface, edited by Helms, C. R. and Deal, B. E. (Plenum Press, New York, 1988, pp. 1723.CrossRefGoogle Scholar
16.Barrer, R. M. and Vaughn, D. E. W., Trans. Faraday Society 63 (9), 22 752 290 (1967).CrossRefGoogle Scholar