New compounds Li6MB3O9 (M=Nd,Sm,Eu,Tm,Er) were synthesized by solid-state reaction. The crystal structure of Li6NdB3O9 was analyzed from both powder and single crystal X-ray diffraction data. The results obtained by powder diffraction analysis and Rietveld refinement are a=7.2725(4) Å, b=16.6398(9) Å, c=6.7529(5) Å, β=105.398(8)°, and space group P21/c, which agree with the results obtained by single crystal diffraction analysis: a=7.2712(4) Å, b=16.6268(9) Å, c=6.7484(4) Å, β=105.411(1)°, and space group P21/c. This compound is isostructural with Li6YB3O9. Single crystal structure analysis showed that the fundamental building unit of these isostructural compounds comprises three isolated [BO3]3− triangles, one distorted [NdO8]13− triangulated dodecahedron, four distorted [LiO5]9− five-coordinated polyhedra, and two [LiO4]7− tetrahedron. An analysis of the infrared spectrum of Li6NdB3O9 confirmed the presence of isolated [BO3]3− triangles in Li6NdB3O9. The remaining four Li6MB3O9 (M=Nd, Sm, Eu, Tm, and Er) compounds were found to be isostructural with Li6NdB3O9. Their unit cell dimensions decrease with an increase in the atomic number of the rare-earth atoms. DTA and TGA measurements of Li6MB3O9 (M=Nd, Sm, Eu, Tm, and Er) revealed that these borates congruently melt from 800 °C to 860 °C.

Rietveld refinement using synchrotron powder X-ray diffraction data of the ranciéite, Ca0.19K0.01(Mn4+0.91◻0.09)O2⋅0.63H2O, crystal structure reveals significant differences from that reported previously. The interlayer H2O molecules occupy sites halfway between the Mn,O octahedral sheets. The Mn sites in the octahedral sheets have 10% vacancies, and the mean Mn–O distance indicates that all Mn is tetravalent (Mn4+). The interlayer Ca cations are located above and below the Mn vacancies and are octahedrally coordinated to three O2 atoms in the octahedral sheet and three H2O molecules in the interlayer.

Crystal structure of the skutterudite-related phase has been refined by the Rietveld method from X-ray powder diffraction data. Refined crystallographic data for CoSn1.5Te1.5 are a=12.9063(2) Å, c=15.7837(3) Å, V=2276.89(4) Å3, space group R3 (No. 148), Z=24, and Dx=7.50 g/cm3. The crystal structure of the title compound can be viewed as a modification of the skutterudite structure (CoAs3)—it is isostructural with CoGe1.5Te1.5 and IrSn1.5Te1.5. In the structure of CoSn1.5Te1.5, the Sn and Te atoms exhibit long-range ordering, which results in lowering of the original cubic symmetry of the skutterudite structure to the trigonal one.

The α, β, γ, and δ polymorphs of Y2Si2O7 were synthesized using sol-gel and solid-state methods. The structures of the α and γ polymorphs were determined by identification of isostructural rare-earth disilicates, and the structures were refined using Rietveld analysis of X-ray powder diffraction data. The α polymorph crystallizes in space group P1, with a=6.5872(6) Å, b=6.6387(7) Å, c=12.032(1) Å, α=94.501(7)°, β=90.984(8)°, γ=91.771(7)°, and volume=524.16(9) Å3. The γ form is described by space group P21/c, a=4.68824(5) Å, b=10.84072(9) Å, c=5.58219(6) Å, and γ=96.0325(3)°. The anisotropic thermal expansion of each phase was measured using high temperature diffraction up to 1200 or 1400 °C, depending on the stability of the polymorph. The thermal expansion is highly anisotropic for all polymorphs, with the low-expansion direction normal to the long axis of the corner-shared SiO4 tetrahedra.

A new ternary compound Dy5Co6Sn18 was synthesized and studied. The crystal structure of Dy5Co6Sn18 was determined using the Rietveld refinement method. The compound was found to crystallize in tetragonal space group I41/acd, Tb5Rh6Sn18-type structure, with a=13.5598(3) Å, c=7.1470(5) Å, Z=8, and Dcalc=8.789 g/cm3. Measurements of magnetic susceptibility and electrical resistivity on polycrystalline samples were also performed. The Curie–Weiss law was followed, with θp=−15.7 K and μeff=10.61μB. Dy5Co6Sn18 is a spin-glass with a freezing temperature of 6.5 K.

CdTe thin films were grown on indium tin oxide glass substrates by a closed-space sublimation method using a resistor heater. Crystalline structure, morphology, and band gaps of the films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical absorption, respectively. The XRD analysis showed that the textures of the films were found to depend on the rate of increase in the heating current. The CdTe thin film had an (111) texture when the heating current rate was 2.0 A/min. The SEM analysis revealed that the film is composed of polyhedral grains of microns size. However, the (111) texture of the CdTe thin film observed by XRD decreased with the appearance of (220), (311), (400), (331), (422), and (511) peaks of the fcc CdTe phase when the heating current rate increased to 4.5 A/min. The (111) texture disappeared when the heating current was increased immediately from 0 A to the target current of 70 A. SEM results revealed that the grains in the film are round and the grain size is smaller than 1 μm. Optical absorption analysis showed that there is no distinctive difference in the band gaps of the films.

Phase transformation temperatures of a polycrystalline Ni-rich Ti49.86Ni50.14 shape memory alloy were investigated using a differential scanning calorimeter. In situ structural and texture analyses of the monoclinic Ti49.86Ni50.14 were investigated using neutron powder diffractometer technique. Differential scanning calorimeter results showed that this Ni-rich alloy has a one-step cubic to monoclinic martensitic phase transformation on cooling and a one-step monoclinic to cubic transformation on heating. In situ high-resolution neutron powder diffraction data of the monoclinic phase from low temperatures to room temperature on heating are consistent with the differential scanning calorimeter’s heating results. In addition, the refined monoclinic crystal structure parameters for all neutron diffraction data sets agree satisfactorily with single-crystal X-ray diffraction results. The multiple-data-set capabilities of the GSAS Rietveld refinement program, with a generalized spherical-harmonics description was used successfully to extract the texture description directly from a simultaneous refinement using 52 time-of-flight monoclinic neutron diffraction patterns, taken from a polycrystalline sample held in 13 orientations inside the diffractometer.

A comparison of different methods of X-ray diffraction analysis for the determination of crystallite size and microstrain; namely, line profile analysis, Rietveld refinement, and three approaches based on the variance method, is presented. The analyses have been applied to data collected on a ceria sample prepared by the IUCr Commission on Powder Diffraction. In the variance method, split Pearson VII, the Voigt function, and its approximation pseudo-Voigt function were fitted to X-ray diffraction line profiles. Based on the fitting results, the variances of line profiles were calculated and then the crystallite size and root mean square strain were obtained from variance coefficients. A SS plot of Langford as well as a Fourier analysis and Rietveld refinement have been carried out. The average crystallite size and microstrain were determined. The values of area-weighted domain size determined from the variance method are in agreement with those obtained from line profile analysis within a single (largest) standard uncertainty, and the volume-weighted domain sizes derived from the SS plot, Fourier size distribution, and Rietveld refinement agree within a single standard uncertainty. The results of rms strain calculated from variance and Pearson VII shape function and those from Rietveld refinements fall within a single esd. However, the variance method in conjunction with pseudo-Voigt and Voigt functions produce rms strains substantially larger than those determined from line profile analysis and Rietveld refinements.

A new Tutton’s salt Tl2[Mn(OH2)6](SO4)2 was grown from aqueous solutions and characterized by chemical analysis and X-ray powder diffraction. It was found to be monoclinic, space group P21/a, a=0.93276(6), b=1.25735(8), c=0.62407(4) nm, and β=106.310(3)°. It is unstable in warm air and dissolves incongruently. A comparison of unit cell volumes for all 37 Tutton sulfate phases found in ICDD’s PDF-2 database (86 entries) reveals a reasonable correlation with Shannon and Prewitt’s ionic radii [Acta Crystallogr. 25, 925–926 (1969)] and several deviations, most of them seeming to be erroneous entries.

A new phase Zn3Cu4Sb2O12 was analyzed by X-ray powder diffraction. Its monoclinic unit cell parameters are a=21.0378(19) Å, b=8.7825(7) Å, c=5.5860(4) Å, and β=112.578(7)°, and the space group is either Cc (9) or C2/c (15). From comparison with density measurements, Z=4.

A new ternary compound Al0.35GdGe2 has been synthesized and studied by means of X-ray powder diffraction technique. The ternary compound Al0.35GdGe2 crystallizes in the orthorhombicwith the CeNiSi2 structure type (space group Cmcm, a=4.0874(2) Å, b=16.1499(5) Å,c=3.9372(1) Å, Z=4, and Dcalc=8.007 g/cm3).