The growth of high-quality indium (In)-rich InXGa1−XN alloys is technologically important for applications to attain highly efficient green light-emitting diodes and solar cells. However, phase separation and composition modulation in In-rich InXGa1−XN alloys are inevitable phenomena that degrade the crystal quality of In-rich InXGa1−XN layers. Composition modulations were observed in the In-rich InXGa1−XN layers with various In compositions. The In composition modulation in the InXGa1−XN alloys formed in samples with In compositions exceeding 47%. The misfit strain between the InGaN layer and the GaN buffer retarded the composition modulation, which resulted in the formation of modulated regions 100 nm above the In0.67Ga0.33N/GaN interface. The composition modulations were formed on the specific crystallographic planes of both the {0001} and {0114} planes of InGaN.

We demonstrated the growth of indium nitride (InN) nanowires on Si(111) substrates by metalorganic chemical vapor deposition without the use of any intermediate GaN or AlN buffer layer. The InN nanowires were grown by forming the Au + In droplets and In droplets on the Au- and In-coated Si substrate. The growth conditions such as chamber pressure, chamber temperature, reaction gas flow rate, and carrier gas flow rate were optimized to yield nanowires free from contamination. Depending on the growth parameters different growth regimes for the InN nanowires were identified. The strength of self-catalytic route has been highlighted. The morphology and microstructures of samples were characterized by x-ray diffraction and scanning electron microscopy (SEM). The transmission electron microscopy and SEM investigations showed that the InN nanowires are single crystals with diameters ranging from 40 to 400 nm, and lengths up to 3 µm. Photoluminescence spectra of the InN nanowires showed a strong broad emission peak at 0.77 eV.