Structure and Electrical Properties of Yttria Stabilized Zirconia by Iron Ion Implantation

Published online by Cambridge University Press:  22 February 2011

Wang Guomei  and
Qu Zuyuan
Wang Guomei
Affiliation:
Wuhan University of Technology, Department of Materials Engineering, Wuhan 430070, China
Qu Zuyuan
Affiliation:
Wuhan University of Technology, Department of Materials Engineering, Wuhan 430070, China
Get access

Abstract

Fe ions were implanted into yttria stabilized zirconia with doses of 5×1015 -2×1017 ions/cm2 at an energy of 140 KeV. The effects of Fe-implanted zirconia and post-implantation thermal annealing on electrical properties and structure of an implanted layer were studies by electric measurement, X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). It was found that the resistivity for the as-implanted sample decreased greatly with increasing ion dose, and at high dose the resistivity decreasing gradually. After annealing at 1200°C in N2 environment, the resistivity relative to that for the as-implanted sample had clearly marked decreases. Results of the XRD and XPS measurements showed that the implanted Fe ion was mainly in a charge state of Fe2+ and the sections of Fe2+ were incorporated into the ZrO2 lattice, forming a FeZrO3 compound. Finally, the conductivity mechanisms were discussed briefly.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 316: Symposium A – Materials Synthesis and Processing Using Ion Beams , 1993 , 367
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Gupta, T.K., Grekila, R.B. and Subbarao, E.C., J. Electronchem. Soc . , 128 (1981) 929.Google Scholar
2 Ikeda, S., Sakural, O., Vematsu, K., Mizutani, N. and Kato, N., J. Mater.Sci., 20 (1985) 4593.Google Scholar
3 Bonanos, N., Slotwinsk, R.K., Steele, B.C.H. and Butler, E.P., J. Mater. Sci. Lett., (3) (1984) 245.Google Scholar
4 Karavaev, Ju.N., Neujmin, A.D. and Zirjanov, V.G., Ijvest, , AN SSSR. Neorgan. Mater., 21 (1985) 1181.Google Scholar
5 Karavaev, Ju.N., Palguev, S.F. and Neujmin, A.D., in High Tech Ceramics, ed., Vincenzini, P., (Amsterdam, (Amsterdam, Oxfore, 1987) 247.Google Scholar
6 Scholten, D. and Burggraaf, A.J., Solid State Ionics, 16 (1985) 147.Google Scholar