Constrained-film sintering of cordierite glass-ceramic on silicon substrate

Published online by Cambridge University Press:  31 January 2011

Jesus Noel Calata ,
Allen Matthys  and
Guo-Quan Lu
Jesus Noel Calata
Affiliation:
Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University, Blacksburg, Virginia 24061
Allen Matthys
Affiliation:
Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University, Blacksburg, Virginia 24061
Guo-Quan Lu
Affiliation:
Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University, Blacksburg, Virginia 24061
Get access

Abstract

The densification behavior of cordierite glass-ceramic films constrained on a rigid silicon substrate was studied in the temperature range from 900 °C to 1000 °C. An optical setup was used to obtain the thickness versus time profiles and in-plane stresses of the constrained glass-ceramic during isothermal sintering. The thickness profiles showed a rapid shrinkage due to sintering followed by an expansion corresponding to crystallization of the glass-ceramic. Measurements of in-plane stresses in constrained-sintering films showed a rapidly rising tensile stress during densification followed by a slight drop during crystallization. In films sintered above 950 °C, the tensile stress rose rapidly again near the end of crystallization, suggesting a further densification in a mostly crystallized film. Scanning electron microscope (SEM) micrographs of the film cross sections revealed the formation and growth of large pores along the interface between the glass-ceramic and silicon substrate that may have contributed to the observed film expansion. These pores are substantially larger than the initial pore size in the films, indicating that they were formed during sintering. We believe that poor wetting of the glass-ceramic on silicon may have contributed to the formation of the porous structure at the interface.

Type
Articles
Information
Journal of Materials Research , Volume 13 , Issue 8 , August 1998 , pp. 2334 - 2341
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Tummala, R. R., in Microelectronics Packaging Handbook, edited by Tummala, R. R. and Rymaszewski, E. J. (Van Nostrand Reinhold, New York, 1989), Chap. 7.Google Scholar
2.Licari, J. J. and Enlow, L. R., Hybrid Microcircuit Technology Handbook (Noyes Publications, Park Ridge, NJ, 1988).Google Scholar
3.Partridge, G., Elyard, C. A., and Budd, M. I., in Glasses and Glass-Ceramics, edited by Lewis, M. H. (Chapman and Hall, London, 1989), Chap. 7.Google Scholar
4.Kingery, W. D., Bowen, H. K., and Uhlmann, D. R., Introduction to Ceramics, 2nd ed. (Wiley, New York, 1976), Chap. 10.Google Scholar
5.Lu, G-Q., Sutterlin, R. C., and Gupta, T. K., J. Am. Ceram. Soc. 76 (8), 1907–1914 (1993).CrossRefGoogle Scholar
6.Rahaman, M. N. and De Jonghe, L. C., J. Am. Ceram. Soc. 69 (1), 53–58 (1986).CrossRefGoogle Scholar
7.Bordia, R. K. and Raj, R., J. Am. Ceram. Soc. 68 (6), 287–292 (1985).Google Scholar
8.Hsueh, C. H., Scripta Metall. 19, 1213–1217 (1985).CrossRefGoogle Scholar
9.Scherer, G. W. and Garino, T., J. Am. Ceram. Soc. 68 (4), 216–220 (1985).CrossRefGoogle Scholar
10.Bang, J. and Lu, G-Q., J. Mater. Res. 10, 1321 (1995).CrossRefGoogle Scholar
11.Choe, J., Calata, J. N., and Lu, G-Q., J. Mater. Res. 10, 986 (1995).CrossRefGoogle Scholar
12.Beall, G. H. and Duke, D. A., in Glass Forming Systems, Vol. 1, edited by Uhlmann, D. R. and Kreidl, N. J. (Academic, New York, 1983).Google Scholar
13.Knickerbocker, S. H., Kumar, A. H., and Herron, L. W., Am. Ceram. Soc. Bull. 72, (1), 90–95 (1993).Google Scholar
14.Tummala, R. R., J. Am. Ceram. Soc. 74 (5), 895–908 (1991).Google Scholar
15.Ceramic Processing Before Firing, edited by Onoda, G-Y. and Hench, L. L. (Wiley, New York, 1978).Google Scholar
16.Reed, J. S., Principles of Ceramic Processing (Wiley, New York, 1978).Google Scholar
17.Garino, T. J. and Bowen, H. K., J. Am. Ceram. Soc. 73 (2), 251–257 (1990).CrossRefGoogle Scholar
18.Ohring, M., The Materials Science of Thin Films (Academic Press, San Diego, CA, 1992), pp. 403–450.CrossRefGoogle Scholar
19.Calata, J. N. and Lu, G-Q., unpublished.Google Scholar
20.Brantley, W. A., J. Appl. Phys. 44 (1), 534–535 (1973).CrossRefGoogle Scholar
21.Kluge, M. D., Ray, J. R., and Rahman, A., J. Chem. Phys. 85 (7), 4028–4031 (1986).CrossRefGoogle Scholar
22.Over, H-H., Knotek, O., and Lugscheider, E., Z. Metallkde. 73 (9), 552–557 (1982).Google Scholar
23.Bordia, R. K. and Jagota, A., J. Am. Ceram. Soc. 76 (10), 2475–2485 (1993).Google Scholar
24.Jagota, A., Mikeska, K., and Bordia, R. K., J. Am. Ceram. Soc. 73 (8), 2266–2273 (1990).CrossRefGoogle Scholar
25.Scherer, G. W., J. Non-Cryst. Solids 34, 239–256 (1979).CrossRefGoogle Scholar
26.Bang, J. and Lu, G-Q., J. Am. Ceram. Soc. 78 (3), 813–815 (1995).CrossRefGoogle Scholar