Thin films of Transition Metal Oxides (TMOs) were deposited by reactive sputtering of pure transition metal targets in Argon-Oxygen gas mixture at elevated substrate temperature for efficient energy consumption. The atomic composition and thickness of the TMO films was determined by Rutherford Backscattering Spectroscopy (RBS). Optical transmittance and reflectance spectrum of the films on quartz substrate was measured with thin film measuring system at room temperature and slightly elevated temperature. The surface morphology and structure of the TMO films was determined with Atomic Force Microscope (AFM).

The oxidation and diffusion of Molybdenum layer sputter-deposited on 2μm CVD diamond grown on silicon substrate has been studied. The Mo layer was protected by refractory metal silicide barrier layer. The samples were annealed in air ambient at 500°C over 30 hours. The oxidation of the samples was monitored with Rutherford Backscattering Spectroscopy (RBS). The effect of reactive sputtering of refractory silicide target in argon-nitrogen gas mixture (5% nitrogen by flow rate) on the barrier characteristics was investigated. The sheet resistivity of the barrier layer on SiC substrates as a function of annealing time in air at 500°C is reported. The surface structure and morphology of the refractory silicide films was determined with X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM).

The interface passivation process based on post-oxidation, high temperature anneals in nitric oxide (NO) is well established for SiO2 on (0001) 4H-SiC. The NO process results in an order of magnitude or more reduction in the interface state density near the 4H conduction band edge. However, trap densities are still high compared to those measured for Si / SiO2 passivated with post-oxidation anneals in hydrogen. Herein, we report the results of studies for 4H-SiC / SiO2 undertaken to determine the effects of additional passivation anneals in hydrogen when these anneals are carried out following a standard NO anneal. After NO passivation and Pt deposition to form gate contacts, post-metallization anneals in hydrogen further reduced the trap density from approximately 1.5 × 1012 cm−2eV−1 to about 6 × 1011 cm−2eV−1 at a trap energy of 0.1 eV below the band edge for dry thermal oxides on both (0001) and (11–20) 4H-SiC.

As the group III nitride semiconductor technology matures, an increasing number of devices are being fabricated with high Al fraction AlGaN. In this study, ohmic behavior is achieved using Ti/Al/Pt/Au contacts to n-Al0.4Ga0.6N, which is the highest Al fraction for which ohmic contact formation has been reported. The effect of contact composition, pretreatment, and annealing conditions is studied by 30 s isochronal annealing experiments between 500°C and 1000°C. A specific contact resistance ρC of (5±3) × 10−5 ωcm2 is obtained using Ti(26 nm)/Al(74 nm)/Pt(50 nm)/Au(50 nm) contacts to n-Al0.4Ga0.6N annealed in N2 at 800°C; however, this value is shown to be artificially high because the metal sheet resistance RM is 4 ω/⊏ causing an artifact in the data analysis. All contacts with ρC < 10−3 ωcm2 exhibit a local minimum in ρC after annealing at 800°C. The observed increase in ρC upon annealing at 850°C and 900°C, however, is not an artifact originating from a change in RM. The top Au layer is found to play an active role in forming ohmic contacts with low ρC, since omitting the Au layer yields an increase in ρC of two orders of magnitude after annealing at 800°C. Furthermore, leaving out the Au layer requires an annealing temperature of 700°C to result in linear I-V curves for currents up to 100 µA, as opposed to 500°C when the Au layer is present. The role of Au is further studied in Ti(26 nm)/Al(74 nm)/Ni(50 nm)/Au(50 nm) contacts, where Rutherford backscattering spectroscopy reveals Ga in the metal layer and/or Au buried deeper than the original semiconductor-metal interface, and x-ray diffraction indicates the formation of new phases to happen concurrently with a decrease in ρC of three orders of magnitude.

The influence of composition on Al-Ti ohmic contacts to 4H p-SiC was studied. When NA was 7 x 1018 cm−3, contacts with 70 wt.% or more Al became ohmic when annealed at 1000°C for 2 min, whereas when there was 60 wt.% or less Al, the contacts did not become ohmic even when annealed under more severe conditions (longer times and/or higher temperatures). Spiking of the contact metallization always accompanied ohmic behavior and could be correlated with Al-Ti compositions that contain both an Al-rich liquid and solid TiAl3 at 1000°C prior to reaction with SiC or evaporative loss of Al. For the 70 wt.× contacts, a specific contact resistance of 1.5 × 10−4 Ω cm2 was measured along with spiking of the metallization into the SiC with a room-mean-square interfacial roughness of 150 Å and a maximum spiking depth of 1200 Å. Although still a concern, this spiking was less severe than observed for the 90 wt.× composition. A conductive CrB2 cap layer was next demonstrated to retard evaporation of Al during annealing of the Al-Ti contacts with 70 wt.× Al. The cap allowed use of thinner contact layers, reducing the depth of spiking and improving the surface morphology and edge definition of the ohmic contacts, with a one order of magnitude penalty in the specific contact resistance.

This paper presents a review of new results obtained by a combination of first-principles theory, Z-contrast imaging, and electron-energy-loss spectroscopy in the context of a broader experimental/theoretical program to understand and control the atomic-scale structure of SiCSiO2 interfaces. The ultimate purpose is to achieve low interface trap densities for device applications. Results are given for global bonding arrangements in comparison with those of the Si-SiO2 interface, the mechanism of the oxidation process, the nature of possible interface defects and their passivation by N and H, and the formation and dissolution of C clusters in SiO2 during oxidation and reoxidation.

Edge termination is an important aspect in the design of high power p-n junction devices. In this paper, we compare the breakdown characteristics of 4H-SiC p+-n diodes with oxide passivation and with edge termination using either low or high energy ion implantations. N- and p-type epilayers of 4H-SiC were grown by chemical vapor deposition on n+ 4H-SiC wafers. Circular mesa structures of different diameters were patterned and isolated by reactive ion etching. Four types of samples were fabricated. The first group was not implanted or passivated and was left for control. The second type consisted of oxide-passivated diode structures while the third and fourth types were ion implanted with 30 keV Ar+ and 2.2 MeV He+ ions, respectively. The time dependent breakdown characteristics were determined using a fast voltage ramp technique. The reverse bias breakdown voltages and leakage currents of these diodes were different for the different types of the edge termination. Diodes terminated using 2.2 MeV ion implantation yielded the best breakdown characteristics. A majority of the diodes exhibited abrupt breakdown.

We have characterized the high electric field breakdown process of several epitaxial 4H-SiC p-n structures with oxide passivation. The breakdown voltage was found to be dependent on the size of the diode structures as well as their proximity to any structural defects. The time dependence of the breakdown process was also measured to determine the characteristics of the breakdown mechanism. This time dependence measurement provides an indication of the quality of the diode structures. Both soft and abrupt breakdown mechanisms were observed showing the influence of defects on the high field behavior of the diode structures. Measurements done with and without the use of Fluorinert fluid did not show any difference in the breakdown voltage indicating that surface flashover breakdown mechanism did not play a major role in the avalanche breakdown process.

Results are reported for ohmic contacts formed on n-type 4H and 6H-SiC using nichrome (80/20 weight percent Ni/Cr). In comparison to contacts formed on 6H-SiC using pure Ni, the electrical characteristics of these NiCr contacts are similar (∼ 1E-5 Ω-cm2 for moderately doped material), and composite Au/NiCr contacts exhibit good stability during long-term anneals (∼ 2500 hr) at 300 C without the requirement of a diffusion barrier layer between the ohmic contact layer and the Au cap layer. The use of NiCr also results in success rates near 100% for direct wire bonding to the Au cap layers.

The current vs voltage characteristics of 4H-SiC MOS capacitors under deep depletion are obtained by a fast ramp response technique so as to obtain the maximum field that can be applied to the MOS structure without the failure of either the semiconductor or the oxide layer. The experiments on n-type 4H SiC wafers having a 5 μm thick epilayer of 1015 – 1016 cm−3 doping concentration and an oxide layer 1200Å – 1500Å thick, indicate the significant influence of the oxide quality and defects in the semiconductor on the nature of the current response during accumulation and deep depletion measurements. The effect of the conductivity of the oxide layer is reflected clearly in the current response, even though classical C-V measurements do not indicate any abnormality. Apart from obtaining the maximum breakdown fields of the semiconductor and the oxide, the fast-ramp response technique provides useful information about the generation processes associated with defects in the MOS structure.