Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Thin and Smooth Cu Seed Layer Deposition using the Reduction of Low Temperature Deposited Cu2O

  • Hoon Kim, Yasuhiko Kojima, Hiroshi Sato, Naoki Yoshii, Shigetoshi Hosaka, Yukihiro Shimogaki
  • Journal:
    MRS Online Proceedings Library Archive / Volume 914 / 2006
    Published online by Cambridge University Press:
    01 February 2011, 0914-F05-11
    Print publication:
    2006

  • Thin and continuous CVD Cu seed layer was successfully deposited on Ru under-layer by Cu oxide deposition and reduction method at 100°C with novel chemistry. Cu oxide was formed with Cu(hface)TMVS and H2O2 at 100°C, and this film was reduced with formic acid at 100°C. Deposited Cu oxide films were Cu2O that was confirmed by XRD and XPS. The morphology of oxide films showed smooth and continuous on Ru and Ta substrate. The reduced Cu film on Ru maintained good surface morphology, and no impurity was detected not only in the Cu film but also the interface between Cu and Ru. However, that on Ta had poor morphology by agglomeration of Cu film during reduction due to poor Cu wettability on oxidized Ta that was oxidized during oxide deposition. The readiness of reduction is very important merit of using Ru under-layer for this oxide deposition and reduction process. The oxide deposition and reduction method on Ru under-layer can be a promising candidate for thin and continuous seed layer deposition method.