The use of Soluble Metal-Polyselenide Complexes as Precursors to Binary and Ternary Solid Metal Selenides

Published online by Cambridge University Press:  28 February 2011

S. Dhingra  and
M. G. Kanatzidis
S. Dhingra
Affiliation:
Department of Chemistry and Center for Fundamental Materials Research, Michigan State University, East Lansing MI 48824USA
M. G. Kanatzidis
Affiliation:
Department of Chemistry and Center for Fundamental Materials Research, Michigan State University, East Lansing MI 48824USA
Get access

Abstract

The use of several soluble metal polychalcogenides to prepare solid state materials is presented. Thermal gravimetric analysis (TGA) data, under inert atmosphere, of the molecular compounds (Ph4P)2[Cd(Se4)2], (Ph4P)4[Cu2Se14], (Ph4P)2[Cu4Se12], (Ph4P)4[In2Se21] and (Et4N)3[M3Se15], (M=In, TI), show that the corresponding binary solid state compounds are formed as single phases at temperatures as low as 530°C. We have grown films of CdSe, Cu2-xSe, β-In2Se3, TISe and CuInSe2 using these complexes as precursors. The films were prepared by pyrolysis of green precursor films, cast from DMF solutions. CuInSe2 was prepared by co-thermolysis of Cu/Sex and In/Sex complexes. The chemical, X-ray, spectroscopic and electron microscopic characterization of these molecular precursor-derived films as well as their charge transport characterization is reported.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 180: Symposium A – Better Ceramics Through Chemistry IV , 1990 , 825
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Fan, G.; Williams, J. O. J. Chem. Soc. Faraday Trans. 1987, 83, 323–338 Google Scholar
2. (a) Smith, R.A. in “Semiconductors” pp. 438, Cambridge University Press, 1978.Google Scholar
(b) Bartlett, B.E. et al. . Infrared Phys. 1969, 9, 35.Google Scholar
3. Kun, Z. K. Solid State Technology 1988, 31, 77–79.Google Scholar
4. Ballman, A.A.; Byer, R.L.; Eimerl, D.; Feigelson, R.S.; Feldman, B.J.; Goldberg, L.S.; Menyuk, N.; Tang, C.L. Applied Optics 1987, 26, 224–227.Google Scholar
5. (a) Mickelsen, R.A.; Chen, W.S. in “Ternary and Multinary Compounds,” Proceedings of the 7th Conference, Deb, S.K. and Zunger, A. Eds., Materials Research Society, 1987, pp. 39–47.Google Scholar
(b) Steward, J.M.; Chen, W.S.; Devaney, W.E.; Mickelsen, R.A. Deb, S.K. and Zunger, A. Eds., Materials Research Society, 1987, pp. 59–64.Google Scholar
6. (a) Whittingham, M.S. Science 1976, 192, 1125.Google Scholar
(b) Whittingham, M.S. J. Solid State Chem. 1979, 29, 303–310.Google Scholar
7. (a) Kanatzidis, M. G. Abstracts of 196th ACS National Meeting, Los Angeles 1988, INORG 469.Google Scholar
(b) Kim, K.-W., Dhingra, S.; Kanatzidis, M. G. unpublishedGoogle Scholar
8. (a) Cusick, J.; Scudder, M. L.; Craig, D. C.; Dance, I. G. Polyhedron 1989, 8, 1139–1141 Google Scholar
(b) Kanatzidis, M. G.; Huang, S.-P.; Dhingra, S. unpublishedGoogle Scholar
(c) Kanatzidis, M. G.; Dhingra, S. Inorg. Chem. 1989, 28, 2024–2026 Google Scholar
(d) Dhingra, S.; Kanatzidis, M. G. submitted for publicationGoogle Scholar
9. (a) β-In2Se3: Popovic, S.; Tonejc, A.; Grzeta-Plenkovic, B.; Celustka, B.; Trojko, R. J. Appl. Crystallogr. 1979, 12, 416–420 Google Scholar
(b) TlSe: Ketelaar, J. A. A.; t'Hart, W. H.; Moerel, M.; Polder, D. Z. Kristallogr. 1939, 101, 396–405 Google Scholar
10. SEM-EDS analysis of the CuInSe2 films indicated the presence of traces of P (<0.07 % per weight)Google Scholar