A nanoparticle catalyst of PtRuAu/C was synthesized by including an Au precursor in the radiolytic process for preparing a PtRu/C catalyst. Their methanol oxidation activity and electrochemical durability were measured by linear sweep voltammetry before and after potential cycling treatment. PtRuAu/C had a significantly higher durability than PtRu/C while maintaining a comparable high activity. The morphology and substructure of the nanoparticles were investigated by energy-dispersive x-ray spectroscopy, x-ray diffraction, and x-ray absorption fine structure spectroscopy. Metallic nanoparticles with diameters of about 2 nm were obtained; they probably had Pt-core/PtRu-shell structures. Transmission electron microscopy observations after potential cycling revealed that 2-nm-diameter nanoparticles containing Au did not coarsen, whereas nanoparticles without Au coarsened significantly to 3.7 nm. Some crystal defaults were observed in the coarsened particles, implying that the coarsening was caused by Ostwald ripening. The Au addition to catalyst particles consisting of PtRu inhibits coarsening and consequently improves the electrochemical durability.

Nanoparticle catalyst of PtRuAu/C for direct methanol fuel cell anodes was synthesized by a radiolytic process. Its methanol oxidation activity and the electrochemical durability were evaluated by using the linear sweep voltammetry and the cyclic voltammety. The Au addition significantly improved the durability in comparison with PtRu/C catalyst without losing its high activity. The atomic structure was characterized with techniques of the transmission electron microscopy, the X-ray diffraction, the X-ray fluorescence spectroscopy and the X-ray absorption fine structure. These results implied that the arrangement of Pt and Ru atoms in the PtRuAu/C has no significant difference from that without Au, possessing a structure of Pt rich core and PtRu alloy shell. We concluded that the improvement in durability could originate from these PtRu nanoparticles decorated with Au, but not from particles with high Au contents.