Template Assisted Fabrication and Magnetic Properties of Cobalt Ferrite Nanostructures

Published online by Cambridge University Press:  29 February 2012

Jian H. Zhang ,
Liyin Chen  and
Xylona L. Williams
Jian H. Zhang
Affiliation:
Department of Chemistry, Xavier University of Louisiana, 1 Drexel Drive, New Orleans, LA 70125, U.S.A
Liyin Chen
Affiliation:
Department of Chemistry, Xavier University of Louisiana, 1 Drexel Drive, New Orleans, LA 70125, U.S.A
Xylona L. Williams
Affiliation:
Department of Chemistry, Xavier University of Louisiana, 1 Drexel Drive, New Orleans, LA 70125, U.S.A
Get access

Abstract

Spinel cobalt ferrite nanotubes and nanowires of about five micrometers in length were fabricated using anodic aluminum oxide (AAO) templates of 20 – 200 nm pore diameters and sol-gel processing. A cobalt ferrite sol was prepared by mixing the acetic acid solution of cobalt (II) acetate and ethanol solution of iron (III) acetylacetonate. The templates filled with precursor were obtained after they were dipped into the sol and dried in air. The template/precursor composites were sintered in air at 500 ºC to form cobalt ferrite phase, which was verified by XRD. The morphology of the nanostructures determined by SEM revealed that the cobalt ferrite nanotubes were formed in the channels of 100 nm and 200 nm diameters in the templates, whereas the nanowires were formed in the 20 nm channels of the templates. The magnetic measurement of cobalt ferrite nanowires by a SQUID magnetometer showed that the nanowires are superparamagnetic at room temperature. The room temperature measurement of magnetization versus the applied field on the nanowire arrays in 20 nm channels of templates showed that the coercivity is 1.57 kOe and 1.47 kOe for the nanowire axis parallel and perpendicular to the applied field, respectively, indicating that the nanowire arrays are nearly magnetically isotropic. However, the coercivity of cobalt ferrite nanowires fabricated in this work is much larger than those in the similar systems reported in the literatures.

Keywords

magnetic propertiesnanostructuresol-gel
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1408: Symposium BB – Functional Nanowires and Nanotubes , 2012 , mrsf11-1408-bb20-55
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Laurent, S., Forge, D., Port, M., Roch, A., Robic, C., Elst, L. V. and Muller, R.N., Chem. Rev., 108, 2064–2110((2008)Google Scholar
2. Hao, R., Xing, R., Xu, Z., Hou, Y., Gao, S. and Sun, S., Advanced Materials, 22, 2729–2742 (2010)Google Scholar
3. Hillebrenner, H., Buyukserin, F., Stewart, J.D., Martin, C.R., Nanomedicine, 1(1), 39–50 (2006)Google Scholar
4. Bjursten, L.M., Rasmusson, L., Oh, S., Smith, G.C., Brammer, K.S., Jin, S., Journal of Biomedical Materials research, Part A, 92A(3), 1218–1224 (2010).Google Scholar
5. Carlier, D. and Ansermet, J-P., Journal of Electrochemical Society, 153(5), C277–C281 (2006).Google Scholar
6. Xu, Y., Wei, J., Yao, J., Fu, J., Xue, d., Materials Letters, 62, 1403–1405 (2008).Google Scholar
7. Yuan, J.J., Zhao, Q., Xu, Y.S., Liu, Z.G., Du, X.B., Wen, G.H., Journal of Magnetism and Magnetic Materials, 321, 2795–2798 (2009),Google Scholar
8. Kanamadi, C.M., Das, B.K., Kim, c.W., Cha, H. G., Ji, E. S., Kang, D. I., Jadhav, A.P., Heo, J. K., Kim, D. and Kang, Y.S., J.Nanosci. Nanotechnol., 9(8), 4942–4947 (2009).Google Scholar
9. Yourdkhani, A. and Caruntu, G., Journal of Materials Chemistry, 21, 7145–7153 (2011)Google Scholar
10. El-Sheikh, S.M., Harraz, F.A. and Hessien, M, M., Materials Chemistry and Physics, 123, 254–259 (2010).Google Scholar