Microstructure and Hydrogen Permeability of Duplex Phase M-ZrNi (M=V, Nb, Ta) Alloys

Published online by Cambridge University Press:  26 February 2011

Kazuhiro Ishikawa ,
Naoshi Kasagami ,
Tomoyuki Takano  and
Kiyoshi Aoki
Kazuhiro Ishikawa
Affiliation:
ishikazu@mail.kitami-it.ac.jp, Kitami Institute of Technology, Materials Science, 165 Koen-cho, Kitami, 090-8507, Japan
Naoshi Kasagami
Affiliation:
mm4@std.mail.kitami-it.ac.jp, Kitami Institute of Technology, Graduate student, 165 Koen-cho, Kitami, 090-8507, Japan
Tomoyuki Takano
Affiliation:
mmm4@std.mail.kitami-it.ac.jp, Kitami Institute of Technology, Graduate student, 165 Koen-cho, Kitami, 090-8507, Japan
Kiyoshi Aoki
Affiliation:
aokiky@mail.kitami-it.ac.jp, Kitami Institute of Technology, Materials Science, 165 Koen-cho, Kitami, 090-8507, Japan
Get access

Abstract

In order to develop non-Pd based high performance hydrogen permeation alloys, microstructure, crystal structure and hydrogen permeability of duplex phase M-ZrNi (M=V and Ta) alloys were investigated using a scanning electron microscope, an X-ray diffractometer and a gas flow meter. These results were compared with those of Nb-ZrNi ones which have been previously published. The hydrogen permeation was impossible in the V-ZrNi alloys, because they were brittle in the as-cast state. On the other hand, duplex phase alloys consisting of the bcc-(Ta, Zr) solid solution and the orthorhombic ZrNi (Cmcm) intermetallic compound were formed and hydrogen permeable in the Ta-ZrNi system. The Ta40Zr30Ni30 alloy shows the highest value of hydrogen permeability of 4.1×10-8 [molH2m-1s-1Pa-0.5] at 673 K, which is three times higher than that of pure Pd.

Keywords

hydrogenationmicrostructurecompound
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II05-53
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Nishimura, C., Komaki, M. and Amano, M., Mater. Trans. JIM 32, 501 (1991).10.2320/matertrans1989.32.501Google Scholar
2. Shimpo, Y., Yamaura, S., Okouchi, H., Nishida, M., Kajita, O., Kimura, H. and Inoue, A., J. Alloys Compd. 372, 197 (2004).Google Scholar
3. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., J. Alloys Compd. 368, 215 (2004).Google Scholar
4. Luo, W., Ishikawa, K. and Aoki, K., J. Alloys Compd. 407, 115 (2006).Google Scholar
5. Buxbaum, R. E. and Kinney, A. B., Ind. Eng. Chem. Res. 35, 530 (1996).10.1021/ie950105oGoogle Scholar
6. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., J. Alloys Compd. 404–406, 273 (2006).Google Scholar
7. Takano, T., Ishikawa, K., Matsuda, T. and Aoki, K., Mater. Trans. 45, 3360 (2004).10.2320/matertrans.45.3360Google Scholar
8. Ishikawa, K., Takano, T., Matsuda, T. and Aoki, K., Appl. Phys. Lett. 87, 081906 (2005).Google Scholar
9. Villars, P., Prince, A. and Okamoto, H., in Handbook of Ternary Alloy Phase Diagrams, CD ROM ed. (ASM International, Materials Park, OH 1995).Google Scholar
10. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., J. Alloys Compd. 425, 284 (2006).10.1016/j.jallcom.2006.01.028Google Scholar