Hydrogen Storage in Magnesium-Based Alloys

Published online by Cambridge University Press:  29 November 2013

R.B. Schwarz
Get access

Extract

Magnesium can reversibly store about 7.7 wt% hydrogen, equivalent to more than twice the density of liquid hydrogen. This high storage capacity, coupled with a low price, suggests that magnesium and magnesium alloys could be advantageous for use in battery electrodes and gaseous-hydrogen storage systems. The use of a hydrogen-storage medium based on magnesium, combined with a fuel cell to convert the hydrogen into electrical energy, is an attractive proposition for a clean transportation system. However, the advent of such a system will require further research into magnesium-based alloys that form less stable hydrides and proton-conducting membranes that can raise the operating temperature of the current fuel cells.

Following the U.S. oil crisis of 1974, research into alternative energy-storage and distribution systems was vigorously pursued. The controlled oxidation of hydrogen to form water was proposed as a clean energy system, creating a need for light and safe hydrogen-storage media. Extensive research was done on inter-metallic alloys, which can store hydrogen at densities of about 1500 cm3-H2 gas/ cm3-hydride, higher than the storage density achieved in liquid hydrogen (784 cm3/cm3 at –273°C) or in pressure tanks (˜200 cm3/cm3 at 200 atm). The interest in metal hydrides accelerated following the development of portable electronic devices (video cameras, cellular phones, laptop computers, tools, etc.), which created a consumer market for compact, rechargeable batteries. Initially, nickel-cadmium batteries fulfilled this need, but their relatively low energy density and the toxicity of cadmium helped to drive the development of higher-energy-density, less toxic, rechargeable batteries.

Type
Advanced Materials for Energy Storage
Information
MRS Bulletin , Volume 24 , Issue 11 , November 1999 , pp. 40 - 44
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Sakai, T., Matsuoka, M., and Iwakura, C., in Handbook of Hie Physics and Chemistry of Rare Earths, vol. 21, edited by Gschneidner, K.A. Jr. and Eyring, L. (Elsevier, 1995).Google Scholar
2.Schlapbach, L., ed., Hydrogen in Intermetallic Compounds, vol. 63 (Springer-Verlag, Berlin, 1968) and Topics in Applied Physics, vol. 67 (Springer-Verlag, Berlin, 1992).Google Scholar
3.Schwarz, R.B. and Khachaturyan, A.G., Phys. Rev. Lett. 74 (1995) p. 2523.CrossRefGoogle Scholar
4.Reilly, J.J., in Hydrogen Storage Materials, Batteries,and Electrochemistry, edited by Corrigan, D.A. and Srinivasan, S. (The Electrochemical Society, Pennington, NJ, 1992) p. 24.Google Scholar
5.Anani, A., Visantin, A., Petrov, K., Srinivasan, S., Reilly, J.J., Johnson, J.R., Schwarz, R.B., and Desch, P.B., J. Power Sources 47 (1994) p. 261.CrossRefGoogle Scholar
6.Lei, Y.-Q., Wu, Y.-M., Yang, Q.-M., Wu, J., and Wang, Q.-D., Z. Phys. Chem. 183 (1994) p. 379.CrossRefGoogle Scholar
7.Cui, N. and Luo, J.L., Electrochim. Acta 44 (1998) p. 711 and Electrochim. Acta 44 (1999) p. 3549.CrossRefGoogle Scholar
8.Guo, N.H., Woo, J.H., and Lee, K.S., J. Alloys Compd. 288 (1999) p. 286.CrossRefGoogle Scholar
9.Reilly, J.J., in Proc. Int. Symp. on Hydrides for Energy Storage, edited by Andersen, A.F. and Maeland, A.J. (Pergamon Press, Elmsford, NY, 1978) p. 527.CrossRefGoogle Scholar
10.Wasz, M.L. and Schwarz, R.B. (unpublished).Google Scholar
11.Gross, K.J., Spatz, P., Zuettel, A., and Schlapbach, L., J. Alloys Compd. 240 (1996) p. 206 and J. Alloys Compd. 261 (1997) p. 276.CrossRefGoogle Scholar
12.Liu, F.-J., Sandrock, G., and Suda, S., J. Alloys Compd. 190 (1992) p. 57.CrossRefGoogle Scholar
13.Krozer, A. and Kasemo, B., J. Less-Common Met. 160 (1990) p. 323.CrossRefGoogle Scholar
14.Zhdanov, V.P., Krozer, A., and Kasemo, B., Phys. Rev. B 47 (1993) p. 11044.CrossRefGoogle Scholar
15.Hoffman, K.C., Winsche, W.E., Wiswall, R.H., Reilly, J.J., Sheehan, T.V., and Weide, C.H., Int. Automotive Eng. Congress, Detroit, MI (Society of Automotive Engineers, New York, 1969) Paper No. 690232.Google Scholar
16.Savadogo, O., J. New Mater. Electrochem. Sys. 1 (1998) p. 47.Google Scholar
17.Khrussanova, M., Terzieva, M., and Peshev, P., Int. J. Hydrogen Energy 16 (1991) p. 265.Google Scholar
18.Cui, N., He, P., and Luo, J.L., Electrochim. Acta 44 (1999) p. 3549.CrossRefGoogle Scholar
19.Orimo, S., Fujii, H., and Tabata, M., J. Alloys Compd. 210 (1994) p. 37.CrossRefGoogle Scholar
20.Liang, G., Boily, S., Hout, J., Neste, A. Van, and Schultz, R., Mater. Sci. Forum 269-272 (1998) p. 1049.CrossRefGoogle Scholar
21.Tessier, P., Enoki, H., Bououdina, M., and Akiba, E., J. Alloys Compd. 268 (1998) p. 285.CrossRefGoogle Scholar
22.Zaluski, L., Zaluska, A., and Strom-Olsen, J.O., J. Alloys Compd. 217 (1995) p. 245.CrossRefGoogle Scholar
23.Ogden, J.M., Int. J. Hydrogen Energy 24 (1999) p. 709.CrossRefGoogle Scholar