Boron Activation During Solid Phase Epitaxial Regrowth

Published online by Cambridge University Press:  17 March 2011

C. D. Lindfors ,
K. S. Jones ,
M. E. Law ,
D. F. Downey  and
R. W. Murto
C. D. Lindfors
Affiliation:
Swamp Center, University of Florida, Gainesville, FL
K. S. Jones
Affiliation:
Swamp Center, University of Florida, Gainesville, FL
M. E. Law
Affiliation:
Swamp Center, University of Florida, Gainesville, FL
D. F. Downey
Affiliation:
Varian Semiconductor Equipment Associates, Gloucester, MA
R. W. Murto
Affiliation:
International SEMATECH, Austin, TX
Get access

Abstract

To continue scaling dimensions of transistors, higher dopant concentration levels are needed for ultra-shallow contacts. Therefore studies of dopant activation have been performed in preamorphized silicon wafers with various boron implant conditions to determine the maximum achievable dopant concentrations after Solid Phase Epitaxial Regrowth (SPER) alone. In the first experiment a silicon piece was preamorphized with a 30 keV, 1×1015 cm−2 and 90 keV, 1×1015 cm−2 Si+ implant followed by a 30 keV, 1×1015 cm−2 B+ implant. Solid phase epitaxial regrowth at 500 °C indicates that boron can be activated at low temperatures. Ultra Low Energy (ULE) implants were studied in the second experiment. Silicon wafers were implanted with 2.5 keV, 1×1015 cm−2 Si+ to amorphize and then B+ was implanted at 0.5 keV in the dose range of 1×1015 to 9×1015 cm−2. Samples were annealed in the temperature range of 500 to 650 °C. High concentrations of boron make it difficult to fully regrow amorphous layers and thus yield marginal electrical properties. Much of the boron remains inactive, particularly at the higher dose implants. In both experiments Variable Angle Spectroscopic Ellipsometry (VASE) is used to measure amorphous layer thickness and Hall effect measures active boron dose. For the first experiment, Secondary Ion Mass Spectrometry (SIMS) data compares chemical dose to active dose during the regrowth process. Sheet resistance data is obtained from a four point probe for the ULE implant experiment.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 610: Symposium B – Si Front End Processing - Physics & Technology..II , 2000 , B10.2
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Harrington, W. L., Magee, C. W., Pawlik, M., Downey, D. F., Osburn, C. M., and Felch, S. B., J. Vac. Sci. Technol. B, 16(1), 286 (1998).10.1116/1.589796Google Scholar
[2] Landi, E., Armigliato, A., Solmi, S., Kogler, R., and Wieser, E., Appl. Phys. A, 47, 359 (1988).10.1007/BF00615499Google Scholar
[3] Murrel, A. J., Collart, E. J. H., Foad, M. A., and Jennings, D., J. Vac. Sci. Technol. B, 18(1), 286 (2000).Google Scholar
[4] Csepregi, L., Kennedy, E. F., Gallagher, T. J., and Mayer, J. W., J. Appl. Phys., 48 (10), 4234 (1977).10.1063/1.323408Google Scholar
[5] Drosd, R. and Washburn, J., J. Appl. Phys., 53 (1), 397 (1982).10.1063/1.329901Google Scholar
[6] Poate, J. M. and Williams, J. S., Ion Implantation and Beam Processing, (Academic Press, New York, 1984) p. 27.Google Scholar
[7] Mizushima, I., Watanabe, M., Murakoshi, A., Hotta, M., and Kashiwagi, M., Appl. Phys. Lett., 63 (3), 373 (1993).10.1063/1.110047Google Scholar
[8] Mizushima, I., Murakoshi, A., Watanabe, M.,M. Yoshiki, Hotta, M., and Kashiwagi, M., Jpn. J. Appl. Phys., 33, 404 (1994).10.1143/JJAP.33.404Google Scholar
[9] Schroder, D. K., Semiconductor Material and Device Characterization, (John Wiley & Sons, Inc., New York, 1990) p. 233.Google Scholar
[10] Dale Jacobson (private communication).Google Scholar