Hot corrosion behavior of Pt-Ir modified aluminide coatings on the nickel-base single crystal superalloy TMS-82+

Published online by Cambridge University Press:  03 March 2011

Y.N. Wu*
Affiliation:
Coating Materials Group, Composites and Coatings Center, National Institute for Materials Science (NIMS), Tsukuba 305-0047, Japan
A. Yamaguchi
Affiliation:
Coating Materials Group, Composites and Coatings Center, National Institute for Materials Science (NIMS), Tsukuba 305-0047, Japan; and Graduate School of Engineering, Division of Materials Science and Engineering, Shibaura Institute of Technology, Tokyo 135-8548, Japan
H. Murakami
Affiliation:
Coating Materials Group, Composites and Coatings Center, National Institute for Materials Science (NIMS), Tsukuba 305-0047, Japan
S. Kuroda
Affiliation:
Coating Materials Group, Composites and Coatings Center, National Institute for Materials Science (NIMS), Tsukuba 305-0047, Japan
*
a) Address all correspondence to this author. e-mail: yingnawu@gmail.com
Get access

Abstract

Platinum-iridium films (Ir = 0, 32, 46, 83, 100 at.%) were deposited on the nickel-base single crystal superalloy through magnetron sputtering. After annealing and aluminizing, the Pt-Ir modified aluminide coatings mainly consisted of PtAl2 and β-(Ni,Pt,Ir)Al phases. Hot corrosion resistance of Pt-Ir modified aluminide coatings with the different Ir contents were evaluated by exposure at 1173 K in the presence of the 90%Na2SO4 + 10%NaCl (wt%) salt deposits. The corrosion kinetics curves of the specimens were plotted up to 100 h heating time. The phase constitution, morphology of corrosion products, and element concentrations along the cross section were also measured. The lowest mass gain (0.299 mg/cm2, after 100 h) was observed for Pt-46Ir aluminide coating because the dense and continuous protective Al2O3 scale formed. Phase transformation from β-(Ni,Pt)Al to γ′-(Ni,Pt)3Al, characteristics of the scale, and protection by Pt/Ir enriched layer had the important effects on the hot corrosion behavior of modified aluminide coatings.

Type
Articles
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Gobel, M., Rahmel, A., and Schutze, M.: The cyclic-oxidation behavior of several nickel-base single-crystal superalloys without and with coatings. Oxid. Met. 41, 271 (1994).CrossRefGoogle Scholar
2Sun, J.H., Jang, H.C., and Chang, E.: Effects of pretreatments on structure and oxidation behaviour of d.c.-sputtered platinum aluminide coatings. Surf. Coat. Technol. 64, 195 (1994).CrossRefGoogle Scholar
3Benoist, J., Badawi, K.F., Malié, A., and Ramade, C.: Microstructure of Pt-modified aluminide coatings on Ni-based superalloys. Surf. Coat. Technol. 182, 14 (2004).Google Scholar
4Fountain, J.G., Golightly, F.A., Scott, F.H., and Wood, G.C.: The influence of platinum on the maintenance of α-Al2O3 as a protective scale. Oxid. Met. 10, 341 (1976).CrossRefGoogle Scholar
5Tawancy, H.M., Abbas, N.M., and Rhys-Jones, T.N.: Role of platinum in aluminide coatings. Surf. Coat. Technol. 49, 1 (1991).Google Scholar
6Niu, Y., Wu, W., Boone, D., Smith, J., Zhang, J., and Chen, C.: Oxidation behavior of simple and Pt-modified aluminide coatings on IN738 at 1100 °C. J. Phys. E 3, 511 (1993).Google Scholar
7Felten, E.J.: Use of platinum and rhodium to improve oxide adherence on Ni-8Cr-6Al alloys. Oxid. Met. 10, 23 (1976).CrossRefGoogle Scholar
8Felten, E.J. and Pettit, F.S.: Development, growth, and adhesion of Al2O3 on platinum-aluminum alloys. Oxid. Met. 10, 189 (1976).CrossRefGoogle Scholar
9Chen, J.H. and Little, J.A.: Degradation of the platinum aluminide coating on CMSX4 at 1100 °C. Surf. Coat. Technol. 92, 69 (1997).CrossRefGoogle Scholar
10Zhang, Y., Haynes, J.A., Lee, W.Y., Wright, I.G., Pint, B.A., Cooley, K.M., and Liaw, P.K.: Effects of Pt incorporation on the isothermal oxidation behavior of chemical vapor deposition aluminide coatings. Metall. Mater. Trans. A 32, 1727 (2001).CrossRefGoogle Scholar
11Deb, P., Boone, D.H., and Manley, T.F.: Surface instability of platinum modified aluminide coatings during 1100 °C cyclic testing. J. Vac. Sci. Technol., A 5, 3366 (1987).CrossRefGoogle Scholar
12He, D., Guan, H., Sun, X., and Jiang, X.: Manufacturing, structure and high temperature corrosion of palladium-modified aluminide coatings on nickel-base superalloy M38. Thin Solid Films 376, 144 (2000).CrossRefGoogle Scholar
13Strangman, T.E. and Solfest, P.A.: U.S. Patent No. 4880614, 14 Nov 1989.Google Scholar
14Murakami, H., Yano, T., and Sodeoka, S.: Process dependence of Ir-based bond coatings. Mater. Trans. 45, 2886 (2004).CrossRefGoogle Scholar
15Hosoda, H., Miyazaki, S., and Hanada, S.: Potential of IrAl base alloys as ultrahigh-temperature smart coatings. Intermetallics 8, 1081 (2000).CrossRefGoogle Scholar
16Karunaratne, M.S.A. and Reed, R.C.: Interdiffusion of the platinumgroup metals in nickel at elevated temperatures. Acta Mater. 51, 2905 (2003).CrossRefGoogle Scholar
17Lee, K.N. and Worrell, W.L.: The oxidation of iridium-aluminum and iridium-hafnium intermetallics at temperatures above 1550 °C. Oxid. Met. 32, 357 (1989).CrossRefGoogle Scholar
18Chou, T.C.: The formation of discontinuous Al2O3 layers during high-temperature oxidation of IrAl alloys. J. Mater. Res. 5, 378 (1990).Google Scholar
19Yamabe-Mitarai, Y. and Aoki, H.: Solid-solution hardening of Ir by Pt and Ni. Mater. Lett. 56, 781 (2002).CrossRefGoogle Scholar
20Bharadwaj, S.R., Tripathi, S.N., and Chandrasekharaiah, M.S.: The Ir-Pt (iridium-platinum) system. J. Phase Equilib. 16, 460 (1995).CrossRefGoogle Scholar
21Wu, Y.N., Suzuki, A., Murakami, H., and Kuroda, S.: Characterization of electroplated platinum–iridium alloys on the nickel-base single crystal superalloy. Mater. Trans. 46, 2176 (2005).CrossRefGoogle Scholar
22Suzuki, A., Harada, M., Wu, Y.N., and Murakami, H.: Microstructual characterization of sputtered Pt-Ir coatings on Ni-base single crystal superalloy. Mater. Trans. 46, 1760 (2005).CrossRefGoogle Scholar
23Fisher, G., Datta, P.K., and Burnell-Gray, J.S.: An assessment of the oxidation resistance of an iridium and an iridium/platinum low-activity aluminide/MarM002 system at 1100 °C. Surf. Coat. Technol. 113, 259 (1999).Google Scholar
24Wu, F., Murakami, H., and Harada, H.: Cyclic oxidation behavior of iridium-modified aluminide coatings for nickel-base single crystal superalloy TMS-75. Mater. Trans. 44, 1675 (2003).Google Scholar
25Kuppusami, P. and Murakami, H.: A comparative study of cyclic oxidized Ir aluminide and aluminized nickel base single crystal superalloy. Surf. Coat. Technol. 186, 377 (2004).CrossRefGoogle Scholar
26Bucher, E., Brinkman, W.F., Maita, J.P., and Cooper, A.S.: Properties of the Ni-Ir alloy system. Phys. Rev. B 1, 274 (1970).CrossRefGoogle Scholar
27Gurrappa, I.: Hot corrosion behavior of CM 247 LC alloy in Na2SO4 and NaCl environments. Oxid. Met. 51, 353 (1999).CrossRefGoogle Scholar
28Goebel, J.A., Pettit, F.S., and Goward, G.W.: Mechanisms for the hot corrosion of nickel-base alloys. Metall. Trans. 4, 261 (1973).CrossRefGoogle Scholar
29Tolpygo, V.K. and Clarke, D.R.: Surface rumpling of a (Ni, Pt)Al bond coat induced by cyclic oxidation. Acta Mater. 48, 3283 (2000).CrossRefGoogle Scholar
30Pint, B.A., Martin, J.R., and Hobbs, L.W.: The oxidation mechanism of θ-Al2O3 scales. Solid State Ionics 78, 99 (1995).CrossRefGoogle Scholar
31Hancock, P.: Vanadic and chloride attack of superalloys. Mater. Sci. Technol. 3, 536 (1987).Google Scholar
32Wu, W.T., Rahmel, A., and Schrorr, M.: Role of platinum in the Na2SO4-induced hot corrosion resistance of aluminum diffusion coatings. Oxid. Met. 22, 59 (1984).CrossRefGoogle Scholar
33Deb, P. and Boone, D.H.: Platinum aluminide coating structural effects on hot corrosion resistance at 900 °C. J. Vac. Sci. Technol., A 3, 2578 (1985).Google Scholar
34Abe, T., Ode, M., Yamabe-Mitarai, Y., and Murakami, H.: to be published.Google Scholar
35Gleeson, B., Wang, W., Hayashi, S., and Sordelet, D.: Effects of platinum on the interdiffusion and oxidation behavior of Ni-Al-based alloys. Mater. Sci. Forum 461–464, 213 (2004).CrossRefGoogle Scholar
36Murakami, H., Honma, T., Koizumi, Y., and Harada, H.: Distribution of platinum group metals in Ni- base single-crystal superalloys. Proceedings of the International Symposium on Superalloys (2000).CrossRefGoogle Scholar