Stabilization of electroluminescence and photoluminescence of porous n-silicon by chemical oxidation in H2O2

Published online by Cambridge University Press:  28 February 2011

F. Kozlowski ,
W. Wagenseil ,
P. Steiner  and
W. Lang
F. Kozlowski
Affiliation:
Fraunhofer Institute for Solid State Technology, Hansastrasse 27d, D-80686 Munich, Germany
W. Wagenseil
Affiliation:
Fraunhofer Institute for Solid State Technology, Hansastrasse 27d, D-80686 Munich, Germany
P. Steiner
Affiliation:
Fraunhofer Institute for Solid State Technology, Hansastrasse 27d, D-80686 Munich, Germany
W. Lang
Affiliation:
Fraunhofer Institute for Solid State Technology, Hansastrasse 27d, D-80686 Munich, Germany
Get access

Abstract

We have oxidized porous (n-)silicon samples in solutions of H202 and have found that PL can be stabilized at a high level. The PL intensity of as prepared samples (PL quantum efficiencies in the range of 5 %) degrades to about 1/3 of the initial value in some ten minutes (the exact value depends on the experimental conditions). After having treated the samples for about 30 - 45 minutes in hydrogen peroxide it can be observed that bright PL remains stable for hours. These results confirm similar experiments performed with porous silicon made from p-substrates1. While red electroluminescing samples have shown long time stability for about 100 hours2, samples with blue-green electroluminescence have a lifetime of about 20 - 40 minutes. Oxidizing electroluminescent samples as described above results in a stabilization of electroluminescence for more than 7 hours.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 358: Symposium F – Microcrystalline and Nanocrystalline Semiconductors , 1994 , 677
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Nakajima, A., Itakura, T., Watanabe, S. and Nakayama, N., Appl. Phys. Lett. 61, 46 (1992)Google Scholar
2 Lang, W., Steiner, P. and Kozlowski, F., Journ. Lumin. 57, 341 (1993)Google Scholar
3 Tischler, M., Collins, R., Stathis, J. and Tsang, J. Appl. Phys. Lett. 60, 639 (1992)Google Scholar
4 Mayer, B. K., et al. , Appl. Phys. Lett. 63, 2110 (1993)Google Scholar
5 Olsen, J. E. and Shimura, F., Appl. Phys. Lett. 53, 1934 (1988)Google Scholar
6 Inoue, K., Matsuda, O., Maehashi, K., Nakashima, H. and Murase, K. Japanese J. Appl. Phys., Part 2 [Letters] 31, L997 (1992).Google Scholar