Elastic and structural properties of alkaline-calcium silica hydrogels

Published online by Cambridge University Press:  03 March 2011

John W. Phair*
Affiliation:
Office of Infrastructure R&D, Federal Highway Administration, McLean, Virginia 22101
Sergey N. Tkachev
Affiliation:
Hawaii Institute of Geophysics and Planetology, School of Ocean and Earth Sciences and Technology, University of Hawaii at Manoa, Honolulu, Hawaii 96822
Murli H. Manghnani
Affiliation:
Hawaii Institute of Geophysics and Planetology, School of Ocean and Earth Sciences and Technology, University of Hawaii at Manoa, Honolulu, Hawaii 96822
Richard A. Livingston
Affiliation:
Office of Infrastructure R&D, Federal Highway Administration, McLean, Virginia 22101
*
a) Address all correspondence to this author. e-mail: jwphair@yahoo.com
Get access

Abstract

Brillouin scattering has been used to study the elastic properties of alkaline-calcium silica hydrogels synthesized from the precipitation of sodium silicate solution with calcium hydroxide. To the best of our knowledge, this is the first determination of the bulk elastic moduli for this type of alkaline-calcium silica hydrogel, also referred to as the alkali-silica reaction (ASR) gel. The measured bulk moduli for the alkaline-calcium silica hydrogels were found to be between 4 and 8 GPa for the gel containing 0.08 M Ca(OH)2 and between 10 and 25 GPa for the gel containing 0.8 M Ca(OH)2, increasing with increasing pressure. Fourier transform infrared measurements were made to correlate the moduli to the silica speciation and network formation within the gels as a function of Ca(OH)2 content. Significantly, for the concentrations considered, both the interconnection of the silica species and the bulk modulus increased with increasing Ca(OH)2 content. On this basis, Brillouin scattering was confirmed to be a useful method for distinguishing between the bulk moduli of alkaline-calcium silica hydrogels in terms of chemical composition. The potential for further characterization of ASR gels as a function of composition and water content by this technique is highly promising.

Type
Articles
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Marfil, S.A. and Maiza, P.J.: Deteriorated pavements due to the alkali-silica reaction: A petrographic study of three cases in Argentina. Cem. Conc. Res. 31, 1017 (2001).CrossRefGoogle Scholar
2.Hobbs, D.W.: Expansion of concrete due to the alkali-silica reaction: An explanation. Mag. Conc. Res. 30, 15 (1978).CrossRefGoogle Scholar
3.Cong, X-D. and Kirkpatrick, R.J.: Silicon-29 MAS NMR spectroscopic investigation of alkali silica reaction product gels. Cem. Conc. Res. 23, 811 (1993).CrossRefGoogle Scholar
4.Bernard, O., Ulm, F-J. and Lemarchand, E.: A multiscale micromechanics-hydration model for the early-age elastic properties of cement-based materials. Cem. Conc. Res. 33, 1293 (2003).CrossRefGoogle Scholar
5.Ulm, F.J., Coussy, O., Kefei, L. and Larive, C.: Thermo-chemo-mechanics of ASR expansion in concrete structures. J. Eng. Mech. 233 (2000).CrossRefGoogle Scholar
6.Lemarchand, E., Dormieux, L. and Ulm, F-J.: Elements of micromechanics of ASR-induced swelling in concrete structures. J. of Conc. Sci. Eng. 4, 12 (2002).Google Scholar
7.Gaboriaud, F., Chaumont, D., Nonat, A., Hanquet, B. and Craeivich, A.: Study of the influence of alkaline ions (Li, Na and K) on the structure of the silicate entities in silico alkaline sol and on the formation of the silico-calco-alkaline gel, J. Sol-Gel Sci. Technol. 13, 353 (1998).CrossRefGoogle Scholar
8.Gaboriaud, F., Nonat, A., Chaumont, D., Craievich, A. and Hanquet, B.: 29Si NMR and small-angle x-ray scattering studies of the effect of alkaline ions (Li+, Na+, and K+) in silico-alkaline sols. J. Phys. Chem. B 103, 2091 (1999).Google Scholar
9.Struble, L. and Diamond, S.: Unstable swelling behaviour of alkali silica gels. Cem. Conc. Res. 11, 611 (1981).CrossRefGoogle Scholar
10.Knudsen, T. and Thaulow, N.: Quantitative microanalyses of alkali-silica gel in concrete. Cem. Conc. Res. 5, 443 (1975).CrossRefGoogle Scholar
11.Gaboriaud, F., Chaumont, D., Nonat, A. and Craievich, A.: Fractal structure of basic silica gels with low Ca content. J. Appl. Crystallogr. 33, 597 (2000).CrossRefGoogle Scholar
12.Mather, B.: Sulfate soundness, sulfate attack and expansive cement in concrete, in International Symposium on the Durability of Concrete, Preliminary Report Part II (Academia, Prague, 1969), pp. C-209C-220.Google Scholar
13.Beaudoin, J.J. and Tamtsia, B.T.: Creep of hardened cement paste—The role of interfacial phenomena. Interface Sci. 12, 351 (2004).CrossRefGoogle Scholar
14.Jayaraman, A.: Diamond anvil cell and high-pressure physical investigations. Rev. Mod. Phys. 55, 65 (1983).CrossRefGoogle Scholar
15.Whitfield, C.H., Brody, E.M. and Bassett, W.A.: Elastic moduli of NaCl by Brillouin scattering at high pressure in a diamond anvil cell. Rev. Sci. Instrum. 47, 942 (1976).CrossRefGoogle Scholar
16.Piermarini, G.J. and Block, S.: Ultrahigh pressure diamond-anvil cell and several semiconductor phase transition pressures in relation to the fixed point pressure scale. Rev. Sci. Instrum. 46, 973 (1975).CrossRefGoogle Scholar
17.Sandercock, J.R.: Light scattering solids, III: Recent results, in Topics of Applied Physics, Vol. 51, edited by Cardona, M. and Guntherodt, G. (Springer-Verlag, Berlin, Germany, 1982), p. 173.Google Scholar
18.Tkachev, S.N. and Bass, J.D.: Brillouin scattering study of pentane at high pressure. J. Chem. Phys. 104, 10059 (1996).CrossRefGoogle Scholar
19.Gaboriaud, F., Nonat, A., Chaumont, D. and Craievich, A.: Aggregation processes and formation of silico-calco-alkaline gels under high ionic strength. J. Colloid Interface Sci. 253, 140 (2002).Google Scholar
20.Marinangeli, A., Morelli, M.A., Simoni, R. and Bertoluzza, A.: A Raman and infrared study of aqueous solutions of sodium silicates as a function of pH. Canad. J. Spectrosc. 23, 173 (1978).Google Scholar
21.Almeida, R.M. and Pantano, C.G.: Structural investigation of silica gel films by infrared spectroscopy. J. App. Phys. 68, 4225 (1990).CrossRefGoogle Scholar
22.Viart, N., Niznansky, D. and Rehspringer, J.L.: Structural evolution of a formamide modified sol—Spectroscopic study. J. Sol-Gel Sci. Technol. 8, 183 (1997).CrossRefGoogle Scholar
23.Chmel, A., Mazurina, E.K. and Shashkin, V.S.: Vibrational spectra and deffect structure of silica prepared by non-organic sol-gel process. J. Non-Cryst. Solids 122, 285 (1990).CrossRefGoogle Scholar
24.Bass, J.L. and Turner, G.L.: Anion distributions in sodium silicate solutions. Characterisation by 29Si NMR and infrared spectroscopies, and vapour phase osmometry. J. Phys. Chem. B 101, 10638 (1997).CrossRefGoogle Scholar
25.Ortego, J.D. and Barroeta, Y.: Leaching effects on silicate polymerisation. An FTIR and 29Si NMR study of lead and zinc in portland cement. Environ. Sci. Technol. 25, 1171 (1991).CrossRefGoogle Scholar
26.Hughes, T.L., Methven, C.M., Jones, T.G.J., Pelham, S.E. and Franklin, P.: The use of Fourier transform infrared spectroscopy to characterize cement powders, cement hydration and the role of additives. Spec. Pub. R. Soc. Chem. 159, 99 (1994).Google Scholar
27.Gaboriaud, F., Nonat, A., Chaumont, D. and Craievich, A.: Aggregation and gel formation in basic silico-calco-alkaline solutions studied: A SAXS, SANS, and ELS study. J. Phys. Chem. B 103, 5775 (1999).Google Scholar