Ion-Beam and Electron-Beam Induced Amorphization of Berlinite (AIPO4)

Published online by Cambridge University Press:  16 February 2011

N. Bordes  and
R.C. Ewing
N. Bordes
Affiliation:
Department of Earth and Planetary Sciences, University of New Mexico, Albuquerque, NM 87131-1116
R.C. Ewing
Affiliation:
Department of Earth and Planetary Sciences, University of New Mexico, Albuquerque, NM 87131-1116
Get access

Abstract

Berlinite (AIPO4) is isostructural with α-quartz. Like α-quartz, berlinite undergoes a pressure-induced amorphization at 15 ±3 GPa; however, upon release of the pressure, unlike α-quartz which remains amorphous, berlinite returns to the original crystalline structure of the single crystal. Berlinite was irradiated with 1.5 MeV Kr+ at temperatures ranging from 20 to 600K. The onset of amorphization was examined by monitoring the electron diffraction pattern by in situ transmission electron microscopy (TEM) at the HVEM-Tandem Facility at Argonne National Laboratory. The berlinite was easily amorphized at 20K at a relatively low dose of 4x1013 ions/cm2 or 0.05 dpa (displacements per atom). The critical amorphization dose increases with the sample temperature. These experiments also showed that the focused electron beam can locally amorphize the berlinite. After these irradiations, berlinite remained amorphous. At 500 °C, berlinite began to recrystallize: small areas of crystalline material appear in the aperiodic matrix. These results suggest that pressure-induced amorphization and ion-beam induced amorphization, in the case of berlinite, are different processes that result in two different aperiodic structural states.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 373: Symposium Y – Microstructure of Irradiated Materials , 1994 , 395
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Beck, W.R., J. Amer. Ceram. Soc., 32(4), 147 (1949).Google Scholar
2. Hummel, F.A., J. Amer. Ceram. Soc. 32(10), 320 (1949).Google Scholar
3. Schwarzenbach, D., Z. Kristallogr. 123, 11 (1966).Google Scholar
4. Kruger, M.B., Jeanloz, R., Science 249, 647 (1990).Google Scholar
5. Sankara, H., Sharma, S.M., Sikka, S.K., Chidambaran, R., Phys. Rev. B38, 170 (1990).Google Scholar
6. Ogata, K., Takeuchi, Y., Kudoh, Y., Z. Kristallogr. 179, 403 (1987).Google Scholar
7. Ng, H.N., Calvo, C., Can. J. Phys. 54, 638 (1976).Google Scholar
8. Philippot, E., Goiffon, A., Maurin, M., Detaint, J., Schwartzel, J.C., Toudic, Y., Capelle, B., Zarca, A., J. Cryst. Growth 104, 713 (1990).Google Scholar
9. Sil'vestrova, I.M., Aleshko-Ozhevskii, O.P., Pisarevskii, Y.V., Shtemberg, A.A., Mironova, G.S., Fiz. Tverd. Tela (Leningrad) 29, 3454 (1987) [Sov. Phys. Solid State 29, 1979 (1987)].Google Scholar
10. Aleshko-Ozhevskii, O.P., Zvereva, O.V., Pogosyan, A.S., Bezdelkin, V.V., Sov. Phys. Crystallogr. 35(4), 1990.Google Scholar
11. Hobbs, L.W., Pascucci, M.R., Journal de Physique, Colloque C6, 41, 237 (1980).Google Scholar
12. Ziegler, J.F., Biersack, J.P., Littmark, U., The Stopping and Range of Ions in Solids (Pergamon, New York, 1985).Google Scholar