Microstructural Characterization of Al2O3 Following Simultaneous Triple Ion Bombardment

Published online by Cambridge University Press:  25 February 2011

S. J. Zinkle
S. J. Zinkle*
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, TN 37831-6376, USA
Get access

Abstract

The through-range microstructure of polycrystalline alumina has been examined by cross-section TEM following simultaneous implantation of 2.0 MeV Al+, 1.44 MeV O+, and 0.2 to 0.4 MeV He+ ions at room temperature to a dose of 3.1 keV/atom. The specimen remained crystalline following the irradiation, and four distinct radiation-induced defect features were observed: Network dislocations, dislocation loops, small cavities, and oblong clusters that may be aluminum colloids. The microstructure near the implanted ion region was qualitatively similar to that observed in irradiated regions far from the implanted zone.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 128: Symposium A – Processing and Characterization of Materials Using Ion Beams , 1988 , 363
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. McHargue, C.J. et al., J. Materials for Energy Systems, 8, 255 (1986).Google Scholar
2. Burnett, P.J. and Page, T.F., Rad. Effects 97, 123 (1986).Google Scholar
3. Kobayashi, S., Hioki, T. and Kamigaito, O., Proc. XIth Int. Cong. on Electron Microscopy (Kyoto, 1986), p. 1303.Google Scholar
4. Hioki, T. et al., Nucl. Instrum. Methods B 7/8, 521 (1985).10.1016/0168-583X(85)90425-2Google Scholar
5. Garner, F.A., J. Nucl. Mater. 117, 177 (1983).Google Scholar
6. Lewis, M.B. et al., submitted to Nuci. Instrum. Methods B (1988).Google Scholar
7. Clinard, F.W. Jr., Hurley, G.F., and Hobbs, L.W., J. Nucl. Mater. 108&109, 655 (1982).Google Scholar
8. Lee, W.E., Jenkins, M.L. and Pells, G.P., Phil. Mag. A 51, 639 (1985).10.1080/01418618508245279CrossRefGoogle Scholar
9. Shikama, T. and Pells, G.P., Phil. Mag. A 47, 369 (1983).Google Scholar
10. Katano, Y., Ohno, H. and Katsuta, H., J. Nucl. Mater. 155–157, 366 (1988).CrossRefGoogle Scholar
11. Zinkle, S.J., NATO-Adv. Study Inst. on Structure-Property Relationships in Surface Modified Ceramics, edited by McHargue, C.J. et al. (Kluwer Academic Publishers, 1988).Google Scholar
12. Angelini, P., Sklad, P.S., McHargue, C.J., Lewis, M.B., and Farlow, G.C., these Proceedings.Google Scholar