Pulsed-Laser-Deposited AlN Films for High-Temperature SiC MIS Devices

  • R. D. Vispute (a1), A. Patel (a1), K. Baynes (a1), B. Ming (a1), R. P. Sharma (a1), T. Venkatesan (a1), C. J. Scozzie (a2), A. Lelis (a2), T. Zheleva (a2) and K. A. Jones (a2)...

Abstract

We report on the fabrication of device-quality AlN heterostructures grown on SiC for high-temperature electronic devices. The AlN films were grown by pulsed laser deposition (PLD) at substrate temperatures ranging from 25 °C (room temperature) to 1000 °C. The as-grown films were investigated using x-ray diffraction, Rutherford backscattering specttroscopy, ion channeling, atomic force microscopy, and transmission electron microscopy. The AlN films grown above 700 °C were highly c-axis oriented with rocking curve FWHM of 5 to 6 arc-min. The ion channeling minimum yields near the surface region for the AlN films were ∼2 to 4%, indicating their high degree of crystallinity. TEM studies indicated that AlN films were epitaxial and single crystalline in nature with a large number of stacking faults as a results of lattice mismatch and growth induced defects. The surface roughness for the films was about 0.5 nm, which is close to the unit cell height of the AlN. Epitaxial TiN ohmic contacts were also developed on SiC, GaN, and AlN by in-situ PLD. Epitaxial TiN/AlN/SiC MIS capacitors with gate areas of 4 * 10-4 cm2 were fabricated, and high-temperature current-voltage (I-V) characteristics were studied up to 450 °C. We have measured leakage current densities of low 10-8 A/cm2 at room temperature, and have mid 10-3 A/cm2 at 450°C under a field of 2 MV/cm.

Copyright

References

Hide All
[1] Nakamura, S. and Fasol, G., The Blue Laser Diode (Springer, Berlin, 1997).
[2] Strite, S. and Morkoc, H., J. Vac. Sci. Technol. B 10, 1237, (1992).
[3] Zetterling, C. M., Wongchotigul, K., Spencer, M. G., Harris, C. I., Wong, S. S., and Ostling, M., Mater. Res. Soc. Symp. Proc. 423, 667, (1996).
[4] Zetterling, C. M., Ostling, M., Wongchotigul, K., Spencer, M. G., Tang, X., Harris, C. I., Nordell, N., and Wong, S. S., J. Appl. Phys. 82, 2990, (1997).
[5] Ouisse, T., Schenk, H. P. D., Karmann, S., and Kaiser, U., in Proceedings of the International Conference on Silicon Carbide III-Nitrides and Related Materials- 1997. Materials Science Forum, edited by Pensl, G., Morkoc, H., Monemar, B., and Janzen, E.Trans Tech, Uetikon, Zuerich, Switzerland. 264–268, 1389, (1998).
[6] Vispute, R. D., Choopun, S., Enck, R., Patel, A., Talyansky, V., Sharma, R. P., Venkatesan, T., Sarney, W.L., Salamanca-Riba, L., Andronescu, S.N., and Iliadis, A. A., Jones, K. A., J. Elect. Materials, 28 275 (1999).
[7] Scozzie, C. J., Lelis, A. J., McLean, B. F., Vispute, R. D., Patel, A., Sharma, R. P., and Venkatesan, T..“High Temperature Characterization of Pulsed-Laser-Deposited AlN on 6H-SiC from 25 to 450°C.” submitted to ISCRM 99 Conference (1999).
[8] Scozzie, C. J., Lelis, A. J., McLean, B. F., Vispute, R. D., Patel, A., Sharma, R. P., and Venkatesan, T., J. Appl. Phys. 86, 4052, (1999).

Pulsed-Laser-Deposited AlN Films for High-Temperature SiC MIS Devices

  • R. D. Vispute (a1), A. Patel (a1), K. Baynes (a1), B. Ming (a1), R. P. Sharma (a1), T. Venkatesan (a1), C. J. Scozzie (a2), A. Lelis (a2), T. Zheleva (a2) and K. A. Jones (a2)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed