Time-Resolved Study of Silicon During Pulsed-Laser Annealing

Published online by Cambridge University Press:  15 February 2011

B. C. Larson ,
C. W. White ,
T. S. Noggle ,
J. F. Barhorst  and
D. M. Mills
B. C. Larson
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
C. W. White
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
T. S. Noggle
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
J. F. Barhorst
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
D. M. Mills
Affiliation:
Cornell High Energy Synchrotron Source and School of Applied and Engineering Physics, Cornell University, Ithaca, NY 14850
Get access

Abstract

Near surface temperatures and temperature gradients have been studied in silicon during pulsed laser annealing. The investigation was carried out using nanosecond resolution x-ray diffraction measurements made at the Cornell High Energy Synchrotron Source. Thermal-induced-strain analyses of these real-time, extended Bragg scattering measurements have shown that the lattice temperature reached the melting point during 15 ns, 1.1–1.5 J/cm2 ruby laser pulses and that the temperature of the liquid-solid interface remained at that temperature throughout the high reflectivity phase, after which time the surface temperature subsided rapidly. The temperature gradients below the liquid-solid interface were found to be in the range of 107°C/cm.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 13 , 1982 , 43
Copyright
Copyright © Materials Research Society 1983

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*.

Research sponsored by the Division of Materials Sciences, U.S. Department of Energy under contract W-7405-eng-26 with Union Carbide Corporation. The CHESS portion of this research was supported by the National Science Foundation.

References

REFERENCES

1.Laser and Electron Beam Interactions with Solids, ed. by Appleton, B. R. and Celler, G. K., North Holland, New York, 1982.Google Scholar
2.Galvin, G. J., Thompson, M. O., Mayer, J. W., Hammond, R. B., Paulter, N. and Peercy, P. S., Phys. Rev. Lett. 48, 33 (1982).Google Scholar
3.Larson, B. C., White, C. W., Noggle, T. S. and Mills, D., Phys. Rev. Lett. 48, 337 (1982).Google Scholar
4.Larson, B. C. and Barhorst, J. F., J. Appl. Phys. 51, 3181 (1980).Google Scholar
5. Int. Tables for X-Ray Crystallography, Vol. II, The Kynoch Press, Birmingham, England, 1959, p. 241.Google Scholar
6.Fukuhara, A. and Takano, Y., Acta Crystallogr., Sect. A 33, 137 (1977).Google Scholar
7.Lowndes, D., Jellison, G. E. Jr., and Wood, R. F., Phys. Rev. (in press).Google Scholar
8.Compaan, A., Aydinli, A., Lee, M. C. and Lo, H. W., Ref. 1, p. 43.Google Scholar