Amplification Path Length Dependence Studies of Stimulated Emission from Optically Pumped InGaN/GaN Multiple Quantum Wells

Published online by Cambridge University Press:  13 June 2014

T.J. Schmidt
Affiliation:
Center for Laser and Photonics Research and Dept. of Physics Oklahoma State University, Stillwater, OK 74078
S. Bidnyk
Affiliation:
Center for Laser and Photonics Research and Dept. of Physics Oklahoma State University, Stillwater, OK 74078
Yong-Hoon Cho
Affiliation:
Center for Laser and Photonics Research and Dept. of Physics Oklahoma State University, Stillwater, OK 74078
A.J. Fischer
Affiliation:
Center for Laser and Photonics Research and Dept. of Physics Oklahoma State University, Stillwater, OK 74078
J.J. Song
Affiliation:
Center for Laser and Photonics Research and Dept. of Physics Oklahoma State University, Stillwater, OK 74078
S. Keller
Affiliation:
Electrical and Computer Engineering and Materials Depts. University of California, Santa Barbara, CA 93106
U.K. Mishra
Affiliation:
Electrical and Computer Engineering and Materials Depts. University of California, Santa Barbara, CA 93106
S.P. DenBaars
Affiliation:
Electrical and Computer Engineering and Materials Depts. University of California, Santa Barbara, CA 93106

Abstract

Optically pumped stimulated emission (SE) from InGaN/GaN multiple quantum wells (MQWs) grown by metalorganic chemical vapor deposition has been systematically studied as a function of excitation length (Lexc). Two distinct SE peaks were observed from these structures: one that originates at 425 nm at 10 K (430 nm at 300 K) and another that originates at 434 nm at 10 K (438 nm at 300 K). The SE threshold for the high energy peak was observed to always be lower than that of the low energy peak, but the difference was found to decrease greatly with increasing Lexc. A detailed study of the emission intensity of these two SE peaks as a function of excitation density shows that the two peaks compete for gain in the MQW active region.

Type
Research Article
Copyright
Copyright © 1999 Materials Research Society

Introduction

GaN-based semiconductors and related heterostructures are attracting an ever-increasing amount of attention due to their large direct band gaps, which make them promising materials for UV-blue-green light emitting devices,Reference Nakamura, Senoh, Iwasa, Nagahama, Yamada and Mukai 1 , Reference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku 2 solar-blind UV detectors,Reference Lim, Chen, Yang and Khan 3 and high power and high temperature devices.Reference Wu, Keller, Keller, Kapolnek, Kozodoy, DenBaars and Mishra 4 , Reference Yang, Schmidt, Shan, Song and Goldenberg 5 In particular, the realization of high brightness blue and green light emitting diodesReference Nakamura, Senoh, Iwasa, Nagahama, Yamada and Mukai 1 and cw blue laser diodesReference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku 2 based on InGaN/GaN multiple quantum wells (MQWs) has focused the efforts of many research groups on these structures. Although a considerable amount of research has been conducted on the optical properties of these materials, there is still much left unknown about the optical processes associated with stimulated emission (SE) and lasing. To aid in a fundamental understanding of the processes leading to optical gain in these structures, excitation length dependent studies of optically pumped SE have been performed and illustrate dramatically different SE behavior for changes in the experimental conditions that would typically be insignificant in other semiconductor materials.

Recently, a considerable amount of attention has been given to the potential role of strongly localized band tail states on the SE and lasing processes in InGaN MQWs.6−11 Although there exists a sizable amount of data to support localized carrier recombination as the mechanism leading to spontaneous emission in these materials,Reference Chichibu, Azuhata, Sota and Nakamura 8 , Reference Narukawa, Kawakami, Funato, Fujita, Fugita and Nakamura 9 , Reference Jeon, Kozlov, Song, Vertikov, Kuball, Nurmikko, Liu, Chen, Kern, Kuo and Craford 12 , Reference Narakawa, Kuwakima, Fujita, Fujita and Nakamura 13 the results for SE behavior in the literature are varied and often contradictory. This has led some research groups to assign the spontaneous emission peak to recombination of localized carriers, and the SE peak to a more traditional recombination mechanism: that of an electron-hole plasma originating from free carriers,Reference Im, Heppel, Kollmer, Sohmer, Off, Scholz and Hangleiter 14 while others claim that strongly localized carriers are the origin of both spontaneous and SE.Reference Narukawa, Kawakami, Funato, Fujita, Fugita and Nakamura 9 - Reference Deguchi, Azuhata, Sota, Chichibu, Arita, Nakanishi and Nakamura 11 With the recent observation of two different SE peaks from InGaN/GaN MQWs grown by Nichia Chemical IndustriesReference Deguchi, Azuhata, Sota, Chichibu, Arita, Nakanishi and Nakamura 11 we see the possibility that some of the varied results reported in the literature may stem from slightly different experimental conditions, which are shown here to result in significant changes in the SE behavior. We report the results of a detailed study of the SE behavior of these two SE peaks as a function of excitation length (Lexc) and excitation density (Iexc) and illustrate dramatically different SE behavior in InGaN MQWs for relatively small changes in the experimental conditions. The observation of these two distinct SE peaks from InGaN/GaN MQWs grown under different conditions by separate research groups suggests this SE behavior is a general property of present state-of-the-art InGaN based blue laser diodes. As such, a better understanding of the SE and lasing behavior of these structures is important for the development and optimization of future laser diode structures.

Experiment

The InGaN/GaN MQWs used in this study were grown by metalorganic chemical vapor deposition (MOCVD) on 1.8 μm thick GaN buffer layers grown on (0001) oriented sapphire substrates. The active regions were made up of 12 quantum wells consisting of 3 nm thick In0.2Ga0.8N wells and 4.5 nm thick GaN barriers. The structures were capped by G6.54.1 μm thick Al0.07Ga0.93N layers. A detailed description of the growth conditions is given elsewhere.Reference Keller, Abare, Minsky, Wu, Mack, Speck, Hu, Coldren, Mishra and DenBaars 15 The InGaN MQWs were optically pumped by the third harmonic of an injection seeded Nd:YAG laser (355 nm, 30 Hz, ∼ 6 ns pulse width). The excitation beam was focused to a line on the sample using a cylindrical lens and the excitation length was varied using a mask connected to a computer controlled stepper motor. The emission was collected from one edge of the sample, coupled into a 1-meter spectrometer, and spectrally analyzed using an optical multi-channel analyzer.

Results

Typical power dependent emission spectra at 10 K are shown in Fig. 1 for Lexc = 1300 μm. At low Iexc, we observe a broad spontaneous emission peak centered at ∼ 441 nm, consistent with low power cw photoluminescence (PL) spectra. As Iexc is increased, a new peak emerges at ∼ 428 nm [designated here as SE peak (1)] and grows superlinearly with increasing Iexc. If we continue to increase Iexc, we observe another new peak at ∼ 433 nm [designated here as SE peak (2)] which also grows superlinearly with increasing Iexc. SE peak (1) is observed to be the statistical distribution of a multitude of narrow (< G6.54.1 nm) emission lines. No significant broadening of these emission lines was observed as the temperature was tuned from 10 K to over 500 K. This is illustrated in Fig. 2. SE peak (2) is observed to always be considerably narrower than SE peak (1). Both SE peaks are seen to originate on the high energy side of the low power spontaneous emission peak (given by the dashed line in Fig. 1) and are seen to be redshifted by more than 30 nm below the start of the “soft” absorption edge. Both SE peaks were found to be highly TE polarized, with a TE to TM ratio of ∼ 200. SE peak (2) has been the subject of previous experiments performed by the authors and has been attributed to stimulated recombination of localized states through the use of energy selective optically pumped SE studies showing “mobility edge” type behavior in the SE spectra as the excitation photon energy is varied,Reference Schmidt, Cho, Gainer, Song, Keller, Mishra and DenBaars 16 and through nanosecond nondegenerate optical pump-probe experiments showing the onset of SE has a direct impact on the bleaching dynamics of the band tail states in these samples.Reference Schmidt, Cho, Gainer, Song, Keller, Mishra and DenBaars 17

Figure 1: 10 K stimulated emission spectra (solid lines) from an InGaN/GaN MQW subjected to several excitation densities, where Io = 100 kW/cmReference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku 2 . The low power PL (dashed line) and PLE (dotted line) spectra are also shown for comparison. The SE spectra have been normalized and displaced vertically for clarity.

Figure 2: Stimulated emission spectra of SE peak (1) at (a) 200 K, (b) 300 K, and (c) 450 K illustrating SE peak (1) is composed of a multitude of narrow (< G6.54.1 nm) stimulated emission peaks that do not noticeably broaden with increasing temperature. The SE spectra shown were collected for excitation densities twice the SE threshold for the respective temperatures. The spontaneous emission spectra (dotted lines) are also shown for excitation densities half that of the SE threshold at each temperature. The SE spectra have been normalized for clarity.

Figure 3(a) shows the SE thresholds (Ith ) of SE peaks (1) and (2) as a function of Lexc. We note that Ith for peak (2) is larger than that of peak (1) for all excitation lengths employed, but approaches that of peak (1) with increasing Lexc. The high SE threshold of peak (2) with respect to peak (1) and its increased presence for longer Lexc suggest that it results from a lower gain process than that of peak (1). Fig. 3(b) shows the peak positions of SE peak (1) and SE peak (2) as a function of Lexc at 10 K. For Lexc less than ∼ 500 μm, only SE peak (1) is observed. It has a peak emission wavelength of ∼ 425 nm (430 nm) and a SE threshold of ∼ 100 kW/cmReference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku 2 (475 kW/cmReference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku 2 ) at 10 K (300 K). As Iexc is increased and/or Lexc is increased, a new SE peak [SE peak (2)] at 434 nm (438 nm at RT) emerges. The peak positions were measured for Iexc fixed relative to the SE thresholds of the respective peaks; i.e. Iexc = 2 × Ith . As Lexc is increased, SE peak (1) shifts to longer wavelengths (due to a re-absorption process), while the peak position of SE peak (2) is observed to be weakly dependent on Lexc. The apparent blueshift of SE peak (2) with increasing Lexc seen in Fig. 3(b) is a result of the experimental conditions. Since the SE threshold of SE peak (2) is a strong function of Lexc, the peak positions shown for small Lexc are for Iexc considerably higher than for large Lexc. The slight redshift of SE peak (2) with increasing Iexc due to many-body effects and lattice heating then manifests itself as the apparent blueshift seen in Fig. 3(b). The same phenomenon is observed at room temperature, as shown in the inset of Fig. 3(b). The redshift of SE peak (1) with increasing Lexc can be explained by gain and absorption competition in the “soft” absorption edge of the InGaN active regions, where gain saturation with longer Lexc combined with the background absorption tail leads to the observed redshift. The fact that SE peak (2) does not experience a re-absorption induced redshift with increasing Lexc is explained by the significant reduction of the absorption tail in this spectral region (see Fig. 1).

Figure 3: (a) Stimulated emission threshold as a function of excitation length for SE peaks (1) and (2) at 10 K. (b) Peak position of SE peaks (1) and (2) as a function of excitation length at 10 K. The insets show the behavior observed at room temperature. The solid lines are given only as guides for the eye.

The gain saturation behavior of SE peak (1) is consistent with the observation of Kuball et al.Reference Kuball, Jeon, Song, Nurmikko, Kozodoy, Abare, Keller, Coldren, Mishra, DenBaars and Steigerwald 18 of a high gain mechanism in the band tail region of MQWs with similar active regions. The large spectral range exhibiting gain is explained by compositional fluctuations inside the active region. The redshift of SE peak (1) with increasing Lexc is consistent with observations of a redshift in the optical gain spectrum with increasing Lexc reported by Mohs et al.Reference Mohs, Aoki, Nagai, Shimano, Kuwata-Gonokami and Nakamura 19 It is also consistent with the observation by NakamuraReference Nakamura 20 that the external quantum efficiency of his cw blue laser diodes decreases with increasing cavity length. These similarities, combined with the relatively low SE threshold of SE peak (1) with respect to SE peak (2) and its similar spectral position with laser emission from diodes of similar structure,Reference Mack, Abare, Aizcorbe, Kozodoy, Keller, Mishra, Coldren and DenBaars 21 suggests that lasing in current state-of-the-art cw blue laser diodes originates from the gain mechanism responsible for SE peak (1). The microscopic origin of this gain is the subject of continuing research, but is shown here to be different than the localized state recombination responsible for SE peak (2). Its origin may lie in an entirely different degree of carrier localization. Further experiments are needed to clarify this issue.

The modal gain spectra measured by the variable-stripe method of Shaklee and LehenyReference Shaklee and Leheny 22 are shown in Fig. 4 at 10 K. The spectra were taken for Lexc less than 200 μm to minimize re-absorption induced distortions in the spectra. The excitation densities in Fig. 4 are given with respect to the SE threshold measured for long (∼ 2.5 mm) excitation lengths. A clear blueshift in the gain peak is seen with increasing excitation. This blueshift was observed to stop for Iexc > 12 × Ith. Further increases in Iexc resulted only in an increase in the modal gain maximum. The maxima of the gain spectra are seen to be redshifted by more than 20 nm with respect to the start of the “soft” absorption edge. The large shift in the gain maximum to higher energy with increasing Iexc is consistent with band filling of localized states in the InGaN active regions. We note that the fully blueshifted gain spectrum covers the entire spectral region in which SE was observed. Similar behavior was observed at room temperature.

Figure 4: 10 K modal gain spectra of an InGaN/GaN MQW at several excitation densities. The excitation densities are given with respect to the SE threshold measured for long (∼ 2.5 mm) excitation lengths.

The dependence of the emission intensity of peaks (1) and (2) on Iexc is shown in Fig. 5 for Lexc = 1300 μm at 10 K. The emission of peak (1) increases in a strongly superlinear fashion (∼ Iexc 3.8 ) until the SE threshold of peak (2) is reached, at which point it turns linear, indicating that peak (2) competes for gain with peak (1). This is most likely a result of competition for carriers or re-absorption of the emitted photons. The presence of SE peak (2) is therefore seen to be deleterious to SE peak (1). The same process is observed at room temperature and for various excitation lengths. This gain competition may limit this material’s performance in high power laser diode applications, where increased driving current and/or longer cavity lengths may result in a shift in the dominant gain mechanism and a drastic change in the emission behavior.

Figure 5: Emission intensity of SE peaks (1) and (2) as a function of optical excitation density at 10 K, illustrating gain competition. The excitation length is 1300 μm. The respective SE thresholds, Ith, of SE peaks (1) and (2) are indicated for completeness. The solid lines are given only as guides for the eye.

Conclusions

In summary, the dependence of stimulated emission on excitation length in MOCVD grown InGaN/GaN MQW structures has been studied. Two distinctly different SE peaks were observed with different dependencies on excitation length. The high energy SE peak exhibits a strong redshift with increasing excitation length due to competition between an easily saturable gain mechanism and a background absorption tail. The lower energy SE peak does not exhibit this re-absorption induced redshift with increasing excitation length. The presence of the lower energy SE peak has been shown to be detrimental to the higher energy SE peak due to gain competition in the InGaN active region. This competition may prove to be an obstacle in the design of InGaN based high power laser diodes, where high current densities and/or long cavity lengths can lead to a shift in the dominant gain mechanism and a change in the emission characteristics.

Acknowledgments

This work was supported by BMDO, AFOSR, ARO, ONR, and DARPA.

Footnotes

MRS Internet J. Nitride Semicond. Res. 4S1, G6.54 (1999)

References

Nakamura, S., Senoh, M., Iwasa, N., Nagahama, S., Yamada, T., and Mukai, T., Jpn. J. Appl. Phys. 34, L1332 (1995).Google Scholar
Nakamura, S., Senoh, M., Nagahama, S., Iwasa, N., Yamada, T., Matsushita, T., Sugimoto, Y., and Kiyoku, H., Appl. Phys. Lett. 69, 4056 (1996).Google Scholar
Lim, B.W., Chen, Q.C., Yang, J.Y., and Khan, M.A., Appl. Phys. Lett. 68, 3761 (1996).Google Scholar
Wu, Y.F., Keller, B.P., Keller, S., Kapolnek, D., Kozodoy, P., DenBaars, S.P., and Mishra, U.K., Appl. Phys. Lett. 69, 1438 (1996).Google Scholar
Yang, X.H., Schmidt, T.J., Shan, W., Song, J.J., and Goldenberg, B., Appl. Phys. Lett. 66, 1 (1995). S. Bidnyk, T.J. Schmidt, Y.H. Cho, G.H. Gainer, J.J. Song, S. Keller, U.K. Mishra, and S.P. DenBaars, Appl. Phys. Lett. 72, 1623 (1998).Google Scholar
Nakamura, S., Senoh, M., Nagahama, S.I., Iwasa, N., Yamada, T., Matsushita, T., Sugimoto, Y., and Kiyoku, H., Appl. Phys. Lett. 70, 1417 (1997).Google Scholar
Nakamura, S., Senoh, M., Nagahama, S.I., Iwasa, N., Yamada, T., Matsushita, T., Sugimoto, Y., and Kiyoku, H., Appl. Phys. Lett. 70, 2753 (1997).Google Scholar
Chichibu, S., Azuhata, T., Sota, T., and Nakamura, S., Appl. Phys. Lett. 69, 4188 (1996).Google Scholar
Narukawa, Y., Kawakami, Y., Funato, M., Fujita, S., Fugita, S., and Nakamura, S., Appl. Phys. Lett. 70, 981 (1997).Google Scholar
Satake, A., Masumoto, Y., Miyajima, T., Asatsuma, T., Nakamura, F., and Ikeda, M., Phys. Rev. B 57, R2041 (1998).Google Scholar
Deguchi, T., Azuhata, T., Sota, T., Chichibu, S., Arita, M., Nakanishi, H., and Nakamura, S., Semicond. Sci. Technol. 13, 97 (1998).CrossRefGoogle Scholar
Jeon, E.S., Kozlov, V., Song, Y.K., Vertikov, A, Kuball, M., Nurmikko, A.V., Liu, H., Chen, C., Kern, R.S., Kuo, C.P., and Craford, M.G., Appl. Phys. Lett. 69, 4194 (1996).Google Scholar
Narakawa, Y., Kuwakima, Y., Fujita, S., Fujita, S., and Nakamura, S., Phys. Rev. B 55, R1938 (1997).Google Scholar
Im, J.S., Heppel, S., Kollmer, H., Sohmer, A., Off, J., Scholz, F., and Hangleiter, A., Proc. 2nd Int. Conf. Nitride Semicond., Tokushima, Japan, 228 (1997).Google Scholar
Keller, S., Abare, A.C., Minsky, M.S., Wu, X.H., Mack, M.P., Speck, J.S., Hu, E., Coldren, L.A., Mishra, U.K., and DenBaars, S.P., Materials Science Forum 264-268, 1157 (1998). B.P. Keller, S. Keller, D. Kapolnek, W.N. Jiang, X.-F. Wu, H. Masui, X.H. Wu, B. Heying, J.S. Speck, U.K. Mishra, and S.P. DenBaars, J. Electron. Mater. 24, 1707 (1995).Google Scholar
Schmidt, T.J., Cho, Y.H., Gainer, G.H., Song, J.J., Keller, S., Mishra, U.K., and DenBaars, S.P., Appl. Phys. Lett. 73, 560 (1998).Google Scholar
Schmidt, T.J., Cho, Y.H., Gainer, G.H., Song, J.J., Keller, S., Mishra, U.K., and DenBaars, S.P., Appl. Phys. Lett. 73, 1892 (1998).Google Scholar
Kuball, M., Jeon, E.S., Song, Y.K., Nurmikko, A.V., Kozodoy, P., Abare, A., Keller, S., Coldren, L.A., Mishra, U.K., DenBaars, S.P., and Steigerwald, D.A., Appl. Phys. Lett. 70, 2580 (1997).CrossRefGoogle Scholar
Mohs, G., Aoki, T., Nagai, M., Shimano, R., Kuwata-Gonokami, M., and Nakamura, S., Proc. 2nd Int. Conf. Nitride Semicond., Tokushima, Japan, 234 (1997).Google Scholar
Nakamura, S., MRS Internet J. Nitride Semicond. Res. 2, Art. 5 (1997).Google Scholar
Mack, M.P., Abare, A., Aizcorbe, M., Kozodoy, P., Keller, S., Mishra, U.K., Coldren, L., and DenBaars, S.P., MRS Internet J. Nitride Semicond. Res. 2, Art. 41 (1997).Google Scholar
Shaklee, K.L. and Leheny, R.F., Appl. Phys. Lett. 18, 475 (1971).CrossRefGoogle Scholar
Figure 0

Figure 1: 10 K stimulated emission spectra (solid lines) from an InGaN/GaN MQW subjected to several excitation densities, where Io = 100 kW/cm2. The low power PL (dashed line) and PLE (dotted line) spectra are also shown for comparison. The SE spectra have been normalized and displaced vertically for clarity.

Figure 1

Figure 2: Stimulated emission spectra of SE peak (1) at (a) 200 K, (b) 300 K, and (c) 450 K illustrating SE peak (1) is composed of a multitude of narrow (< G6.54.1 nm) stimulated emission peaks that do not noticeably broaden with increasing temperature. The SE spectra shown were collected for excitation densities twice the SE threshold for the respective temperatures. The spontaneous emission spectra (dotted lines) are also shown for excitation densities half that of the SE threshold at each temperature. The SE spectra have been normalized for clarity.

Figure 2

Figure 3: (a) Stimulated emission threshold as a function of excitation length for SE peaks (1) and (2) at 10 K. (b) Peak position of SE peaks (1) and (2) as a function of excitation length at 10 K. The insets show the behavior observed at room temperature. The solid lines are given only as guides for the eye.

Figure 3

Figure 4: 10 K modal gain spectra of an InGaN/GaN MQW at several excitation densities. The excitation densities are given with respect to the SE threshold measured for long (∼ 2.5 mm) excitation lengths.

Figure 4

Figure 5: Emission intensity of SE peaks (1) and (2) as a function of optical excitation density at 10 K, illustrating gain competition. The excitation length is 1300 μm. The respective SE thresholds, Ith, of SE peaks (1) and (2) are indicated for completeness. The solid lines are given only as guides for the eye.