Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Yttria-stabilized zirconia crystallization in Al2O3/YSZ multilayers

  • Nihan Kemik, Sergey V. Ushakov, Meng Gu, Nicole Schichtel, Carsten Korte, Nigel D. Browning, Yayoi Takamura, Alexandra Navrotsky
  • Journal:
    Journal of Materials Research / Volume 27 / Issue 6 / 28 March 2012
    Published online by Cambridge University Press:
    25 January 2012, pp. 939-943
    Print publication:
    28 March 2012

  • Yttria-stabilized zirconia (YSZ)/Al2O3 multilayers deposited on Pt foil were studied by differential scanning calorimetry. Observed thermal effects were interpreted using additional evidence from x-ray diffraction and transmission electron microscopy. The crystallization temperature of YSZ increases from 344 to 404 °C as the layer thickness decreases from 15 to 4 nm. The enthalpy of crystallization becomes more exothermic with decreasing thickness, and it was measured to be −26 kJ/mol YSZ for 4-nm-thick layers and −12 kJ/mol for 15-nm-thick layers. The latter value is consistent with the reported crystallization enthalpy for YSZ powder of the same composition prepared by precipitation from aqueous solution. The more exothermic crystallization enthalpies for thinner films are indicative of a decrease in their degree of crystallinity. The 2–6-nm-thick Al2O3 layers remain amorphous when heated to 1000 °C. The described methodology enables thermal analysis of oxide thin films using commercial instruments.