Wet Etching of Bulk AlN Crystals

Published online by Cambridge University Press:  01 February 2011

Dejin Zhuang ,
Ziad G. Herro ,
Xianglin Li ,
Raoul Schlesser  and
Zlatko Sitar
Dejin Zhuang
Affiliation:
dzhuang@ncsu.edu, North Carolina State University, Materials Science and Engineering, Rm. 219 RB1, Campus Box 7919, Raleigh, NC, 27695-7919, United States
Ziad G. Herro
Affiliation:
zgherro@ncsu.edu, North Carolina State University, Materials Science and Engineering, Campus Box 7919, Raleigh, NC, 27695-7919, United States
Xianglin Li
Affiliation:
xli9@unity.ncsu.edu, North Carolina State University, Materials Science and Engineering, Campus Box 7919, Raleigh, NC, 27695-7919, United States
Raoul Schlesser
Affiliation:
raoul_schlesser@ncsu.edu, North Carolina State University, Materials Science and Engineering, Campus Box 7919, Raleigh, NC, 27695-7919, United States
Zlatko Sitar
Affiliation:
sitar@ncsu.edu, North Carolina State University, Materials Science and Engineering, Campus Box 7919, Raleigh, NC, 27695-7919, United States
Get access

Abstract

AlN bulk crystals of different crystallographic orientations were etched in aqueous KOH solution (general etchant) and molten KOH/NaOH eutectic alloy (defect selective etchant). In the general etchant, the aluminum polar surface (0001) was found to be stable while the nitrogen polar (0001) surface and non-polar m-plane (1010) surfaces showed significant etching. Etch patterns on nitrogen polar surfaces consisted of complete coverage of hexagonal pyramids while the m-plane surfaces were etched in a layer-by-layer mode. TEM studies revealed that the observed etch hillocks on nitrogen polar surfaces were not associated with extended structural defects. When etched in a defect-selective etchant, the aluminum polar surface showed well-defined hexagonal etch pits, with an etch pit density (EPD) of 2×104 cm−2. The nitrogen polar surfaces and m-plane surfaces showed etch features similar to the one obtained during general etching, however, the etch feature density was significantly lower. The etch mechanisms, etch kinetics, as well as the correlation between the observed etch features and structural defects in bulk crystals will be discussed.

Keywords

III-Vcrystalkinetics
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 955: Symposium I – Advances in III-V Nitride Semiconductor Materials and Devices , 2006 , 0955-I07-10
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ambacher, O., J. Phys. D: Appl. Phys. 31, 2653 (1998).Google Scholar
2. Edgar, J.H., Editor, Properties of Group III Nitrides, Electronic Materials Information Service (EMIS), London (1994).Google Scholar
3. Liu, L. and Edgar, J.H., Mater. Sci. Eng. R, 37, 61 (2002).Google Scholar
4. Zhuang, D., Herro, Z.G., Schlesser, R., and Sitar, Z., J. Cryst. Growth, 287, 372 (2006); D. Zhuang, Z.G. Herro, R. Schlesser, B. Raghothamachar, M. Dudley, and Z. Sitar, J. Electron. Mater., 35, 1513 (2006).Google Scholar
5. Herro, Z.G., Zhuang, D., Schlesser, R., Collazo, R. and Sitar, Z., J. Cryst. Growth, 286, 205 (2006).Google Scholar
6. Vartuli, C.B., Pearton, S.J., Lee, J.W., Hong, J., Abernathy, C.R., MacKenzie, J.D., and Shul, R.J., Appl. Phys. Lett., 69, 1426 (1996).Google Scholar
7. Zhuang, D. and Edgar, J.H., Mater. Sci. Eng. R, 48, 1 (2005).Google Scholar
8. Schowalter, L.J., Rojo, J.C., Yakolev, N., Shusterman, Y., Dovidenko, K., Wang, R., Bhat, I., Slack, G., MRS Internet J. Nitride Semicond. Res., 5S1, W6.7 (2000).Google Scholar
9. Zhuang, D., Edgar, J.H., Liu, Lianghong, Liu, B., and Walker, L., MRS Internet J. Nitride Semicond. Res., 7, 4 (2002).Google Scholar
10. Zhuang, D., Edgar, J. H., Strojek, B., Chaudhuri, J. and Rek, Z., J. Cryst. Growth, 262, 89 (2004).Google Scholar
11. Li, D., Sumiya, M., Fuke, S., Yang, D., Que, D., Suzuki, Y., Fukuda, Y., J. Appl. Phys., 90, 4219 (2001).Google Scholar
12. Mileham, J.R., Pearton, S.J., Abernathy, C.R., MacKenzie, J.D., Shul, R.J., and Kilcoyne, S.P., Appl. Phys. Lett., 67, 1119 (1995).Google Scholar
13. Raghothamachar, B., Vetter, W.M., Dudley, M., Dalmau, R., Schlesser, R., Sitar, Z., Michaels, E., Kolis, J. W., J. Cryst. Growth. 246, 271–280 (2002).Google Scholar
14. Schlesser, R., Dalmau, R., and Sitar, Z., J. Cryst. Growth 241, 416–420 (2002).Google Scholar