Dislocation Interactions in Two-Phase Tial Alloys

Published online by Cambridge University Press:  01 January 1992

M.A. Morris
M.A. Morris*
Affiliation:
Institute of Structural Metallurgy, University of Neuchâtel Av. Bellevaux 51, 2000 Neuchâtel, Switzerland,
Get access

Abstract

Dislocation configurations produced by room and high temperature deformation of two alloys with compositions Ti-48A1 and Ti-47.5Al-2.5Cr have been compared. At room temperature the major differences between the two alloys is the increased twinning activity and that of 1%2 <112] superdislocations in the chromium containing alloy while the binary alloy contains a larger contribution from <101] superdislocations. At 400°C, the temperature at which a peak in flow stress is observed in both alloys, an increase in twinning activity and emission of 1%2<110] dislocations on (001) planes is observed from twin intersections in both materials. The contribution of superdislocations to the deformation process is limited and their effect on the flow stress increase appears irrelevant. Instead the anomalous strengthening effect has been related to the cross-slip of single dislocations from cube planes, on which they are emitted, to octahedral planes where they can also glide.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 403
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kawabata, T., Kanai, T. and Izumi., O. Acta Metall., 33,1355, (1985)Google Scholar
2. Huang, S.C., Scripta Metall., 22, 1885, (1987)Google Scholar
3. Huang, S.C. and Hall, E.L., Metall. Trans. A, 22, 427, (1991)Google Scholar
4. Kim, Y.W., Acta Metall. Mat., 40, 1121, (1992)Google Scholar
5. Vasudevan, V. K., Stucke, M.A., Court, S.A. and Fraser, H.L., Phil. Mag. Letters, 59, 299, (1989)Google Scholar
6. Inui, M., Nakamura, A., Oh, M.H. and Yamaguchi, M., Phil. Mag. 66, 557, (1992)Google Scholar
7. Hug, G., Loiseau, A. and Veyssière, P., Phil. Mag. A, 57, 499, (1988)Google Scholar
8. Greenberg, B.A., Antonova, O.V., Indenbaum, V.N., Karkina, L.A., Notkin, A.B., Ponomarev, M.V., Acta Metall. Mat., 40, 815, (1992)Google Scholar
9. Morris, M.A., Phil. Mag. in pressGoogle Scholar
10. Hug, G. and Veyssière, P. in Electron Microscopy in Plasticity and Fracture Research of Materials, edited by Messeschmidt, U., Appel, F. and Schmidt, V., Akademic-Verlag (Berlin), 451, (1990)Google Scholar