Broadband near-infrared (IR) luminescence in transparent alkali gallium silicate glass-ceramics containing Ni2+-doped β-Ga2O3 nanocrystals was observed. This broadband emission could be attributed to the 3T2g (3F) → 3A2g (3F) transition of octahedral Ni2+ ions in glass-ceramics. The full width at half-maximum (FWHM) of the near-IR luminescence and fluorescent lifetime of the glass-ceramic doped with 0.10 mol% NiO were 260 nm and ∼1220 μs, respectively. It is expected that transparent Ni2+-doped β-Ga2O3 glass-ceramics with this broad near-IR emission and long fluorescent lifetime have potential applications as super-broadband optical amplification media.

Infrared (IR) luminescence covering 1.1 to ∼1.6 μm wavelength region was observed from bismuth-doped barium silicate glasses, excited by a laser diode at 808 nm wavelength region, at room temperature. The peak of the IR luminescence appears at 1325 nm. A full width half-maximum (FWHM) and the lifetime of the fluorescence is more than 200 nm and 400 μs, respectively. The fluorescence intensity increases with Al2O3 content, but decreases with BaO content. We suggest that the IR luminescence should be ascribed to the low valence state of bismuth Bi2+ or Bi+, and Al3+ ions play an indirect dispersing role for the infrared luminescent centers.

We report on ultrabroad infrared (IR) luminescences covering the 1000–1700-nm wavelength region, from Bi-doped 75GeO2–20RO–5Al2O3–1Bi2O3(R = Sr, Ca, and Mg) glasses. The full width at half-maximum of the IR luminescences excited at 980 nm increases (315 → 440 → 510 nm) with the change of alkaline earth metal (Mg2+→ Ca2+→ Sr2+). The fluorescence lifetime of the glass samples is 1725, 157, and 264 μs when R is Sr, Ca, and Mg, respectively. These materials may be promising candidates for broad-band fiber amplifiers and tunable laser resources.