Microstructural Characterization and Phase Diagram Calculation of a Less Known Al–Fe–Mn–Si Phase in a SiCp/2014Al Composite

Published online by Cambridge University Press:  16 May 2019

Ying Hu ,
Qiubao Ouyang ,
Bingbing Zhao  and
Lanting Zhang
Ying Hu
Affiliation:
School of Materials Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China Baoshan Iron & Steel Co., Ltd. Research Institute, 655 Fu Jin Road, Shanghai 201900, China
Qiubao Ouyang
Affiliation:
School of Materials Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China
Bingbing Zhao
Affiliation:
School of Materials Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China Materials Genome Initiative Center, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China
Lanting Zhang*
Affiliation:
School of Materials Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China Materials Genome Initiative Center, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240, China
*
*Author for correspondence: Lanting Zhang, E-mail: lantingzh@sjtu.edu.cn
Get access

Abstract

A systematic characterization of a less known Al, Fe, Mn, and Si phase in a SiC particulate-reinforced 2014Al composite (SiCp/2014Al) was performed. In addition to the expected CuAl2 phase, the Al, Fe, Mn, and Si phase was formed as either an adhesion (>1 µm) onto SiC in the as-cast composite, or as a precipitate (<100 nm) in the matrix after hot extrusion. The structure of the phase was identified as cubic by both X-ray diffraction and selected area electron diffraction (SAED). The SAED pattern also indicated that the structure belongs to the Pm$\bar{3}$ space group instead of Im$\bar{3}$. The thermodynamic phase diagram was calculated, confirming the presence of an α-AlFeMn or α-AlFeSi phase in the Al–Fe–Mn and Al–Fe–Si ternary systems, respectively, within the Fe, Mn, and Si content range corresponding to 2014Al. Wavelength-dispersive spectroscopy analysis indicated that the composition of the phase is close to Al12(Fe, Mn)3Si2, in which the Mn/Fe ratio is in the range of 0.6–1.4. The determined Mn/Fe ratio corresponds to the nominal composition of Mn and Fe in the alloy.

Keywords

Al–Fe/Mg–Si alloyscrystal structureintermetallic alloys and compoundsmetal matrix compositesSiCp/Al composites
Type
Materials Applications
Information
Microscopy and Microanalysis , Volume 25 , Issue 4 , August 2019 , pp. 859 - 865
Copyright
Copyright © Microscopy Society of America 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Alphabetical indexes for experimental patterns, Sets 1–52, International Center for Diffraction Data (ICDD) (2008). Powder Diffraction File Number (PDF no. 01-071-4015).Google Scholar
Ansara, I, Dinsdale, AT & Rand, MH (1998). Ternary alloy systems. In COST 507: Thermochemical Database for Light Metal Alloys, vol. 2, pp. 319–355. Luxembourg: Office for Official Publications of the European Communities.Google Scholar
Buchanan, K, Ribis, J, Garnier, J & Colas, K (2016). Identification of monoclinic θ-phase dispersoids in a 6061 aluminium alloy. Phil Mag Lett 96, 121–131.Google Scholar
Cooper, MJ (1967). The crystal structure of the ternary alloy α(AlFeSi). Acta Cryst 23, 1106–1107.10.1107/S0365110X67004372Google Scholar
Cooper, MJ & Robinson, K (1966). The crystal structure of the ternary alloy α(AlMnSi). Acta Cryst 20, 614–617.Google Scholar
Donnadieu, P, Lapasset, G & Sanders, TH (1994). Manganese-induced ordering in the α-(Al–Mn–Fe–Si) approximant phase. Phil Mag Lett 70, 319–326.10.1080/09500839408240993Google Scholar
Eivani, AR, Ahmed, H, Zhou, J & Duszczyk, J (2009). Evolution of grain boundary phases during the homogenization of AA7020 aluminum alloy. Metall Mater Trans A 40, 717–728.Google Scholar
Eivani, AR, Ahmed, H, Zhou, J & Duszczyk, J (2010). Modeling the TDFD dissolution of Al–Fe–Mn–Si particles in an Al–4.5Zn–1Mg alloy. Philos Mag 90, 2865–2897.10.1080/14786431003662580Google Scholar
Eivani, AR, Ahmed, H, Zhou, J, Duszczyk, J & Kwakernaak, C (2011). Characterisation of different types of dispersoids present in homogenised Al–4.5Zn–1Mg alloy containing Zr, Cr and Mn. Mater Sci Technol 27, 1294–1298.10.1179/026708310X12635619988267Google Scholar
Jeniski, RA, Thanaboonsombut, B & Sanders, TH (1996). The effect of iron and manganese on the recrystallization behavior of hot rolled and solution-heat-treated aluminum alloy 6013. Metall Mater Trans A 27, 19–27.Google Scholar
Li, Y & Mohamed, FA (1997). An investigation of creep behavior in a SiC–2124 Al composite. Acta Mater 45, 4775–4785.10.1016/S1359-6454(97)00130-4Google Scholar
Lodgaard, L & Ryum, N (2000). Precipitation of dispersoids containing Mn and/or Cr in Al–Mg–Si alloys. Mater Sci Eng A 283, 144–152.10.1016/S0921-5093(00)00734-6Google Scholar
Mandal, D & Viswanathan, S (2013a). Effect of heat treatment on microstructure and interface of SiC particle reinforced 2124 Al matrix composite. Mater Charact 85, 73–81.Google Scholar
Mandal, D & Viswanathan, S (2013b). Effect of re-melting on particle distribution and interface formation in SiC reinforced 2124Al matrix composite. Mater Charact 86, 21–27.Google Scholar
Miracle, DB (2005). Metal matrix composites—from science to technological significance. Compos Sci Technol 65, 2526–2540.Google Scholar
Wang, SY, Tang, Q, Li, DJ, Zou, JX, Zeng, XQ & Ouyang, QB (2015). The hot workability of SiCp/2024 Al composite by stir casting. Mater Manuf Process 30, 624–630.10.1080/10426914.2014.952027Google Scholar
Wang, Z, Song, M, Sun, C & He, Y (2011). Effect of dispersoid size on the sliding wear behavior of Al–2014–10% SiC composites. Mater Sci Eng A 528, 1131–1137.10.1016/j.msea.2010.11.028Google Scholar
Wang, Z, Song, M, Sun, C, Xiao, D & He, Y (2010). Effect of extrusion and particle volume fraction on the mechanical properties of SiC reinforced Al–Cu alloy composites. Mater Sci Eng A 527, 6537–6542.Google Scholar
Weiland, A, Hultman, L, Wahlström, U, Persson, C & Johannesson, T (1998). Internal stress and microstructure of SiC reinforced aluminium alloy 2014. Acta Mater 46, 5271–5281.10.1016/S1359-6454(98)00212-2Google Scholar
Yoo, J, Shan, A, Moon, I & Maeng, S (1999). A study on composition and crystal structure of dispersoids in AlMgSi alloys. J Mater Sci 34, 2679–2683.Google Scholar
Zhang, J, Ouyang, QB, Guo, Q, Li, ZQ, Fan, GL & Su, YS (2016). 3D Microstructure-based finite element modeling of deformation and fracture of SiCp/Al composites. Compos Sci Technol 123, 1–9.10.1016/j.compscitech.2015.11.014Google Scholar