Chemical Spray Pyrolysis of Complex Thin Solid Films

Published online by Cambridge University Press:  22 February 2011

Clayton W. Bates Jr ,
Elizabeth B. Varner ,
Svetlana Alshvang  and
Keith Summers
Clayton W. Bates Jr
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Elizabeth B. Varner
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Svetlana Alshvang
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Keith Summers
Affiliation:
Tuskegee University, Department of Electrical Engineering, Tuskegee, AL 36088
Get access

Abstract

Chemical spray pyrolysis (CSP) is a technique in which compounds of the constituents of the thin film to be fabricated are dissolved in an aqueous solution which is subsequently sprayed onto a heated substrate using nitrogen as the atomizing gas. At relatively low substrate temperatures (150–400°C) chemical reactions take place in which film formation of the desired compound occurs concomitantly with the release of volatile chemical reactants. The technique has advantages that include: (1) simplicity, (2) low cost and simple equipment, (3) the ability to prepare films over large areas with various shapes with relative ease and (4) the possibility of varying the physical properties through chemical means in known ways at modest temperatures. Results on the preparation of CuInSe2 which is a defect dominated semiconductor of technological interest are presented. Both n- and p- type materials were prepared with resistivities varying from 10−2 – 104 ohm-cm illustrating the use of the control of solution chemistry to produce films with reproducibly controlled properties.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 282: Symposium E – Chemical Perspectives of Microelectronic Materials III , 1992 , 653
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Mochel, J. M., 1951, U.S. Patents No's. 2,564,707, 2,564,987, 2,564,709, 2,564,710, 2,564,708, 2,564,706.Google Scholar
2. Chamberlin, R. R. and Skarman, J. S., J. Electrochem. So. 113 (1) 86 (1966).Google Scholar
3. Chamberlin, R. R. and Skarman, J. S., Solid State Electron. 9, 819 (1966).Google Scholar
4. Mooney, J. B. and Radding, S. B., Ann. Rev. Mater. Sci. 12, 81 (1982).Google Scholar
5. lynch, A. and Bates, C. W. Jr, “Deposition of Y-Ba-Cu-O Superconducting Thin Films by Chemical Spray Pyrolysis,” Master's Research Report, Stanford University, CA (1988).Google Scholar
6. Bates, C. W. Jr, and Varner, E. B., unpublished results, 1991.Google Scholar
7. Brown, B. J., “Chemical Spray Pyrolysis of Copper Indium Diselenide/Cadmium Sulfide Solar Cells,” PhD. Thesis, Stanford University, Stanford, CA 1989).Google Scholar
8. Varner, E. B. and Strifler, W., unpublished results on X-ray Diffraction and Electrical Transport measurements on p- CuInSe2 prepared by Chemical Spray Pyrolysis, Stanford University 1991.Google Scholar
9. Noufi, R., Axton, R., Herrington, C., and Deb, S. K., Appl. Phys. Lett. 45 (6), 668 (1984).Google Scholar
10. Abernathy, C. R., “Chemical Spray Pyrolysis of Copper Indium Diselenide Thin Films and Devices,” PhD. Thesis, Stanford University, Stanford, CA (1985).Google Scholar