The rehydration properties and behavior of interlayer cations of Ca-, Mg-, Na-, and K-saturated homoionic saponite and vermiculite heated at various temperatures were examined and their rehydration mechanisms elucidated. The most notable features of saponite were (1) except for the Mg-saturated specimen, all saponite samples rehydrated until the crystal structure was destroyed by heating; (2) the rehydration rate in air after heating decreased in the order: K+ > Na+ > Ca2+ > Mg2+; (3) the interlayer cations apparently migrated into hexagonal holes of the SiO4 network on thermal dehydration; and (4) the b-parameter expanded on thermal dehydration. The rehydration properties and behavior of interlayer cations of vermiculite were: (1) except for the K-saturated specimen, all vermiculite samples rehydrated until the crystal structure was destroyed by heating; (2) the rehydration rate in air after heating decreased in the order: Mg2+ > Ca2+ > Na+ > K+; (3) the interlayer cations apparently did not migrate into the hexagonal holes, but remained at the center of the interlayer space, even after thermal dehydration; and (4) except for the K-saturated specimen, the 6-parameters of the samples contracted on thermal dehydration. The different rehydration properties of saponite and vermiculite were apparently due to the behavior of the interlayer cations during thermal dehydration. For rehydration to occur, the interlayer cations of saponite had to migrate out of the hexagonal holes. Consequently, saponite saturated with a large cation rehydrated rapidly, whereas saponite saturated with a small cation rehydrated slowly. On the other hand, the interlayer cations of vermiculite remained in the interlayer space; therefore, the rehydration properties of vermiculite were strongly affected by the hydration energies of the interlayer cations. Furthermore, electron diffraction patterns suggested that the saponite and vermiculite consisted of random stacking and ordered stacking of adjacent 2:1 layers, respectively. The nature of the stacking of the minerals seemed to be the most important factor controlling the behavior of interlayer cations in the thermal dehydration process.

Two distinct zonal sequences of clay minerals (H- and L-type) were found around silicified rocks in the Makurazaki volcanic area, Kagoshima Prefecture, Japan. The clay mineral sequences from the inner to the outer parts of the alteration aureoles are: 1. H-type, pyrophyllite → dickite → 2M2 mica → sudoite → tosudite; and 2. L-type, kaolinite → rectorite → smectite. The structural formula for the sudoite is: (Al1.04Mg1.28Fe3+0.20Ti0.03Li0.01K0.02Na0.01(OH)6Al2.00(Si3.54Al0.46)O10(OH)2. It is characterized by relatively large amounts of Mg and very small amounts of Li. The polytype is identified as IIb. The chemical analysis of tosudite shows that the sample is composed of an interstratification of sudoite-like and beidellite-like layers. The structural formula for rectorite is: (K0.45Na0.19Ca0.01Mg0.01)(Al1.81Fe3+0.04Mg0.13Ti0.03)(Si3.41Al0.59)O10(OH)2, suggesting that the nonexpandable and expandable layers have K-mica-like and beidellite-like compositions, respectively. These clay minerals in the H- and L-type alteration aureoles were formed under relatively high- and low-temperature conditions, respectively, with pH value and K- and Mg-activities increasing as the fluids ascended through the wall rocks.

The rehydration properties of Ca-, Mg-, Na-, and K-saturated homoionic beidellites after heating at various temperatures were compared with those of montmorillonites. The behavior of interlayer Na+ during dehydration and rehydration was also investigated by means of one-dimensional Fourier analysis. The K- and Mg-saturated specimens exhibited fast and slow rehydration rates, respectively, during exposure to air of 50% RH after heating at 800°C. These homoionic specimens showed strong rehydration properties on saturation with deionized water after heating <900°C for 1 hr. On the basis of Fourier analysis, the interlayer cations appeared to have migrated into the hexagonal holes of SiO4 network on thermal dehydration, and the migrated cations returned to the interlayer space on rehydration. This behavior of the interlayer cations appears to have been strongly dependent on value of the octahedral negative charge and on the sizes of interlayer cations. The small octahedral negative charge of beidellite produced a weaker attractive electrostatic force between the octahedral sheets and the migrated interlayer cations. Therefore, the migrated interlayer cations in beidellite were easily extracted from the hexagonal holes, and rehydration was rapid. The small cation migrated easily into hexagonal holes and was fixed to the holes. On the contrary, large cations were probably difficult to fix and were easily extracted from the hexagonal holes. Consequently, the rehydration rate of K-saturated beidellite was fast, and that of Mg-saturated beidellite was slow.

Experimental alteration of obsidian with HCl solution was performed to elucidate dissolution mechanism and formation process of clay minerals in acid solution. Reactions were carried out using 0.1, 0.5, and 4.0 g of obsidian to 100 ml of 0.01 N HCl solution at 150° and 200°C for 1 to 60 days. The reaction products were examined by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive X-ray analysis. The surface composition of obsidian before and after alteration was investigated by X-ray photoelectron spectroscopy (XPS). TEM showed that boehmite precipitated at early stage and spherical kaolinite appeared subsequently by 200°C reactions. However, spherical halloysite occurred predominantly with small amounts of allophane, boehmite, and kaolinite by 150°C reaction in which formation process of the halloysite from allophane passing through an intermediate phase of small size rounded aggregate that consists of fine particles of allophane was observed. A boehmite exhibiting hexagonal platy habit with higher degree of crystallinity was formed by 200°C reaction as a stable phase in solution containing lower Si concentration at which the solution composition coincides with the stability field of boehmite on activity diagram for the system Na2O-Al2O3-SiO2-H2O. The fibrous boehmite having lower crystallinity appeared with increasing Si concentration, considered as a metastable phase in the stability field of kaolinite. XPS indicated that dissolution of obsidian in acid solution proceeded initially by cation exchange between Na ions and hydronium ions in solution and subsequently by preferential release of Al ions relative to Si from the Na depleted surface.

Formation processes of weathering products of pumice collected from a rhyolitic pyroclastic flow deposit were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive X-ray analysis (EDX). SEM clearly showed the presence of some weathering products adhering to the surface of pumice. XRD showed that the products were composed mainly of noncrystalline materials with a relatively small amount of halloysite (10 Å). TEM and EDX revealed texture transformation sequences from the earliest weathering product to a final product of halloysite as follows: 1) precipitation of very thin flaky or film-like noncrystalline Al-hydroxide; 2) transformation into irregularly aggregated Al-Fe-Si-rich fibrous material; 3) morphological changes to rounded aggregates; 4) development of halloysite-like curled domains with successive decrease in Fe content; and 5) further development of curled domains in rounded aggregates. These materials must be metastable phases at early reaction stages with kinetics limiting formation of the stable equilibrium phase of kaolinite.

Experimental alteration of obsidian was performed in 0.001 to 0.5 N NaOH and KOH solutions at 150 and 200 °C for 1 to 30 d. The products were examined by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX). Changes in chemical composition and pH value of solutions during the reactions were also measured. As the pH of reacting solutions was increased, smectite, phillipsite and rhodesite crystallized progressively in NaOH solutions, while smectite, merlinoite and sanidine grew successively in KOH solutions. In addition, a small amount of less-soluble, poorly ordered boehmite was present as products of all the experiments. Smectite mainly appeared at slightly high pH, Si/Al and Na/K conditions, whereas rhodesite should be produced in extremely high pH, Na/K and Si/Al conditions. Sanidine was also formed in conditions of very high pH and Si/Al and very low Na/K. In intermediate conditions of pH and Si/Al, crystallization of phillipsite was stimulated in solutions of Na/K > 10, while formation of merlinoite was favored in conditions of Na/K < 1.

Weathering products formed on the surface of K-feldspar in Yakushima Island, Japan were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX) and X-ray photoelectron spectroscopy (XPS). XRD confirmed that the weathering products were composed mainly of gibbsite and halloysite. SEM, TEM and EDX clearly showed formation of amorphous aluminum hydroxide exhibiting 2 distinct habits: 1) curled fibrous or circular forms less than 0.02 μm in diameter; and 2) a spherical habit less than 1.0 μm in diameter. The fibrous aluminum hydroxide exhibited curled fibrous forms or circular forms less than 0.02 μm in diameter and gave a diffuse electron diffraction halo. EDX indicated that the material consisted mainly of Al and very small amounts of Si and Fe. The spherical aluminum hydroxide also gave similar EDX and electron diffraction characteristics to the fibrous material. These fibrous and spherical aluminum hydroxides must be formed as a metastable phase in the earliest weathering stages, and transformed into a stable phase of gibbsite and halloysite as the reaction proceeded.

The rehydration and rehydroxylation properties of homoionic rectorites (saturated with Ca2+, Mg2+, Na+, or K+) were further investigated. The rehydration properties of the rectorite were characterized as follows: (1) basal spacings of rehydrated materials after heating above 500°C changed to 22.5 Å for H2O-complexes, 26.85 Å for ethylene glycol-complexes, and 27.65 Å for glycerol-complexes; (2) rehydrated Ca- and Mg-materials exhibited single layer hydrates at <50% RH, and rehydrated K-material showed double layer hydrates at 80% RH; (3) IR absorption spectra due to rehydrated H2O and OH exhibited the same or very close absorption intensities and frequencies to each other; (4) DTA-TGA curves of rehydrated materials indicated that the amount of rehydrated H2O approached about 4.2 wt. %, and about one-half of OH was rehydroxylated after heating at 800°C; and (5) interlayer cations of expandable layer components became non-exchangeable after heating above 500°C. These results suggest the following rehydration mechanism of rectorite: the interlayer cations migrate into the hexagonal holes of the SiO4 network by thermal dehydration. The cations migrated below 400°C easily return to the interlayer space and their original hydrated configurations have been recovered completely on rehydration. However, those migrated above 500°C are fixed to the hexagonal holes but water molecules are regained in the interlayer space. Consequently, electrostatic effects of interlayer cations on formation of water molecule layers are considerably reduced.

Experimental alteration of volcanic glass has been carried out in distilled water at 200°C and 150°C. The formation and transformation processes of alteration products have been examined by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray powder diffraction (XRD), infrared absorption analysis, and X-ray photoelectron spectroscopy. SEM and TEM clearly show that amorphous aluminum-silicate coatings with allophane particles precipitate on the surface of volcanic glass during the earliest alteration stage. Noncrystalline flaky and/or fibrous materials are formed from the allophane aggregates and from the amorphous coatings as new reaction products. The flaky and/or fibrous materials curl inward and transform into 100–500 nm circular smectite. The Al/Si atomic ratio of 1.09 for allophane decreases progressively to 0.65 for smectite through 0.86 for noncrystalline transitional material. The smectite has d(06) spacing of 1.497 Å and consists mainly of Si, Al, and small amounts of Fe, Ca, and Na.

Experimental alteration of albite in deionized-distilled water at 150° to 225°C for various times up to 30 days was performed to elucidate formation processes for alteration products of albite in aqueous solution. The alteration products were examined by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX). The surface compositions of albite before and after alteration were investigated by X-ray photoelectron spectroscopy (XPS). TEM clearly showed that an amorphous leached layer was produced on the albite surface at the earliest alteration stage together with small amounts of allophane. The leached layer increased successively in thickness and tended to be detached from the albite surface as alteration proceeded. Noncrystalline fibers less than 0.5 µm in length appeared within the leached layer matrix and transformed into thin flaky smectite and small amounts of K-mica. The leached layer gave electron diffraction patterns with a diffuse halo, whereas the flaky smectite displayed rings at 4.51, 2.61, and 1.54 Å. EDX confirmed that the flaky smectite consisted mainly of Si and Al, and small amounts of Na. The smectite was formed in the stability field of Na-smectite for the system of Na2O-Al2O3-SiO2-H2O.

Experimental alterations of K-feldspar in distilled-deionized water at 150°, 175°, 200°, and 225°C were performed. The alteration products and dissolution mechanism of K-feldspar were examined by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX), and X-ray photoelectron spectroscopy (XPS). SEM, TEM, and EDX clearly showed formation of fibrous boehmite less than 1.0 μm in length at the early alteration stages. The boehmite fibers decreased in abundance and rounded platy 1 M mica was produced as alteration proceeded. The mica exhibited initially angular shaped small flakes of 0.69 μm in average size, which developed to rounded platy particles of 1.97 μm. The main chemical reactions occurring in this experimental system can be expressed by: $$\begin{array}{l} \mathop {KAlS{i_3}{O_3}}\limits_{\left[ {K - feldspar} \right]} + 6{H_2}O + {H^ + } \to \mathop {AlO\left( {OH} \right)}\limits_{\left[ {boehmite} \right]} + 3{H_4}Si{O_4} + {K^ + }, \\ \mathop {3KAlS{i_3}{O_8}}\limits_{\left[ {K - feldspar} \right]} + 12{H_2}O \to \mathop {KA{l_3}S{i_3}{O_{10}}{{\left( {OH} \right)}_2}}\limits_{\left[ {mica} \right]} + 2{K^ + } + 6{H_4}Si{O_4} + 22{H^ + }. \\ \end{array}$$ XPS showed no significant changes in intensities of photoelectron lines excited from K, Si, and Al in the K-feldspar surface before and after alteration, however the K/Si molar ratios in the solutions were considerably smaller than that of the original K-feldspar. The results of XPS strongly indicate that no dealkalized layer was produced on the surface, and that dissolution of K-feldspar in aqueous solution proceeded congruently by a surface-reaction mechanism. The discrepancy of mass balance in the solutions may be mainly caused by adsorption of K on the surface of boehmite.

Experimental alteration of obsidian in distilled-deionized water at 150°, 175°, 200°, and 225°C was studied. The alteration products were examined by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX) to evaluate the formation process of clay minerals. The surface composition of obsidian before and after alteration was examined by X-ray photoelectron spectroscopy (XPS), and concentrations of released elements in solution were measured to elucidate alteration and dissolution processes. TEM clearly showed that allophane appeared as the first reaction product in each experiment. With increasing reaction length, noncrystalline straight fibrous material was formed in the aggregates of allophane particles as a metastable transitional phase, and tended to form curled or wavy bundles of fibers with longer reaction. The non-crystalline fibers were transformed into highly curled smectite exhibiting small circular forms less than 1.0 µm in diameter as reaction progressed. EDX confirmed that the smectite consisted mainly of Si, Al, and small amounts of Ca, K, and Fe. XPS revealed the formation of a dealkalized leached layer on the surface of obsidian during the reaction. The concentration of released elements suggested that nonstoichiometric dissolution proceeded during the reaction.

Smectite and zeolites were formed from a volcanic glass as the products of reaction with NaOH solution at 90°C and 100°C under atmospheric pressure. Formation conditions of smectite and various zeolites were determined by the ratio of the amounts of volcanic glass (g) to NaOH (g) in the solution. Smectite was formed under the condition that the values of weight of volcanic glass (g)/(NaOH(g)/40) are between 0.5 and 6. Fe was an important constituent of the octahedral layer of smectite.

Bacterial mineralization in weathered pyroclastic deposits of the Kaimondake volcanic ash (4040 ybp) and the Koya pyroclastic flow (6400 ybp) was investigated to evaluate the impacts of bacteria on mineral formation, and to characterize the microbiogenic minerals in the weathering environment. The mineralogy of abiogenic weathering products was also investigated for comparison with the microbiogenic products, and mineral saturation indices were calculated for porewaters using the PHREEQC computer code. The results indicated that these weathered pyroclastic deposits contain 108–109 cells/g, consisting of spherical to rod-shaped bacteria. Associated abiogenic allophane had an Al/Si ratio ranging from 1.01 to 2.13. The bacterial cell surfaces were completely or partially covered by poorly-ordered silicate minerals, which could be divided into two groups based on their chemical and morphological characteristics. Group I was characterized by well developed fibrous to smectite-like flaky habits with variable Al, Si and Fe, corresponding to compositions between proto-imogolite allophane and chamosite. These Al-Si-Fe minerals were the most abundant and major microbiogenic products in both lithologies. Group II exhibited poorly-developed aggregates of allophane-like granular materials composed mainly of Al and Si with minor Fe. Geochemical calculations revealed that the porewaters were saturated with respect to allophane and other crystalline clay minerals such as halloysite, kaolinite, montmorillonite and nontronite. These microbiogenic minerals may be formed as the earliest phase of these clay minerals after interaction of the bacterial cell surfaces with dissolved cations mainly Si, Al and Fe, in the porewaters.

Guanidine and imidazole are important functional molecules that constitute the side chain of basic amino acids (arginine and histidine); these molecules are capable of interacting with mineral surfaces. However, little information is available about the effect of these molecules on mineral dissolution, including amorphous silica. In this study, to evaluate the effect of these organic molecules on the dissolution rates of amorphous silica, dissolution experiments were performed in solutions containing these molecules and other related heterocyclic compounds. The dissolution experiments were conducted by the batch method using 0.1 g of amorphous silica and 100 mL of 0.1 mM NaCl solution with 0.0, 0.1, 1.0, and 10.0 mM of guanidine, imidazole, pyrazole, or pyrrole at pH values of 4, 5, and 6. The results demonstrated that these compounds can enhance the dissolution rate of amorphous silica, depending on their ionic speciation in the following order: guanidine = imidazole > pyrazole > pyrrole. When 10.0 mM solutions were used, both guanidine and imidazole greatly increased the dissolution rate with an enhancement factor of 5.5—6.5, pyrazole exhibited a smaller change in the dissolution rate with an enhancement factor of 1.5—2.4, and pyrrole exhibited no significant enhancement. ChemEQL calculations confirmed that guanidine (pK = 13.6) and imidazole (pK = 6.99) are fully protonated and mostly present as cationic species in a pH range of 4—6; therefore, these compounds are capable of interacting with the >SiO- sites of amorphous silica. Pyrazole (pK= 2.61) and pyrrole (pK = 0.4), however, existed mostly as neutral forms. The concentrations of cationic species of pyrazole and pyrrole were at least one and three orders of magnitude lower than those of fully protonated compounds, respectively; therefore, pyrazole and pyrrole were less reactive than the fully protonated compounds on the surfaces of amorphous silica.

Amino acids are ubiquitous in the Earth’s surface environments as reactive biological molecules produced by every living thing including bacteria. To evaluate the effects of amino acids on mineral dissolution and to reveal the mechanism by which they interact with the mineral surface, we performed dissolution experiments of X-ray amorphous silica in solution containing 0.1 mmol Na with 10.0 mmol amino acids such as cysteine, asparagine, serine, tryptophan, alanine, threonine, histidine, lysine and arginine in near-neutral solutions. Dissolution experiments in solutions of 0.1, 1.0 and 10.0 mmol NaCl without amino acids were also conducted as amino acid-free controls. The results of this study indicate that basic amino acids such as histidine, lysine and arginine can interact more strongly with the negatively charged surface of amorphous silica than other non-basic amino acids due to their greater dissociation, thus forming cationic species. This electrostatical interaction enhanced dissolution rates of amorphous silica by approximately one order of magnitude compared with amino acid-free controls. In contrast, no significant effect on the dissolution rates of amorphous silica was observed in solutions containing cysteine, asparagine, serine, tryptophan, alanine and threonine because of lesser interaction with the surface of amorphous silica.

Six-membered ring heterocyclic compounds are widely present in the Earth's surface environments as biological organic molecules composed of soil organic matter including plant and microbial residues, while little is known about their effect on the dissolution of silicate minerals including amorphous silica. To evaluate the effect of these biological molecules on amorphous silica dissolution, dissolution experiments were carried out by the flow-through method using 0.1 g of amorphous silica and 0.1 mM NaCl electrolyte solutions containing 0.0, 0.1, 1.0, or 10.0 mM of the heterocyclic compounds, piperidine (pK = 11.12), pyridine (pK = 5.25), or pyridazine (pK = 2.33), at a pH of 6, 5, or 4. Additionally, adsorption experiments of the compounds on the amorphous silica surface were performed to confirm the adsorption affinity for the amorphous silica surface. The results demonstrated that these heterocyclic compounds enhance the dissolution rate of amorphous silica in the following order: piperidine > pyridine > pyridazine. When 10.0 mM solutions were used, the heterocyclic compounds enhanced greatly the dissolution rate up to enhancement factors of 6.0 to ~14.8, 5.0 to ~14.0, and 1.0 to ~2.6 through an interaction of piperidine, pyridine, and pyridazine, respectively, in the pH range of approximately 6 to ~ 4. The adsorption experiments indicated that the heterocyclic compounds exhibited significant adsorption affinity for the amorphous silica surface as follows: piperidine > pyridine > pyridazine, which was consistent with the order of their effects on the dissolution enhancement. The geochemical calculation revealed that this order of enhancement was in good agreement with the concentrations of cationic species of heterocyclic compounds at corresponding pH conditions. Consequently, the enhancement of amorphous silica dissolution is likely to be influenced by the electrostatic complexation of the cationic species of the heterocyclic compounds with the negative >SiO– sites on the amorphous silica surface.

Proteins and protein-like molecules are abundant in various geochemical environments; they form complexes with mineral surfaces and with dissolved organic matter. To evaluate the effect of proteins on rates of dissolution of minerals, experiments on the dissolution of amorphous silica in solutions containing various concentrations of bovine serum albumin (BSA) were performed in this study. The dissolution experiments were carried out by a batch method using solutions of 0.1 mM NaCl with 0.00, 0.05, 0.1, 0.2, 0.5, and 1.0 mg/mL of BSA at three different pH conditions, 6, 5, and 4. The results of the experiments demonstrated that BSA exhibited strong rate-enhancement effects on the dissolution of amorphous silica and were dependent on BSA concentration and the solution pH. At pH 6, the dissolution rates of amorphous silica appeared to increase successively by ~1.6, 2.2, 2.4, 2.5, and 2.9 times with increasing BSA concentrations of 0.05, 0.1, 0.2, 0.5, and 1.0 mg/mL, respectively. The rates of dissolution increased by greater degrees, ~3.1–5.8 and 4.9–13.0 times at pH 5 and 4, respectively. According to the calculated charge distributions of amino acid residues of the BSA molecule, the dissolution rates of amorphous silica were likely to be enhanced by attractive electrostatic interactions of the positively charged side chains of lysine, arginine, and histidine residues with the negatively charged >SiO− sites on the amorphous silica surface. The negatively charged side chains such as glutamic acid and aspartic acid residues may inhibit the attractive interaction, depending on the degree of deprotonation.