Spin-Valve GMR Films Based on Antiferromagnetic NiMn

Published online by Cambridge University Press:  10 February 2011

Geoff Anderson ,
Yiming Huai  and
Lena Miloslavsky
Geoff Anderson
Affiliation:
Spin-Valve Materials/Process, Read-Rite Corporation 44100 Osgood Rd. Fremont, CA 94539
Yiming Huai
Affiliation:
Spin-Valve Materials/Process, Read-Rite Corporation 44100 Osgood Rd. Fremont, CA 94539
Lena Miloslavsky
Affiliation:
Spin-Valve Materials/Process, Read-Rite Corporation 44100 Osgood Rd. Fremont, CA 94539
Get access

Abstract

In this work we have investigated the magnetic and structural properties of spin-valve films exchange biased by CoFe/NiMn compared to CoFe/lrMn spin valves. A spin-valve film of structure Ta/NiFe/CoFe/Cu/CoFe/NiMnITa showed a giant-magnetoresistance of 5.5% with a Hex∼850 Oe after annealing. Structural ordering of the NiMn in an fct phase after annealing has been observed using x-ray diffraction, with the data exhibiting pure fct(111) texture. The thermal stability of both the exchange pinning and magnetoresistance of NiMn spin-valves was evaluated. The blocking temperature (Tb) of this film is 400°C, compared to 225°C for IrMn based spin-valve films (IrMn thickness ∼50 Å). Blocking temperature distribution and remnant blocking temperature measurements also suggest that NiMn based spin-valves have far superior pinning stability with temperature than IrMn based spin-valves. Magnetoresistance measurements show a linear decrease with temperature due to electron-phonon scattering with the ∆R/R being reduced by 33% at 150°C (as compared to a 50% decrease for IrMn based spinvalves). Extended annealing at 150°C did not effect spin-valve performance, with ∆R/R and R being constant over 60 hours, suggesting that no appreciable interdiffusion is occurring.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 562: Symposium L – Polycrystalline Metal & Magnetic Thin Films , 1999 , 45
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lin, T., Mauri, D., Staud, N., Hwang, C., Howard, K. and Gorman, G., Appl. Phys. Lett. 65, 1163 (1994).Google Scholar
2. Mao, S., Gangopadhyay, S., Amin, N. and Murdock, E., Appl. Phys. Lett. 69, 3594 (1996).Google Scholar
3. Wong, B. Y., Mitsumata, C., Prakash, S., Laughlin, D. E. and Kobayashi, T., J. Appl. Phys. 79, 7896 (1996).Google Scholar
4. Araki, S., Sano, M., Ohto, M., Tsuchiya, Y., Noguchi, K., Morita, H. and Matsuzaki, M., IEEE Trans. Mag. 34, 1426 (1998).Google Scholar
5. Mao, S., Amin, N. and Murdock, E., presented at the 1998 MMM conference, Miami, FL, 1998 (to be published).Google Scholar