To save content items to your account,
please confirm that you agree to abide by our usage policies.
If this is the first time you use this feature, you will be asked to authorise Cambridge Core to connect with your account.
Find out more about saving content to .
To save content items to your Kindle, first ensure email@example.com
is added to your Approved Personal Document E-mail List under your Personal Document Settings
on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part
of your Kindle email address below.
Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations.
‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi.
‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Nd-bearing zirconolite was leached at 90°C for 157 days in 0.001M citric acid under single-pass-flow-through conditions (modified MCC-4 protocol). Three different flow rates were used, ranging in an order of magnitude from 10 mL per day to 100 mL per day, to determine the effect of the rate of leachant replenishment on the durability of the zirconolite. Results of previous studies on the role of complexing agents on the leaching behaviour of single-phase zirconolite have been included in the discussion.
The pH of the citric acid solution was adjusted to 5 using KOH, mimicking that of the water in the parallel tests, to avoid the influence of pH on chemical durability of the zirconolite.
Simulated groundwater containing 0.001M citric acid at 90°C led to congruency in elemental releases and a diminution of release rate with time of about an order of magnitude, reaching virtual constancy after about 50 to 60 days to a level of about 10−5 g m−2 day−1. The most significant finding was that the elemental release rates of Nd, Ti and Zr (and Ca and Al where detected) were similar for all flow rates. Clearly, varying flow rate by up to an order of magnitude had no effect on elemental releases i.e. there is no solubility limit control on releases at 0.001M citric acid concentration.
An important finding of previous studies using identical leaching protocols with 0.001M citric acid, and inferred in our latest investigations reported here, was that there is no secondary layer development at the surface of the zirconolite to affect leach rates. In contrast, parallel tests carried out in deionised water instead of citric acid showed that hydroxides form in situ on the zirconolite surface, effectively forming hydrolysed zirconolite. This controls further dissolution of the zirconolite matrix due to the solubility limit being reached with respect to the hydrolysed phases rather than with zirconolite. Complexation by citrate ions prevents such control by hydrolysed species on zirconolite solubility.
Even under the more aggressive conditions imposed in these studies (0.001M citric acid), and regardless of flow rate of the leachant, elemental releases from zirconolite are very low for a candidate wasteform and demonstrate its attributes as a ceramic-based wasteform for the containment of actinides.