The Problem of High Temperature Alloys for Gas Turbines
Published online by Cambridge University Press: 03 February 2016
Abstract
It is now a matter of history that the development of an efficient gas turbine for use in aircraft engines had to await the availability of materials with the properties which would give an adequate life under the conditions which have to be imposed for efficient and economic service. These conditions are, of their type, more severe than any so far imposed on materials in other mechanical equipment. For efficient operation the gases employed in the turbine must be at a high temperature and the flow of gas passing through must be large. In aircraft engines also, the turbine must operate at high speed, with the resulting accompaniment of high stresses. It was to the metallurgist that the engineer naturally turned first for materials to meet these conditions of high temperatures and high stresses and, although some attention has been given to non-metallic substances, the problem still remains essentially a metallurgical one.
- Type
- Research Article
- Information
- Copyright
- Copyright © Royal Aeronautical Society 1948
References
1.
Kanter, J. J. and Sticha, E. A.
Creep rates from tests of short duration. Trans. Amer. Soc. Metals, 1940, XXVIII, 257–271.Google Scholar
Glen, J.
Fundamentals of high temperature testing of steel. Jnl. West Scotland Iron and Steel Inst., 1940-41, XLVIII, 19–34.Google Scholar
Krisch, A.
Determination of creep strength of steel at temperatures above 600°C. Archiv. f.d. Eisenhiittenwesen, 1940-41, XIV, 325–333.Google Scholar
McVetty, P. G.
Interpretation of creep test data. Proc. Amer. Soc. Testing Materials, 1943, XLIII, 707–727.Google Scholar
A.S.T.M. and A.S.M.E. Joint Research Ctte.
Correlation of short- and long-time elevated temperature test methods. Proc. Amer. Soc. Testing Materials, 1944, XLIV, 186–214.Google Scholar
2. See Steels for use at elevated temperatures. Jnl. Iron and Steel Inst., 1947, CLVI, 321–369.Google Scholar
3.
Oliver, D. A. and Harris, G. T.
High creep strength austenitic gas turbine forgings. Trans. Inst. Marine Eng., 1947, LIX, 79–89.Google Scholar
Oliver, D. A. and Harris, G. T.
The development of a high creep strength austenitic steel for gas turbines. West of Scotland Iron and Steel Inst., Advance copy, 1947; Metallurgia, 1947, XXXV, 235–238.Google Scholar
4.
Tapsell, H. J. and Bradley, J.
Mechanical tests at high temperatures on a non-ferrous alloy of nickel and chromium. Engineering, 1925, CXX, 614–615; 648-649; 746-747.Google Scholar
6.
Hall, C. C.
Gas turbines—Use of steel under high temperature conditions. Iron and Steel, 1946, XIX, 455–457; 499–501; 505.Google Scholar
7. Symposium on Materials for gas turbines. Amer. Soc. Testing Materials, 1946.Google Scholar
8.
Collection of Reports on design of, and materials for, gas turbines and other hightemperature service. Trans. Amer. Soc. Mech. Eng., 1947, LXIX, 549–612.Google Scholar
9.
Grant, N. J.
High temperature alloys. Iron Age, 1946, CLVII, May 23, 42–48; May 30, 50-56; June 6, 77-80; June 20, 60-63.Google Scholar
10.
Bollenrath, F., Cornelium, H. and Bungardt, W.
Study of the suitability of heat-resisting materials for internal combustion engines. Luftfahrtforschung, 1938, XV, 468–480, 505-510; 1941, XVIII, 275-279, 305-310.Google Scholar
11.
Bennek, H. and Bandel, G.
The influence of the genesis of structure resulting from heattreatment and alloy content on the creep strength of steel. Stahl und Eisen, 1943, LXIII, 653–659, 673-684, 695-700; Tech. Mitt. Krupp, 1943, VI, 143-176. 18Google Scholar