To save content items to your account,
please confirm that you agree to abide by our usage policies.
If this is the first time you use this feature, you will be asked to authorise Cambridge Core to connect with your account.
Find out more about saving content to .
To save content items to your Kindle, first ensure firstname.lastname@example.org
is added to your Approved Personal Document E-mail List under your Personal Document Settings
on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part
of your Kindle email address below.
Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations.
‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi.
‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
PbTe-PbS materials are promising for thermoelectric power generation applications. For the composition of (Pb0.95Sn0.05Te)0.92(PbS)0.08 nanostructuring from nucleation and growth and spinodal decomposition has been reported along with thermal conductivity of approximately 1.1 W/m·K at 650 K . Based on temperature-dependent measurements of electrical conductivity, thermopower, and thermal conductivity, the thermoelectric figure of merit, ZT, are ~1.5 at 650 K for cast ingots.
To develop larger quantities of material for device fabrication, advancement in the synthesis, processing and production of (Pb0.95Sn0.05Te)0.92(PbS)0.08 is necessary. Powder processing of samples is a well-known technique for increasing sample strength, and uniformity. In this presentation, we show sample fabrication and processing details of pulsed electric current sintering (PECS) processed (Pb0.95Sn0.05Te)0.92(PbS)0.08 materials and their thermoelectric properties along with the latest advancements in the preparation of these materials.
The U.S. military uses large amounts of fuel during deployments and battlefield operations. Consequently, the U.S. military has a strong need to develop technologies that increase fuel efficiency and minimize fuel requirements all along the logistics trail and in all battlefield operations. There are additional requirements to reduce and minimize the environmental footprint of various military equipment and operations and reduce the need for batteries (non-rechargeable) in battlefield operations. The tri-agency SERDP (Strategic Environmental Research and Development Program) office is sponsoring a challenging, high-payoff project to develop a lightweight, small form-factor, soldier-portable advanced thermoelectric generator (TEG) system prototype to recover and convert waste heat from a variety of deployed equipment with the ultimate purpose of obtaining additional power for soldier battery charging, advanced capacitor charging, and other battlefield power applications. The project seeks to achieve power conversion efficiencies of 10% (double current commercial TE conversion efficiencies) in a system with ˜1.6-kW power output for a spectrum of battlefield power applications. In order to meet this objective, the project is taking on the multi-faceted challenges of tailoring LAST/LASTT-based thermoelectric (TE) materials for the proper temperature ranges (300 K – 700 K), fabricating these materials with cost-effective hot-pressed and sintered processes while maintaining their TE properties, measuring and characterizing their thermal fatigue and structural properties, developing the proper manufacturing processes for the TE materials and modules, designing and fabricating the necessary microtechnology heat exchangers, and fabricating and testing the final TEG system. The ultimate goal is to provide an opportunity to deploy these TEG systems in a wide variety of current military equipment. This would help the Army in achieving one of the Office of Secretary of Defense’s major strategic objectives to maintain and enhance operational effectiveness while reducing total force energy demands. The presentation will review the progress made on 1) the performance of LAST / LASTT TE materials and tailoring their temperature dependency; 2) evaluating the structural (Elastic modulus, Poisson’s ratio and mechanical strength) properties of these materials, 3) development of the necessary LAST/LASTT-based TE modules, 4) development of the required hot- and cold-side microtechnology heat exchangers, and 5) the overall system designs for 30 kW and 60 kW TQG applications and potential performance pathways/differences for these two TQG cases. This work leverages critical fundamental research performed by the Office of Naval Research in developing LAST/LASTT materials.
Copper aluminum oxide (CuAlO2) with delafossite structure is a promising candidate for high temperature thermoelectric applications because of its modest band gap, high stability and low cost. We investigate magnesium doping on the aluminum site as a means of producing higher electrical conductivity and optimized Seebeck coefficient. Powder samples were synthesized using solid-state reaction and bulk samples were prepared using both cold-pressing and hot-pressing techniques. Composition analysis, microstructural examination and transport property measurements were performed, and the results suggest that while hot-pressing can achieve high density samples, secondary phases tend to form and lower the performance of the materials.
For the material (Pb0.95Sn0.05Te)1-x(PbS)x nanostructuring from nucleation and growth and spinodal decomposition were reported to enhance the thermoelectric figure of merit over bulk PbTe, producing ZT of 1.1 - 1.4 at 650 K for x = 0.08. Thermoelectric modules made from (Pb0.95Sn0.05Te)1-x(PbS)x materials with various hot-side metal electrodes were fabricated and tested. Short circuit current was measured on unicouples of Pb0.95Sn0.05Te – PbS 8% (n-type) legs and Ag0.9Pb9Sn9Sb0.6Te20 (p-type) legs over 10 (A) for a hot side temperature of 870K, and a cold side of 300K. Hot pressed (Pb0.95Sn0.05Te)1-x(PbS)x materials were also investigated for module fabrication. Investigations of the electrical properties of hot-pressed (Pb0.95Sn0.05Te)1-x(PbS)x materials are presented along with the latest advancements in the fabrication and characteristics of modules based on the processing of these materials.
Thermoelectric modules are of great interest for power generation applications where temperature gradients of approximately 500K exist, and hot side temperatures near 800K. The fabrication of such modules requires optimization of the material compositions, low contact resistivities, and low thermal loss.
AgPbmSbTe2+m (LAST) and Ag(Pb1-xSnx)m SbTe2+m (LASTT) compounds are among the best known materials appropriate for this temperature range. Various measurement systems have been developed and used to characterize bulk samples in the LAST and LASTT systems within this operating temperature range. From the characterized data, modeling of modules based on these materials and segmented legs using LAST(T) with Bi2Te3 have been used to identify the optimal geometry for the individual legs, and the length of the Bi2Te3 segments. We have segmented LAST(T) with Bi2Te3 and achieved contact resistivities of less than 10 μΩ•cm2.
Here we give a detailed presentation on the procedures used in the fabrication of thermoelectric generators based on LAST, LASTT, and segmented with Bi2Te3 materials. We also present the output data on these generators.
Low electrical contact resistance is essential for the fabrication of high efficiency thermoelectric generators in order to convert heat to electricity. These contacts must be stable to high temperatures and through thermal cycling. A ratio of the contact resistance to the leg resistance below 0.1 is the goal for fabrication of a high efficiency thermoelectric power generation device. Here we present the fabrication procedures and characterization of contacts of metal alloys to Pb-Sb-Ag-Te (LAST) and Pb-Sb-Ag-Sn-Te (LASTT) compounds. Contacts were fabricated and measured for both ingot and hot pressed materials. Stainless steel 316 has shown a low resistance contact to these thermoelectric materials when the proper bonding conditions are used. Different time-temperature-pressure conditions for bonding to n-type and to p-type legs are presented. Contact resistances below 10μΩcm2 have been measured. In addition, break tests have shown bond strengths exceeding the semiconductor fracture strength. One of the considerations used in selecting iron alloys for electrical interconnects is the similarity in the coefficient of thermal expansion to the LAST and LASTT materials which is 18 ppm/°C and relatively temperature insensitive. Contacts to the thermoelectric materials were accomplished by diffusion bonding in a furnace developed in our lab at Michigan State University. The furnace is capable of reaching temperatures of up to 1000°C with a controlled atmosphere of a reducing gas. Fabrication procedures and contact data are presented in this paper.
PbTe-based thermoelectric (TE) materials exhibit promising thermoelectric properties and have potential applications in waste heat recovery from sources such as truck engines and shipboard engines. TE components designed for these applications will be subject to mechanical/thermal loading and vibration as a result from in-service conditions, including mechanical vibration, mechanical and/or thermal cycling, and thermal shock.
In the current study, we present and discuss the mechanical properties of several PbTe-based compositions with different dopants and processing methods, including n-type and p-type specimens fabricated both by casting and by powder processing. Room temperature hardness and Young's modulus are studied by Vickers indentation and nanoindentation while fracture strength is obtained by biaxial flexure testing. Temperature dependent Young's modulus, shear modulus, and Poisson's ratio are studied via resonant ultrasound spectroscopy (RUS).