The Effect of the Passivation Material on the Stress and Stress Relaxation Behavior of Narrow Al-Si-Cu Lines

Published online by Cambridge University Press:  15 February 2011

A. Witvrouw ,
P. Flinn  and
K. Maex
A. Witvrouw
Affiliation:
IMEC, Kapeldreef 75, 3001 Leuven, Belgium
P. Flinn
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA, U.S.A.
K. Maex
Affiliation:
IMEC, Kapeldreef 75, 3001 Leuven, Belgium
Get access

Abstract

800 nm thick and 1 jim wide Al-lwt.%Si-0.5wt.% Cu parallel lines with I μm spacing were passivated with PECVD oxide, oxynitride or nitride. Substrate curvature measurements as a function of temperature and XRD-measurements at room temperature were used to characterize macroscopic samples of these parallel Al-Si-Cu-lines. By using both techniques the average inplane stresses for the Al-Si-Cu lines as well as for the covering passivation material can be determined as a function of temperature. The highest and lowest stresses in the Al-Si-Cu are observed for lines with nitride and oxide passivations, respectively. Also the number of voids in the lines after a storage test at 250 °C is clearly highest for a nitride passivation and lowest for an oxide passivation.

The stress in the passivation itself and its temperature dependence is found to be very different from the stress in a blanket passivation film.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 428: Symposium L – Materials Reliability in Microelectronics VI , 1996 , 519
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Smith, J. F. and Wagner, I., Advanced Aluminum Metallization. Part I: Aluminum Thin Film Properties, (1991 MRC Thin Film School), 2.Google Scholar
[2] d'Heurle, F. M. and Ho, P.S.: inThin FilmsInterdiffusion and Reactions, ed. by Poate, J., Tu, K. and Mayer, J. (N.Y.), 293 (1978).Google Scholar
[3] Okabayashi, H., Mat. Sci. Eng. Ri 1 (5), 191–241 (1993).Google Scholar
[4] Sauter, A.I., Nix, W.D., IEEE Trans. Comp. Hybr. Man. Tech., 15 (4), 594–600 (1992).Google Scholar
[5] Witvrouw, A., Proost, J., Deweerdt, B., Roussel, Ph. and Maex, K., Mat. Res. Soc. Symp. Proc. 356, 441–446 (1995).Google Scholar
[6] Nix, W.D., Metall. Trans A 20A, 3317 (1989).Google Scholar
[7] Witvrouw, A. and Spaepen, F., JAP 73 (11), 7344 (1993).Google Scholar
[8] Flinn, P.A. and Chiang, Chieng, JAP 67 (6), 2927 (1990).Google Scholar
[9] Burges, U., Eppler, I., Schilling, W., Schroeder, H. and Trinkaus, H., ‘Analysis of Stresses in Passivated Metal Lines’, presented at the 3rd Conf. on Stress Phenomena in Metallizations, Stanford, June 1995.Google Scholar
[10] Besser, P.R., Marieb, T.N., Lee, J., Flinn, P.A. and Bravman, J.C., J. Mater. Res. 11, 184 (1996).Google Scholar
[11] Sauter, A.I. and Nix, W.D., J. Mater. res. 7 (5), 1133 (1992).Google Scholar