Intersecting basal plane and prismatic stacking fault structures and their formation mechanisms in GaN

Published online by Cambridge University Press:  01 February 2011

Jie Bai
Affiliation:
jbai@ic.sunysb.edu, State University of New York at Stony Brook, Department of Materials Science and Engineering, 314 Old Engineering Bldg., Stony Brook, NY, 11794-2275, United States, 631-827-6482, 631-632-8052
X. Huang
Affiliation:
Department of Materials Science and Engineering, State University of New York at Stony Brook, Stony Brook, New York 11794-2275, U.S.A
M. Dudley
Affiliation:
Department of Materials Science and Engineering, State University of New York at Stony Brook, Stony Brook, New York 11794-2275, U.S.A
Get access

Abstract

Comparative TEM studies have been carried out on GaN/AlN epifilms grown on both on-axis and off-cut 6H-SiC substrates to study the defects formed in the GaN/AlN films and the state of strain relaxation at the interface. Prismatic Stacking Faults (PSFs) are observed to form at I1 type substrate steps in both the on-axis and vicinal samples. In the vicinal samples, the PSFs expand into GaN/AlN film forming intersecting stacking fault configurations comprising faults that fold back and forth from the basal plane (I1 Basal-Plane Stacking Faults; BSFs) to the prismatic plane (PSFs). On the other hand, in the on-axis sample the PSFs are observed to mostly annihilate each other to form enclosed domains confined to the near-interface region. In addition, HRTEM studies suggest the existence of Geometric Partial Misfit Dislocations (GPMDs) at the SiC/AlN interface of the vicinal sample, which form at I2 type substrate steps. These GPMDs simultaneously accommodate the lattice mismatch and stacking sequence mismatch present at the SiC/AlN interface. This provides explanation of the improved strain relaxation observed in the vicinal versus the on-axis sample.

Type
Research Article
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kato, Jun-ichi, Tanaka, Satoru, Yamada, Satoshi, and Suemune, Ikuo, Appl. Phys. Lett. 83 (8), 1569 (2003).CrossRefGoogle Scholar
2. Benyoucef, M., Kuball, M., Koleske, D. D., Wickenden, A. E., Henry, R. L., Fatemi, M. and Twigg, M. E., Mater. Sci. Eng. B93, 15 (2002).CrossRefGoogle Scholar
3. Grudowski, P. A., Holmes, A. L., Eiting, C. J. and Dupuis, R. D., Appl. Phys. Lett. 69 (24), 3626 (1996).CrossRefGoogle Scholar
4. Bai, J., Huang, X., Dudley, M., Wagner, B., Davis, R. F., Wu, L., Sutter, E., Zhu, Y., J. Appl. Phys. 98, 063510 (2005).CrossRefGoogle Scholar
5. Shi, Y., Xie, Z.Y., Liu, L.H., Edgar, J.H., and Kiball, M., J. Cryst. Growth, 233, 177 (2001).CrossRefGoogle Scholar
6. Sakamoto, Kunihiro, Miki, Kazushi and Sakamoto, Tsunenori, J. Crys. Growth 99, 510 (1990).CrossRefGoogle Scholar
7. Tyc, S., Silicon Carbide and Related Materials, edited by Spencer, M. G., Devaty, R. P., Edmond, J. A., Khan, M. A., Kaplan, R. and Rahman, M. M. (Inst. of Physics, Bristol), p. 333 (1994).Google Scholar
8. Xie, M. H., Seutter, S. M., Zhu, W. K., Zheng, L. X., Wu, Huasheng, and Tong, S. Y., Phys. Rev. Lett. 82(13), 2749 (1999).CrossRefGoogle Scholar
9. Vermaut, P., Ruterana, P., Nouet, G. and Morkoc, H., Phil. Mag. A 75 (1), 239 (1997).CrossRefGoogle Scholar
10. Pirouz, P. and Yang, J. W., Ultramicroscopy 51, 189 (1993).CrossRefGoogle Scholar
11. Northrup, John E., Appl. Phys. Lett. 72(18), 2316 (1998)CrossRefGoogle Scholar
12. Huang, X. R., Bai, J., Dudley, M., Wagner, B., Davis, R. F., and Zhu, Y., Phys. Rev. Lett. 95, 086101 (2005).CrossRefGoogle Scholar