Role of nitrogen on the atomistic structure of the intergranular film in silicon nitride: A molecular dynamics study

Published online by Cambridge University Press:  01 December 2004

Xiaotao Su  and
Stephen H. Garofalini
Xiaotao Su
Affiliation:
Department of Ceramics and Materials Engineering, Rutgers University, Piscataway, New Jersey 08854
Stephen H. Garofalini
Affiliation:
Department of Ceramics and Materials Engineering, Rutgers University, Piscataway, New Jersey 08854
Get access

Abstract

Molecular dynamics simulations of intergranular films (IGFs) containing Si, O, N, and Ca in contact with three different types of surface terminations of Si3N4 were performed using a multi-body interatomic potential. IGFs with the same Ca concentration (12 mol% CaO) but different nitrogen concentrations [N/(N + O) = 0, 15, 30, and 50%] were studied. In all 12 IGFs, Ca ions did not compete with the first adsorbed layer of Si at the IGF/basal crystal interface, but did so at the IGF/prism crystal interface. The simulations show the epitaxial adsorption of Si, O, and N from the IGF onto the basal and prism crystal surfaces. While more adsorbed N was expected as nitrogen concentration increases, there was a significantly larger amount of N adsorbed to the basal surface than to the prism surface. It was found that Ca ions sit closer to the prism surface than the basal surface but move closer to the crystal at both surfaces with increasing nitrogen concentration, although the effect was more pronounced at the basal interface. With the increase of nitrogen concentration, the percentage of two-coordinated oxygen remained about the same, but there was a change in the type of defect oxygen present. In all the simulations, the central position of the first peak in the Si–O pair distribution fixation (PDF) ranges from 1.63 to 1.65 Å, and that of Si–N PDF ranges from 1.71 to 1.73 Å, both consistent with experimental findings. Furthermore, the first peak of both the Si–O and Si-N PDF shifts to larger values as the nitrogen concentration increases, indicating the elongation of the Si–O and Si–N bond in the IGF with the increase of nitrogen concentration. Elongation of both the Si–N and Si–O bonds could lead to weakening of the IGF as nitrogen concentration increases, although competing changes in bonding of the O complicate the effect of N addition on the strength of the IGF.

Keywords

Computer simulationGrain boundariesNanoscale
Type
Articles
Information
Journal of Materials Research , Volume 19 , Issue 12 , December 2004 , pp. 3679 - 3687
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Lange, F.F.: Fabrication and properties of dense polyphase silicon nitride. Am. Ceram. Soc. Bull. 62, 1368 (1983).Google Scholar
2Tsai, R.L. and Raj, R.: The role of grain boundary sliding in fracture of hot-pressed Si3N4 at high temperatures. J. Am. Ceram. Soc. 63, 513 (1980).CrossRefGoogle Scholar
3Raj, R.: Creep in polycrystalline aggregates by matter transport through a liquid phase. J. Geophys. Res. B 87, 4731 (1982).CrossRefGoogle Scholar
4Kleebe, H-J.: Structure and chemistry of interfaces in Si3N4 ceramics studied by transmission electron microscopy. J. Ceram. Soc. Jpn. 105, 453 (1997).CrossRefGoogle Scholar
5Bruley, J., Tanaka, I., Kleebe, H-J. and Rühle, M.: Chemistry of grain boundaries in calcia doped silicon nitride studied by spatially resolved electron energy-loss spectroscopy. Anal. Chimica Acta. 297, 97 (1994).CrossRefGoogle Scholar
6Gu, H., Pan, X., Cannon, R.M. and Rühle, M.: Dopant distribution in grain-boundary films in calcia-doped silicon nitride ceramics. J. Am. Ceram. Soc. 81, 3125 (1998).CrossRefGoogle Scholar
7Gu, H., Cannon, R.M. and Rühle, M.: Composition and chemical width of ultra-thin amorphous films at grain boundaries in silicon nitride. J. Mater. Res. 13, 376 (1998).Google Scholar
8Gu, H., Cannon, R.M., Seifert, H.J., Hoffmann, M.J. and Tanaka, I.: Solubility of Si3N4 in Liquid SiO2. J. Am. Ceram. Soc. 85, 25 (2002).CrossRefGoogle Scholar
9Ching, W-Y., Mo, S-D. and Chen, Y.: Calculation of XANES/ELNES spectra of all edges in Si3N4 and Si2N2O. J. Am. Ceram. Soc. 85, 11 (2002).CrossRefGoogle Scholar
10Yoshiya, M., Tatsumi, K., Tanaka, I. and Adachi, H.: Theoretical study on the chemistry of intergranular glassy film in Si3N4-SiO2 ceramics. J. Am. Ceram. Soc. 85, 109 (2002).CrossRefGoogle Scholar
11Painter, G.S., Becher, P.F. and Sun, E.Y.: Bond energetics at intergranular interfaces in alumina-doped silicon nitride. J. Am. Ceram. Soc. 85, 65 (2002).Google Scholar
12Pezzotti, G. and Painter, G.S.: Mechanisms of dopant induced changes in intergranular SiO2 viscosity in polycrystalline silicon nitride. J. Am. Ceram. Soc. 85, 91 (2002).CrossRefGoogle Scholar
13Garofalini, S.H. and Luo, W.: Molecular dynamics simulations of calcium silicate intergranular films between silicon nitride crystals. J. Am. Ceram. Soc. 86, 1741 (2003).CrossRefGoogle Scholar
14Su, X. and Garofalini, S.H.: Atomistic structure of calcium silicate intergranular films between prism and basal planes in silicon nitride: A molecular dynamics study. J. Mater. Res. 19, 752 (2004).Google Scholar
15Sjoberg, J., Helgesson, G. and Idrestedt, I.: Refinement of the structure of Si2N2O. Acta Crystallogr. C47, 2438 (1991).Google Scholar
16Berendsen, H., Postma, J., van Gunsteren, W., DiNola, A. and Haak, J.: Molecular dynamics with coupling to an external bath. J. Chem. Phys. 81, 3684 (1984).CrossRefGoogle Scholar
17Blonski, S. and Garofalini, S.H.: Molecular dynamics simulations of α-alumina and γ-alumina surfaces. Surf. Sci. 295, 263 (1993).Google Scholar
18Blonski, S. and Garofalini, S.H.: Atomistic structure of calcium silicate intergranular films in alumina studied by molecular dynamics simulations. J. Am. Ceram. Soc. 80, 1997 (1997).Google Scholar
19McBride, W. and Cockayne, D.J.H.: The structure of nanovolumes of amorphous materials. J. Non-Cryst. Solids 318, 233 (2003).Google Scholar