Improvement Of Cavitation Erosion Resistance and Corrosion Resistance Of Brass by Laser Surface Modification

Published online by Cambridge University Press:  10 February 2011

K. F. Tam ,
F. T. Cheng  and
H. C. Man
K. F. Tam
Affiliation:
Department of Applied Physics, The Hong Kong Polytechnic University, Hong Kong, People's Republic of China
F. T. Cheng
Affiliation:
Department of Applied Physics, The Hong Kong Polytechnic University, Hong Kong, People's Republic of China
H. C. Man
Affiliation:
Department of Manufacturing Engineering, The Hong Kong Polytechnic University, Hong Kong, People's Republic of China
Get access

Abstract

Laser surface modification of brass (Cu-38Zn-1.5Pb) using AISiFe and NiCrSiB alloy was achieved by using a 2kW continuous wave Nd-YAG laser with the aim of improving the cavitation erosion resistance and corrosion resistance. The alloying powder was preplaced on the brass substrate by thermal spraying to a thickness of 350µm, followed by laser beam scanning to effect melting, mixing and alloying. A modified surface was achieved by overlapping of adjacent tracks. The cavitation erosion resistance and the anodic polarization characteristics of the laser surface modified specimens in 3.5% NaCI solution at 23°C were studied by means of a 20kHz ultrasonic vibrator at a peak to peak amplitude of 60µm and a potentiostat respectively. The cavitation erosion resistance of the specimens modified with AlSiFe and NiCrSiB was improved by a factor of 3 and 7 respectively, compared with that of the brass substrate. Potentiodynamic test, however, indicated that the corrosion resistance of specimens modified with AlSiFe deteriorated, as reflected by a shift of the polarization curve towards higher current densities. On the other hand, the corrosion resistance of specimens modified with NiCrSiB was significantly improved, as evidenced by the presence of a passive region (from −175 mV to −112 mV) and a reduction in the anodic current density by at least an order of magnitude compared with the substrate at the same anodic potential. The hardness profile and the compositional profile were measured using a Vickers hardness tester and EDX respectively. The microstructure and the surface morphology of the specimens were investigated with the aid of SEM and optical microscopy.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 617: Symposium J – Laser-Solid Interactionsfor Materials Processing , 2000 , J3.2
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Karimi, A., Martin, J. L., International Metals Reviews, 31, 1–26 (1986).Google Scholar
2 Polan, N. W., “Corrosion of Copper and Copper Alloys” in: ASM Handbook, Vol. 13, Corrosion, ASM International, USA, (1992).Google Scholar
3 Steen, W. M., in: Draper, C. W., Mazzoldi, P. (Eds), Laser Surface Treatment of Metals, 387–396, Martinus Nijhoff Publishers, Dodrechent, (1996).Google Scholar
4 Mordike, B. L., in: Cahn, R. W., Haasen, P., Kramer, E. J. (Eds), Materials Science and Technology: Processing of Metals and Alloys, Vol. 15 VCH, New York, 111–136 (1991).Google Scholar
5 Dehm, G. et al. , Wear, 225–229, 18–26 (1999).Google Scholar
6 ASTM Standard G32-92, Standard Test Method for Cavitation Erosion Using Vibratory Apparatus, in: Annual Book of ASTM Standards, Vol. 03.02, ASTM, Philadelphia, (1992).Google Scholar
7 Vyas, B., Hansson, I. L. H., Corrosion Science, 30, 8-9, 261–270 (1990).Google Scholar
8 ASTM Standard G5-94, Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements, in: Annual Book of ASTM Standards, Vol. 03.02, ASTM, Philadelphia, (1994).Google Scholar