Effect of growth rate on microstructure and microstructure evolution of directionally solidified Nb-Si alloys

Published online by Cambridge University Press:  21 September 2018

Yoshihito Sekito
Affiliation:
Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
Seiji Miura
Affiliation:
Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
Kenji Ohkubo
Affiliation:
Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
Tetsuo Mohri
Affiliation:
Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
Norihito Sakaguchi
Affiliation:
Center for Advanced Research of Energy Conversion Materials, Hokkaido University
Seiichi Watanabe
Affiliation:
Center for Advanced Research of Energy Conversion Materials, Hokkaido University
Yoshisato Kimura
Affiliation:
Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology
Yoshinao Mishima
Affiliation:
Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology
Get access

Abstract

In the present work, Nb-18.1Si-1.5Zr alloy rods are produced with a growth rate ranging from 1.5 to about 1500 mm/h using the optical floating zone (OFZ) furnace. A part of each specimen is heat-treated at 1650 oC for 100 h. The microstructure was observed using SEM and TEM and analyzed using EPMA and EBSD.

Eutectic-cells are observed in as-grown specimens with a growth rate of 150 mm/h or higher. It is found by EBSD analysis that the solidification direction of Nb is along <113> and that of Nb3Si is along <001], and {112} of Nb and {110) of Nb3Si are parallel. The present crystallographic orientation relationship between Nb and Nb3Si is different from that found in previous reports by several researchers. It was also confirmed that the heat-treated microstructure in the specimen grown by OFZ with a growth rate of 150 mm/h is similar to that in the heattreated specimen prepared by arc-melting.

Type
Articles
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Ghosh, G., Olson, G. B., Acta Mater. 55 (2007), 32813303.Google Scholar
[2] Bewlay, B., Jackson, M., Zhao, J. Subramanian, P., Mendiratta, M., Lewandowski, J., MRS Bull. 28 (2003), 646653.Google Scholar
[3] Miura, S., Aoki, M., Saeki, Y., Ohkubo, K., Mishima, Y., Mohri, T., Metall. Mater. Trans. A, 36 (2005), 489496.Google Scholar
[4] Miura, S., Ohkubo, K., Mohri, T., Intermet., 15 (2007), 783790.Google Scholar
[5] Miura, S., Murasato, Y., Ohkubo, K., Kimura, Y., Sekido, N., Mishima, Y., Mohri, T., MRS. Symp. Proc. 980 (2006), 0980-II05-33.Google Scholar
[6] Miura, S., H.|Kim, J., Ohkubo, K., Kimura, Y., Sekido, N., Mishima, Y., Mohri, T., Mater. Sci. Forum, 539-543 (2007), 15071522.Google Scholar
[7] Veyssiere, P., Douin, J., ed. Westbrook, J. H., Fleischer, R. L., Intermetallic Compounds, John Wiley & Sons Ltd, Chichester, Vol. 1 (1995), p. 530.Google Scholar
[8] Cockram, B., Lipsitt, H. A., Srinivasan, R., Weiss, I., Scr. Metall. Mater., 25 (1991), 21092114.Google Scholar
[9] Elliott, R., Eutectic Solidification Processing, Butterworths & Co Ltd., London, (1983), p. 92.Google Scholar
[10] Drawin, S., Petit, P., Boivin, D., Metall. Mater. Trans. A, 36 (2005), 497505. Google Scholar
[11] Sekido, N., Kimura, Y., Miura, S., Mishima, Y., Mater. Sci. Eng., A, 444 (2007), 5157.Google Scholar
[12] Sekido, N., Wei, F. G., Kimura, Y., Miura, S., Mishima, Y., Philos. Mag. Lett., 86, (2006).Google Scholar