Synthesis of Indium Tin Oxide Nanoparticles and Application to Near IR-reflective Film

Published online by Cambridge University Press:  21 March 2011

Ja Eun Song  and
Young Soo Kang
Ja Eun Song
Affiliation:
Department of Chemistry, Pukyong National University, Busan, 608-737, Korea
Young Soo Kang
Affiliation:
Department of Chemistry, Pukyong National University, Busan, 608-737, Korea
Get access

Abstract

ITO nanoparticles were synthesized by coprecipitation method in an aqueous solution and thermal method in an alcohol solution. The coprecipitate prepared at room temperature showed the crystal structure of indium oxide in X-ray diffraction when it was annealed above 300°C. In thermal method, the nanoparticles have two phase crystal structure of indium oxide hydroxide (InOOH) and indium hydroxide (In(OH)3). Annealing at the temperature above 300 °C, it showed the rhombohedral crystal structure of indium oxide (In2O3). The phase transition of ITO nanoparticle was also detected with DSC. Near IR-reflective film was prepared by spin coating using ITO sol solution. Transmission electron microsopy (TEM) and energy dispersive X-ray spectrometer (EDS) were used to characterize the morphology and composition of ITO nanoparticles. Near-IR (NIR) spectrometer was used to determine reflectance on the surface of ITO film in the NIR-radiation region.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 818: Symposium M – Nanoparticles and Nanowire Building Blocks-Synthesis, Processing, Characterization and Theory , 2004 , M5.14.1
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Murali, A., Barve, A., Leppert, V. J. and Risbud, S. H., NANO LETTERS, 1, 287 (2001).Google Scholar
2. Pissadakis, S., Mallis, S., Reekie, L., Wikinson, J. S., Eason, R. W., Vainos, N. A., Moschovis, K. and Kiriakidis, G., Appl. Phys. A, 69, 333 (1999).Google Scholar
3. Mattox, D. M., Thin Solid Films, 204, 25 (1991).Google Scholar
4. Hamberg, I. and Granqvist, C. G., J. Appl. Phys., 60, R123, (1986).Google Scholar
5. Lee, D. H., Vuong, K. D., Williams, J. A. A., Fagan, J., Condrate, R. A., Wang, Sr. and Wang, X. W. J., Mater. Res., 11, 895 (1996).Google Scholar
6. Minami, T., Kakumu, T., Shimokawa, K. and Takata, S., Thin Soild Films, 318, 317 (1998).Google Scholar
7. Kang, M., Lee, S. Y., Chung, C. H., Cho, S. M., Han, G. Y., Kim, B. W. and Yoon, K. J. J., Photochem. Photobiol. A, 185, 144 (2001).Google Scholar
8. Kang, M. S., Jang, J. H., Park, S. H., Lee, S. C., Lee, B. Y., Yi, Y. L., Lee, J. H. and Hong, Y. K., Theories and Application of Chem. Eng., 9, 85 (2003).Google Scholar
9. Arfsten, N. J., J. Non-Cryst. Soilds, 63, 243 (1984).Google Scholar
10. Song, J. E., Kang, Y. S., (manuscript in preparation).Google Scholar