Size matters in mechanical behavior of bulk metallic glasses

By Aditi Risbud May 9, 2017
size-matters
Evolution of failure in the in situ tested small Pd77.5Cu6Si16.5 sample. The onset of shear-band formation for the pre-cracked sample occurred around ∼200 N before shear bands formed both in the back of the sample and from the root of the razor-notch at a load of ∼800 N, leading to pronounced crack-tip opening displacement as shown in this figure. Credit: Bernd Gludovatz, Lawrence Berkeley National Laboratory.

Based on their recent work understanding variations in the properties of BMGs, scientists at Lawrence Berkeley National Laboratory, University of California, Berkeley, and ETH Zürich examined the variation in fracture toughness of the palladium-based metallic glass Pd77.5Cu6Si16.5. Led by Bernd Gludovatz and Robert O. Ritchie, the team studied the material in a highly constrained single-edge notched bend geometry in two different sizes: one significantly smaller than, and another comparable to, the critical bending thickness—which is the critical dimension below which the number of shear bands needed to demonstrate significant ductility when subjected to bending is achieved. The resultant fracture toughness and fracture behavior were compared with ASTM-recommended sample geometries and size configurations.

As reported in a recent issue of Acta Materialia, the research team found marked differences between the toughness values and failure characteristics of the two samples. The larger samples showed significantly larger variations in toughness values—and all essentially failed catastrophically—while none of the smaller samples failed catastrophically, yet displayed far less scatter in their measured toughness.

To gain further insight, in situ tests were carried out in a scanning electron microscope. These revealed that metallic glasses show a transition in fracture behavior that is linked to their sample size. Samples with ligament widths—that is, the dimension from the root of a pre-cracked notch to the back of the sample—larger than the critical bending thickness of the material demonstrated brittle failure characteristics and low fracture toughness values with only small variations. In contrast, samples with dimensions comparable to the critical bending thickness yielded highly variable, size- and geometry-dependent fracture toughness results.

“Based on the findings of this study, it is apparent that the reliable measurement of the toughness of metallic glasses presents a considerable challenge. These materials clearly can display quite brittle behavior in appropriately large sections yet distinctly different fracture properties in much thinner sections,” Ritchie says. “These insights may help us unlock the technological promise of BMGs and the scientific underpinnings of their complex metallic glass behavior.”

In general, the team’s findings suggest that the fracture toughness measured for metallic glass samples tested with ligament widths either comparable or below the critical bending thickness should be considered size- and geometry-dependent. A ligament and thickness dimension exceeding the critical bending thickness is mandatory to determine a size- and geometry-independent fracture toughness of a metallic glass.

“This is a meaningful beginning for revealing the real fracture behavior of metallic glasses,” says K.-F. Yao of Tsinghua University, who was not involved in this research. “Additional studies will help our community fully understand the exact effects of size and geometry in determining precisely the fracture toughness values of BMGs, which is based on the many factors affecting their fracture behavior such as sample size and shape, notch radius, fatigue crack, loading condition, and measuring method.”

This article originally published in MRS Bulletin.