Microstructural Development of TiB2 Ion Implanted with 1 Mev Nickel*

Published online by Cambridge University Press:  25 February 2011

P. S. Sklad ,
P. Angelini ,
M. B. Lewis  and
C. J. Mchargue
P. S. Sklad
Affiliation:
Metals and Ceramics Division Oak Ridge National Laboratory, Post Office Box X, Oak Ridge, TN 37831
P. Angelini
Affiliation:
Metals and Ceramics Division Oak Ridge National Laboratory, Post Office Box X, Oak Ridge, TN 37831
M. B. Lewis
Affiliation:
Metals and Ceramics Division Oak Ridge National Laboratory, Post Office Box X, Oak Ridge, TN 37831
C. J. Mchargue
Affiliation:
Metals and Ceramics Division Oak Ridge National Laboratory, Post Office Box X, Oak Ridge, TN 37831
Get access

Abstract

An Analytical Electron Microscopy (AEM) investigation of polycrystalline TiB2 implanted with 1 MeV Ni+ to 1 × 1021 ions/m2 has shown that the implanted region remained crystalline and showed no evidence of precipitation. A region containing tangled dislocations extended from the implanted surface to ∼500 nm. Between ∼500 and 750 nm, the microstructure was more complicated and could be indicative of a high density of 5 to 10 nm diam defects. The maximum nickel concentration determined by energy dispersive spectroscopy (EDS) occurred at ∼450 nm, slightly deeper than the calculated depth of 390 nm. Observations after in situ annealing revealed cavities and nickel-rich precipitates. Radiation damage models are invoked to explain the microstructures observed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 27: Symposium E – Ion Implantation and Ion Beam Processing of Materials , 1983 , 407
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*

Research sponsored by the Division of Materials Sciences, U.S. Department of Energy under contract W–7405–eng–26 with the Union Carbide Corporation

References

REFERENCES

1. Zaluzec, N.J., “Introduction to Analytical Electron Microscopy,” Hren, J.J., Goldstein, J.I., and Joy, D.C., eds. (Plenum Press, New York 1979) p. 121.Google Scholar
2. Manning, I. and Mueller, G.P., Comp. Phys. Comm. 7, 85 (1974).Google Scholar
3. Robinson, M.T. and Torrens, I.M., Phys. Rev. B9, 5008 (1974).Google Scholar
4. Mansur, L.K. and Yoo, M.H., J. of Nucl. Mater, 85 and 86 523–532 (1979).Google Scholar
5. Evans, J.H., Mahajan, S., and Eyre, B.L., Phil. Mag. 26, 813 (1972).Google Scholar
6. Mazey, D.J. and Francis, S., Proc. of the Consultant Symposium, “The Physics of Irradiation-Produced Voids,” Harwell (1974).Google Scholar