Ionization-induced effects in amorphous apatite at elevated temperatures
Published online by Cambridge University Press: 31 January 2011
Abstract
Electron-beam-induced effects in preamorphized Sr2Nd8(SiO4)6O2 were investigated in situ using transmission electron microscopy with 200-keV electrons at temperatures ranging from 380 to 780 K. Within the electron-irradiated area, epitaxial recrystallization was observed from the amorphous/crystalline interface toward the surface, with the rate of recrystallization increasing as temperature increased from 380 to 580 K. Structural contrast features (i.e., O deficient amorphous material), as well as recrystallization, were observed outside of the irradiation area at temperatures from 680 to 780 K. Ionization-induced processes and local nonstoichiometry induced by oxygen migration and desorption are possible mechanisms for the electron-beam- induced recrystallization and for the formation of the structural contrast features, respectively.
Keywords
- Type
- Articles
- Information
- Copyright
- Copyright © Materials Research Society 2008
References
REFERENCES
- 8
- Cited by