Effect on Performance of Composition of Li-ion carbon Anodes derived from PMAN/DVB copolymers

Published online by Cambridge University Press:  10 February 2011

Ronald A. Guidotti  and
William R. Even
Ronald A. Guidotti
Affiliation:
Sandia National Laboratories P.O. Box 5800, Albuquerque, NM 87185-0614, raguido@sandia.gov
William R. Even
Affiliation:
Sandia National Laboratories P.O. Box 969, Livermore, CA 94551
Get access

Abstract

The effects on electrochemical performance of the nitrogen content of disordered carbons derived from polymethacryonitrile (PMAN)-divinylbenzene (DVB) copolymers were examined in galvanostatic cycling tests between 2 V and 0.01 V vs. Li/Li+ in IM LiPF6/ethylene carbonate (EC)-dimethyl carbonate (DMC). The first-cycle reversible capacities and coulombic efficiencies increased with increase in the level of nitrogen for samples prepared at 7000°C. However, the degree of fade also increased. Similar tests were performed on materials that were additionally heated at 1,000° and 1,300°C for five hours. Loss of nitrogen, oxygen, and hydrogen occurred under these conditions, with none remaining at the highest temperature in all cases but one. The pyrolysis temperature dominated the electrochemical performance for these samples, with lower reversible and irreversible capacities for the first intercalation cycle as the pyrolysis temperature was increased. Fade was reduced and coulombic efficiencies also improved with increase in temperate. The large irreversible capacities and high fade of these materials makes them unsuitable for use in Li-ion cells.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 575: Symposium CC – New Materials for Batteries & Fuel Cells , 1999 , 165
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Manev, V., Naidevnov, I., Puresheva, B., Zlatilova, P., and Pistoia, G., J. Power Sources, 55 211(1995).Google Scholar
2. Xing, W., Xue, J. S., and Dahn, J. R., J. Electrochem. Soc., 143 (10), 3048 (1996).Google Scholar
3. Zheng, T., Liu, Y., Fuller, E. W., Tseng, S., von Sacken, U., and Dahn, J. R., J. Electrochem. Soc., 142 (8), 2581 (1995).Google Scholar
4. Wilson, A. M. and Dahn, J. R., J. Electrochem. Soc., 142 (2), 326 (1995).Google Scholar
5. Dahn, J. R., Sleigh, A. K., Shi, H., Way, B. M., Weydanz, W. J., Reimers, J. N., Zhong, Q., and von Sacken, U., Lithium Batteries - New Materials, Development and Perspectives, Pistoia, G., ed. (Elsevier, New York, 1994), p. 1.Google Scholar
6. Zavadil, Kevin R., Guidotti, Ronald A., and Even, William R., Proc. 1997 Fall MRS Meeting, Boston. MA, 539 (1997).Google Scholar
7. Even, William R., Peng, Lawrence W., Yuang, Nancy, Guidotti, Ronald, and Headley, Thomas, Proc. 1997 Fall MRS Meeting, Boston, MA, 619 (1997).Google Scholar
8. Guidotti, Ronald A. and Johnson, Bryan J., Proc. 38th Power Sources Conf, 440 (1998).Google Scholar
9. Even, W. R. and Gregory, D. P., MRS Bulletin, 19 (4), 29 (1994).Google Scholar