Influence of Si-Doping on Carrier Localization of Mocvd-grown InGaN/GaN Multiple Quantum Wells

Published online by Cambridge University Press:  13 June 2014

Yong-Hoon Cho
Affiliation:
Center for Laser and Photonics Research and Department of Physics Oklahoma State University, Stillwater, OK 74078
T. J. Schmidt
Affiliation:
Center for Laser and Photonics Research and Department of Physics Oklahoma State University, Stillwater, OK 74078
S. Bidnyk
Affiliation:
Center for Laser and Photonics Research and Department of Physics Oklahoma State University, Stillwater, OK 74078
J. J. Song
Affiliation:
Center for Laser and Photonics Research and Department of Physics Oklahoma State University, Stillwater, OK 74078
S. Keller
Affiliation:
Electrical and Computer Engineering and Materials Departments University of California, Santa Barbara, CA 93106
U. K. Mishra
Affiliation:
Electrical and Computer Engineering and Materials Departments University of California, Santa Barbara, CA 93106
S. P. DenBaars
Affiliation:
Electrical and Computer Engineering and Materials Departments University of California, Santa Barbara, CA 93106

Abstract

We have systematically studied the influence of Si doping on the optical characteristics of InGaN/GaN multiple quantum wells (MQWs) using photoluminescence (PL), PL excitation (PLE), and time-resolved PL spectroscopy combined with studies of optically pumped stimulated emission and structural properties from these materials. The MQWs were grown on 1.8-μm-thick GaN layers on c-plane sapphire films by metalorganic chemical vapor deposition. The structures consisted of 12 MQWs with 3-nm-thick InGaN wells, 4.5-nm-thick GaN barriers, and a 0.1-μm-thick Al0.07Ga0.93N capping layer. The Si doping level in the GaN barriers was varied from 1 × 1017 to 3 × 1019 cm−3. PL and PLE measurements show a decrease in the Stokes shift with increasing Si doping concentration. The 10 K radiative recombination lifetime was observed to decrease with increasing Si doping concentration (n), from ∼ 30 ns (for n < 1 × 1017 cm−3) to ∼ 4 ns (for n = 3 × 1019 cm−3). To elucidate whether non-radiative recombination processes affect the measured lifetime, the temperature-dependence of the measured lifetime was investigated. The reduced Stokes shift, the decrease in radiative recombination lifetime, and the increase in structural and interface quality with increasing Si doping indicate that the incorporation of Si in the GaN barriers results in a decrease in carrier localization at potential fluctuations in the InGaN active regions and the interfaces.

Type
Research Article
Copyright
Copyright © 1999 Materials Research Society

Introduction

Group III nitride semiconductors and their heterostructures have recently attracted much attention for their versatile applications as light emitting devices, solar-blind ultraviolet detectors, and high power/high temperature/high frequency devices [Reference Nakamura, Senoh, Iwasa, Nagahama, Yamada and Mukai1-Reference Morkoç, Strite, Gao, Lin, Sverdlov and Burns6]. Much interest has been focused on InGaN/GaN quantum wells (QWs) because of their applications as high brightness light emitting diodes and cw blue laser diodes [Reference Nakamura, Senoh, Iwasa, Nagahama, Yamada and Mukai1,Reference Nakamura, Senoh, Nagahama, Iwasa, Yamada, Matsushita, Sugimoto and Kiyoku2]. Detailed knowledge of the effects of Si doping on the optical properties of these materials is crucial, especially for designing practical devices. Recently, the effects of Si doping on the optical properties of GaN epilayers [Reference Ruvimov, Liliental-Weber, Suski, Ager, Washburn, Krueger, Kisielowski, Weber, Amano and Akasaki7,Reference Schubert, Goepfert, Grieshaber and Redwing8], InGaN/GaN QWs [Reference Grudowski, Eiting, Park, Shelton, Lambert and Dupuis9-Reference Bidnyk, Schmidt, Cho, Gainer, Song, Keller, Mishra and DenBaars11], and GaN/AlGaN QWs [Reference Salvador, Liu, Kim, Aktas, Botchkarev and Morkoç12,Reference Zeng, Lin, Jiang, Salvador, Popovici, Tang, Kim and Morkoç13] have been reported. However, the influence of Si doping on both optical properties and structural qualities in InGaN/GaN multiple quantum well (MQW) device structures is presently not well understood.

In this study, we present a comprehensive study of the optical properties of InGaN/GaN MQWs using photoluminescence (PL), PL excitation (PLE), and time-resolved PL (TRPL) spectroscopy, combined with studies of optically pumped stimulated emission (SE) and structural properties from these materials. In particular, the influence of Si doping in the GaN barriers on the characteristics of the MQWs is investigated. PL and PLE results show that increasing the Si doping concentration (n) reduces the Stokes shift of the InGaN emission. TRPL experiments show the 10 K recombination lifetime decreases with increasing n, from ∼ 30 ns (for n < 1 × 1017 cm−3) to ∼ 4 ns (for n = 3 × 1019 cm−3). In addition, it is shown that Si doping improves the structural and interface properties of the InGaN/GaN MQW samples from atomic force microscopy (AFM) images. From the results, we demonstrate that Si doping in the GaN barriers affects the interface quality of the InGaN/GaN MQW systems, and influences the optical properties.

Experiment

The InGaN/GaN MQWs used in this study were grown on c-plane sapphire films by metalorganic chemical vapor deposition, following the deposition of a 1.8-μm-thick GaN buffer layer. The structures consisted of 12 MQWs with 3-nm-thick In0.2Ga0.8N wells and 4.5-nm-thick GaN barriers, and a 100-nm-thick Al0.07Ga0.93N capping layer. Trimethylgallium (TMGa), trimethylindium (TMIn), trimethylaluminum, and ammonia were used as the precursors and disilane was used as the n-type dopant. The growth temperatures of the GaN base layer, the superlattice (SL) region, and the AlGaN capping layer were 1050, 790, and 1040°C, respectively. The TMGa and TMIn fluxes during the SL growth were 5 and 14 μmol/min, respectively, while the ammonia flow was held constant at 0.35 mol/min. In order to study the influence of Si doping in the GaN barriers, the disilane doping precursor flux was systematically varied from 0 to 4 nmol/min during GaN barrier growth. Accordingly, a doping concentration in the range of < 1 × 1017 to 3 × 1019 cm−3 was achieved for the different samples, which was determined by secondary ion mass spectroscopy and Hall measurements. To investigate the effect of Si doping on the GaN surface morphology, three reference 7-nm-thick GaN epilayers were also grown at 800°C, which have different disilane flux rates of 0, 0.2, and 2 nmol/min during growth. The surface morphology of the reference samples were investigated using a Digital Instruments Nanoscope III AFM operated in tapping mode and the root-mean-square surface roughness was estimated by the AFM software. Details of the growth procedure and the other structural properties are given elsewhere [Reference Keller, Abare, Minsky, Wu, Mack, Speck, Hu, Coldren, Mishra and DenBaars10,Reference Cho, Fedler, Hauenstein, Park, Song, Keller, Mishra and DenBaars14]. PL and PLE spectra were measured using the 325 nm line of a 20 mW cw He-Cd laser and the quasi-monochromatic light from a xenon lamp dispersed by a 1/2 m monochromator, respectively. TRPL measurements were carried out using a picosecond pulsed laser system consisting of a cavity-dumped dye laser for sample excitation and a streak camera for detection. The output laser pulses from the dye laser had a duration of less than 5 ps and were frequency doubled into the UV spectral region by a nonlinear crystal. The overall time resolution of the system is better than 15 ps. The temperature of the sample in the experiments described above was varied from 10 to 300 K.

Results and Discussions

Figure 1 shows 10 K PL (solid lines) and PLE (dashed lines) spectra of the main InGaN-related PL emission peak with the decay time plotted as a function of emission energy (open circles). The near-band-edge emission from the AlGaN cladding layer and the GaN barriers are also clearly seen at 3.60 and 3.48 eV, respectively. The PLE detection energy is set at the main PL peak energy. The contributions from the GaN barriers and the AlGaN capping layer are clearly distinguishable, and the band-edge PLE positions are coincident with the PL peak positions. A large Stokes shift of the PL emission from the InGaN wells with respect to the bandedge measured by PLE is clearly observed, which is attributed to crystal imperfections such as In alloy fluctuations and interface roughness. We observed that as the Si doping concentration increases, the Stokes shift decreases. The Stokes shift for the sample with n = 3 × 1019 cm−3 is ∼ 120 meV smaller than that of the nominally undoped sample (see Table I). The effect of Si doping on the decay time of the MQWs was also explored using TRPL measurements. Figure 1 (open circles) shows the 10 K decay time (τd) monitored at different emission energies. The measured lifetime becomes longer with decreasing emission energy, and hence, the peak energy of the emission shifts to the low energy side as time proceeds. This behavior is characteristic of localized states, which in this case are most likely due to alloy fluctuations and/or interface irregularities in the MQWs [Reference Cho, Gainer, Fischer, Song, Keller, Mishra and DenBaars15]. A decrease in τd with increasing Si doping, from ∼ 30 ns (for n < 1 × 1017 cm−3) to ∼ 4 ns (for n = 3 × 1019 cm−3), is clearly seen, which can be attributed to a decrease in the potential fluctuations leading to recombination.

Table I. Observed Stokes shift, measured lifetime, Tc , HRXRD FWHM, and SE threshold density for InGaN/GaN MQW samples with different Si doping concentration n by adjusting disilane flow rate FSi.

n (cm−3)(nmol FSi (nmol/min) Stokes shift at 10K (meV) Measured lifetime (nsec) Tc (K) HRXRD FWHM (arcsec) a) SE threshold density at 300 K (kW/cm2) b)
10 K 300 SL-2 SL-1 SL0
< 1 × 1017 0 ∼ 355 24 − 36 6 ∼ 70 589 312 219 58
2 × 1018 0.26 ∼ 305 7 − 18 5 ∼ 100 335 276 229 55
3 × 1019 4 ∼ 235 3−5 2 ∼ 140 234 212 227 165

Figure 1. 10 K PL (solid lines), PLE (dashed lines), and TRPL data (open circles) of 12-period InGaN/GaN MQWs with Si doping concentrations ranging from < 1 × 1017 to 3 × 1019 cm−3 in the GaN barriers. The Stokes shift between the PL emission peak and the absorption band-edge observed from PLE spectra decreases significantly as the Si doping concentration increases. Luminescence decay times measured by TRPL are shown as a function of emission energy. With increasing Si doping concentration, the 10 K lifetimes decrease from ∼ 30 ns (for n < 1 × 1017 cm−3) to ∼ 4 ns (for n = 3 × 1019 cm−3).

One should be very careful interpreting the low temperature lifetime results because the non-radiative recombination processes (which can be caused by poor sample quality) may affect the measured lifetime. To clarify this point, we investigated the temperature dependence of the lifetime as shown in Fig. 2. For the nominally undoped sample with n < 1 × 1017 cm−3 (open symbols), we observed an increase of τd with temperature (up to around 40 ns for the higher energy side emission) at temperatures below 70 K, in qualitative agreement with the temperature dependence of radiative recombination. As the temperature is further increased beyond a certain crossover temperature, Tc , which is determined by the radiative and non-radiative recombination rates, the lifetime starts to decrease, since non-radiative processes predominantly influence the emission. Further evidence of this is given by the fact that the lifetimes become independent of emission energy at higher temperatures. We note that Tc gradually increases as n increases: Tc ∼ 70 K for n < 1 × 1017 cm−3, Tc ∼ 100 K for n = 2 × 1018 cm−3 (not shown here), and Tc ∼ 140 K for n = 3 × 1019 cm−3. This indicates that the decrease in lifetime is due to a decrease of the radiative recombination lifetime itself rather than an increased influence of non-radiative recombination processes. Therefore, we conclude that the decrease in lifetime with increasing n is mainly due to a decrease in potential localization, and hence, a decrease in the carrier migration time into the lower tail states in the MQW active regions.

Figure 2. Temperature dependence of decay times monitored above (up triangles), below (down triangles), and at (circles) the emission peak for the InGaN/GaN MQWs with n < 1 × 1017 cm−3 (open symbols) and n = 3 × 1019 cm−3 (closed symbols) in the GaN barriers. The characteristic crossover temperature, Tc , (which is determined by the radiative and non-radiative recombination rates) gradually increases as n increases: Tc ∼ 70 K for n < 1 × 1017 cm−3, Tc ∼ 100 K for n = 2 × 1018 cm−3 (not shown), and Tc ∼ 140 K for n = 3 × 1019 cm−3.

To further study the influence of Si doping on the structural properties, AFM measurements were carried out. Figure 3 shows 2 μm × 2 μm AFM images of three reference 7-nm-thick GaN films with different disilane flow rates during growth. The root-mean-square surface roughness estimated from AFM images was 0.49, 0.42, and 0.22 nm for GaN epilayers with disilane flow rates of (a) 0, (b) 0.2, and (c) 2 nmol/min during growth, respectively. Thus, smoother GaN surfaces with more homogeneous terrace length were achieved at higher Si doping levels. In addition, the recent high-resolution x-ray diffraction (HRXRD) study showed that as n increases, the full width at half maximum (FWHM) of the higher-order SL satellite peaks narrows: the FWHM of the second order SL peaks was observed to be 589, 335, and 234 arcsec for n < 1 × 1017, n = 2 × 1018, and n = 3 × 1019 cm−3, respectively (see Table I) [Reference Cho, Fedler, Hauenstein, Park, Song, Keller, Mishra and DenBaars14].

Figure 3. 2 μm × 2 μm AFM images of three 7-nm-thick GaN films with different disilane flow rates during growth. The root-mean-square surface roughness estimated from AFM images was 0.49, 0.42, and 0.22 nm for GaN epilayers with the disilane flow rate of (a) 0, (b) 0.2, and (c) 2 nmol/min, respectively. A higher quality GaN surface morphology and a larger average terrace length were achieved by increasing Si incorporation.

Accordingly, we conclude that Si doping in the GaN barriers significantly improves the structural and interface quality of the InGaN/GaN MQWs. Since the incorporation of Si atoms can change the quality and/or surface free energy of the GaN barriers, it may affect the growth condition (or mode) of the subsequent InGaN wells and the interfaces [Reference Ruvimov, Liliental-Weber, Suski, Ager, Washburn, Krueger, Kisielowski, Weber, Amano and Akasaki7,Reference Osten, Klatt, Lippert, Dietrich and Bugiel16,Reference Eaglesham, Unterwald and Jacobson17]. The observed experimental results such as (i) a decrease in Stokes shift and (ii) a decrease in radiative recombination lifetime with increasing Si doping can be explained in terms of a decrease in potential fluctuations and enhancement of the interfacial structural qualities with incorporation of Si in the GaN layers.

Finally, we note that the influence of Si doping on the emission efficiency and the SE threshold pump density was also investigated for the InGaN/GaN MQWs with different Si doping concentration in the GaN barriers [Reference Bidnyk, Schmidt, Cho, Gainer, Song, Keller, Mishra and DenBaars11]. For all the samples, power dependent PL studies show a strong blueshift of the spontaneous emission with increasing excitation density mainly due to band filling of the energy tail states. The blueshift is observed to cease shortly before the onset of SE [Reference Schmidt, Cho, Gainer, Song, Keller, Mishra and DenBaars18]. The SE spectrum for the MQW sample with n = 2 × 1018 cm−3 was composed of many narrow peaks of less than 1 Å FWHM and there was no noticeable broadening of the SE peaks when the temperature was tuned from 175 to 575 K. Interestingly, only moderately Si doped MQW samples exhibited enhanced luminescence efficiency and a reduction of the SE threshold (see Table I). That is, the maximum emission intensity and the lowest SE threshold (55 kW/cm2) were achieved for the sample with n = 2 × 1018 cm−3, while a SE threshold of 165 kW/cm2 was obtained for the sample with n = 3 × 1019 cm−3. This fact, combined with the results presented in this paper, indicates that although Si doping improves the interface properties, it does not necessarily enhance the SE properties, reflecting the fact that localized carriers at potential fluctuations may play an important role in the emission from the InGaN/GaN MQW structures used for current state-of-art laser diodes.

Conclusions

We have investigated the optical properties of InGaN/GaN MQW structures as a function of Si doping concentration in the GaN barriers. As the Si doping of the GaN barriers increases, the Stokes shift of the PL emission peak with respect to the PLE band-edge was found to decrease. In addition, the radiative recombination lifetime measured at 10 K was observed to decrease significantly from ∼ 30 ns for n < 1 × 1017 cm−3 to ∼ 4 ns for n = 3 × 1019 cm−3 with increasing n. The results presented here, combined with the observed structural properties, are well explained by a decrease in carrier localization at potential fluctuations with increasing Si doping of the GaN barriers. These potential fluctuations are most likely a result of In alloy fluctuations and/or thickness variations of the InGaN well regions. The influence of Si doping on the emission efficiency and stimulated emission threshold was also discussed.

Acknowledgments

This work was supported by AFOSR, ARO, ONR, DARPA, and KOSEF.

Footnotes

MRS Internet J. Nitride Semicond. Res. 4S1, G6.44 (1999)

References

Nakamura, S., Senoh, M., Iwasa, N., Nagahama, S., Yamada, T., and Mukai, T., Jpn. J. Appl. Phys. Part 2 34, L1332 (1995).Google Scholar
Nakamura, S., Senoh, M., Nagahama, S., Iwasa, N., Yamada, T., Matsushita, T., Sugimoto, Y., and Kiyoku, H., Appl. Phys. Lett. 69, 4056 (1996).Google Scholar
Lim, B. W., Chen, Q. C., Yang, J. Y., and Khan, M. A., Appl. Phys. Lett. 68, 3761 (1996).Google Scholar
Wu, Y. F., Keller, B. P., Keller, S., Kapolnek, D., Kozodoy, P., DenBaars, S. P., and Mishra, U. K., Appl. Phys. Lett. 69, 1438 (1996).Google Scholar
Yang, X. H., Schmidt, T. J., Shan, W., Song, J. J., and Goldenberg, B., Appl. Phys. Lett. 66, 1 (1995).Google Scholar
Morkoç, H., Strite, S., Gao, G. B., Lin, M. E., Sverdlov, B., and Burns, M., J. Appl. Phys. 76, 1363 (1994).Google Scholar
Ruvimov, S., Liliental-Weber, Z., Suski, T., Ager, J. W. III, Washburn, J., Krueger, J., Kisielowski, C., Weber, E. R., Amano, H., and Akasaki, I., Appl. Phys. Lett. 69, 990 (1996).Google Scholar
Schubert, E. F., Goepfert, I. D., Grieshaber, W., and Redwing, J. M., Appl. Phys. Lett. 71 , 921 (1997).Google Scholar
Grudowski, P. A., Eiting, C. J., Park, J., Shelton, B. S., Lambert, D. J. H., and Dupuis, R. D., Appl. Phys. Lett. 71, 1537 (1997).Google Scholar
Keller, S., Abare, A. C., Minsky, M. S., Wu, X. H., Mack, M. P., Speck, J. S., Hu, E., Coldren, L. A., Mishra, U. K., and DenBaars, S. P., Materials Science Forum 264-268, 1157 (1998).Google Scholar
Bidnyk, S., Schmidt, T. J., Cho, Y. H., Gainer, G. H., Song, J. J., Keller, S., Mishra, U. K., and DenBaars, S. P., Appl. Phys. Lett. 72, 1623 (1998).Google Scholar
Salvador, A., Liu, G., Kim, W., Aktas, O., Botchkarev, A., and Morkoç, H., Appl. Phys. Lett. 67, 3322 (1995).Google Scholar
Zeng, K. C., J. Lin, Y., H. Jiang, X., Salvador, A., Popovici, G., Tang, H., Kim, W., and Morkoç, H., Appl. Phys. Lett. 71, 1368 (1997).Google Scholar
Cho, Y. H., Fedler, F., Hauenstein, R. J., Park, G. H., Song, J. J., Keller, S., Mishra, U. K., and DenBaars, S. P., J. Appl. Phys. (to be published).Google Scholar
Cho, Y. H., Gainer, G. H., Fischer, A. J., Song, J. J., Keller, S., Mishra, U. K., and DenBaars, S. P., Appl. Phys. Lett. 73, 1370 (1998).Google Scholar
Osten, H. J., Klatt, J., Lippert, G., Dietrich, B., and Bugiel, E., Phys. Rev. Lett. 69, 450 (1992).Google Scholar
Eaglesham, D. J., Unterwald, F. C., and Jacobson, D. C., Phys. Rev. Lett. 70, 966 (1993).Google Scholar
Schmidt, T. J., Cho, Y. H., Gainer, G. H., Song, J. J., Keller, S., Mishra, U. K., and DenBaars, S. P., Appl. Phys. Lett. 73, 560 (1998); ibid. 73, 1892 (1998).Google Scholar
Figure 0

Table I. Observed Stokes shift, measured lifetime, Tc, HRXRD FWHM, and SE threshold density for InGaN/GaN MQW samples with different Si doping concentration n by adjusting disilane flow rate FSi.

Figure 1

Figure 1. 10 K PL (solid lines), PLE (dashed lines), and TRPL data (open circles) of 12-period InGaN/GaN MQWs with Si doping concentrations ranging from < 1 × 1017 to 3 × 1019 cm−3 in the GaN barriers. The Stokes shift between the PL emission peak and the absorption band-edge observed from PLE spectra decreases significantly as the Si doping concentration increases. Luminescence decay times measured by TRPL are shown as a function of emission energy. With increasing Si doping concentration, the 10 K lifetimes decrease from ∼ 30 ns (for n < 1 × 1017 cm−3) to ∼ 4 ns (for n = 3 × 1019 cm−3).

Figure 2

Figure 2. Temperature dependence of decay times monitored above (up triangles), below (down triangles), and at (circles) the emission peak for the InGaN/GaN MQWs with n < 1 × 1017 cm−3 (open symbols) and n = 3 × 1019 cm−3 (closed symbols) in the GaN barriers. The characteristic crossover temperature, Tc, (which is determined by the radiative and non-radiative recombination rates) gradually increases as n increases: Tc ∼ 70 K for n < 1 × 1017 cm−3, Tc ∼ 100 K for n = 2 × 1018 cm−3 (not shown), and Tc ∼ 140 K for n = 3 × 1019 cm−3.

Figure 3

Figure 3. 2 μm × 2 μm AFM images of three 7-nm-thick GaN films with different disilane flow rates during growth. The root-mean-square surface roughness estimated from AFM images was 0.49, 0.42, and 0.22 nm for GaN epilayers with the disilane flow rate of (a) 0, (b) 0.2, and (c) 2 nmol/min, respectively. A higher quality GaN surface morphology and a larger average terrace length were achieved by increasing Si incorporation.