Structural Thermodynamic Model for the Durability and Viscosity of Nuclear Waste Glasses

Published online by Cambridge University Press:  28 February 2011

Xiangdong Feng  and
Aaron Barkatt
Xiangdong Feng
Affiliation:
The Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Aaron Barkatt
Affiliation:
The Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Get access

Abstract

A model based upon structural thermodynamic considerations has been proposed for both chemical durability and viscosity of nuclear waste glasses. This model assumes the bond strength between atoms in the glass to be the predominant factor in controlling the composition dependence of physical properties such as viscosity and chemical properties like durability. These characteristic bond strengths in the glass are obtained from known heats of formation of the constituent oxides with a few simple structural rules deduced by distinguishing the structural roles of the various oxides, i.e., separating those components that are clearly “network-formers” (e.g. SiO2, Al2O3, ZrO2) from those that are clearly “network-breakers” (e.g. alkali oxides). This model has been successfully applied to the correlation of glass composition with modified MCC-3 leach test results on nuclear waste glasses measured at various laboratories on one hand and with the viscosities of numerous glasses over a temperature range of 850°C to 1600°C with remarkable accuracy on the other hand.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 112: Symposium P – Scientific Basis for Nuclear Waste Management XI , 1987 , 543
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[ 1] Hench, L.L. and Clark, D.E., J. Non-Cryst. Solids, 28, 83 (1987)CrossRefGoogle Scholar
[ 2] Grambow, B., Mat. Res. Soc. Symp. Proc. Vol.44, 15 (1985)Google Scholar
[ 3] Lasaga, C., J. Geophysical Research,89, 4009(1984)Google Scholar
[ 4] Chick, L.A., Bowen, W.M., Lokken, R.O., Wald, J.W., Bunnell, L.R., Strachan, D.M., Report no. PNL-4992, 1984Google Scholar
[ 5] Jantzen, C.M. and Plodinec, M.J., J. Non-Cryst. solids, 67, 207 (1984)CrossRefGoogle Scholar
[ 6] Plodinec, M.J., Jantzen, C. M., and Wick, G.G., Advances in Ceramics, 8 491 (1984)Google Scholar
[ 7] Jantzen, C.M., Advances in Ceramics, 20, 703 (1987)Google Scholar
[ 8] Feng, X., Barkatt, A., Water Management 87 vol.1, edited by Post, R.G., University of Arizona, Board of Regent, 584 (1987)Google Scholar
[ 9] Paul, A., Chemistry of Glass, (Chapman and Hall, New York, 1982), p.126 Google Scholar
[ 10] Morey, G.W., Fournier, R.O. and Rowe, J.J., J. of Geophysical Research, 69, 1995 (1964); J.D. Rimstidt, in The Kinetics of Water Silica Reactions, PhD thesis Univ. of Penn. State Univ. Pa, (1979), P.135CrossRefGoogle Scholar
[ 11] Jantzen, C.M. Plodinec, M.J., Report no. DPST-86–372, Savannah River Lab, 1986 Google Scholar
[ 12] Bottinga, Y., Weill, D.F., Am. J. Sci., 272, 438 (1972)CrossRefGoogle Scholar
[ 13] Turkdogan, E.T., Bills, P.M., Am. Ceram. Soc. Bull. 39, 682 (1960)Google Scholar
[ 14] Urbain, G., Cambier, F., Deletter, M., and Anseau, M.R., Trans. J. Br. Ceram. Soc. 80, 139(1981)Google Scholar
[ 15] Ilhan, A. and Hrma, P., presented at ACS 1986 annual meetingGoogle Scholar
[ 16] Feng, X. and Barkatt, Aa., presented at MRS 1987 Fall Meeting, Boston, Nov. 30-Dec. 5, 1987 Google Scholar
[ 17] Saad, E.E., Am. Ceram. Soc. Bull., 66, 571 (1987)Google Scholar
[ 18] Sun, K.-H., J. Amer Ceram. Soc. 30, 277 (1947)CrossRefGoogle Scholar
[ 19] Boyd, D.C., Thompson, D.A., in Kirk-Othmer: Encyclopedia of Chemical Technology, 3ed ed. John Wiley and Son Inc., 807–880 (1980)Google Scholar
[ 20] Pauling, L., The Nature of Chemical Bond and Structure of Molecules and Crystals, 2ed. Ed., Cornell Univ. Press, N.Y. 1940 Google Scholar
[ 21] Dean, J.A. ed. Lange's Handbook of Chemistry, 13th. Ed. McGraw-Hill Book Co. Table 9–1 (1985)Google Scholar
[ 22] Zachariasen, W. H., J. Amer. Chem. Soc., 54, 3841(1932)CrossRefGoogle Scholar
[ 23] Fajans, K. and Barber, D.S.W. J. Amer. Chem. Soc. 74, 276(1952)Google Scholar
[ 24] Krogh-Moe, J., Phys. and Chem. of Glasses, 1, 26(1960)Google Scholar
[ 25] Bourgeois, G. and Mathieu, J., Chim. Ind.-Gen. Chim., 105, 345(1972)Google Scholar
[ 26] Mackenzie, J.D., in Modern Aspects of The Vitreous State, Butterworths, London, 190(1960)Google Scholar
[ 27] Bettie, I.R., Trans. Faraday Soc., 49, 1059 (1953)Google Scholar
[ 28] Barkatt, A. et.al., submitted to Waste Management’ 88Google Scholar
[ 29] Mendel, J.E., Report no. PNL-5157, Pacific Northwest Laboratory, 1984 Google Scholar
[ 30] Piepel, G.F., Report no. WVST 87–213, Pacific Northwest Laboratory, 1987 Google Scholar
[ 31] Vogel, H., Phys. 2, 22, 645(1921)Google Scholar
[ 32] Fulcher, G.S., J. Am. Ceram. Soc., 8, 339(1925)Google Scholar
[ 33] Arrhenius, S., Meddel. Vetenskapsaked, 20, 3(1916)Google Scholar
[ 34] Feng, X. et.al. to be publishedGoogle Scholar